Fluororubber modified PVC (polyvinyl chloride) cable material for automobile wire harnesses and preparation method thereof

Abstract

The invention relates to a fluororubber modified PVC (polyvinyl chloride) cable material for automobile wire harnesses, which is prepared from the following raw materials in parts by weight: 65-70 parts of PVC, 7-8 parts of calcium zinc stabilizer, 40-50 parts of trioctyl trimellitate, 2.5-3 parts of triallyl isocyanurate, 0.2-0.3 part of dicumyl peroxide, 0.1-0.2 part of boric acid, 20-25 parts of hexafluoropropylene terpolymer rubber, 4-4.5 parts of nano zinc oxide, 1.8-2.1 parts of vinyl acetate, 1.4-1.8 parts of nano cellulose, 2.4-2.8 parts of zinc diethyl dithiocarbamate, 1-1.3 parts of triethanolamine, 2-2.5 parts of E-12 epoxy resin, 1.2-1.6 parts of xylene, 18-22 parts of thermoplastic polyurethane and 0.8-0.9 part of antioxidant 1010. The E-12 epoxy resin is utilized to enhance the bonding strength and dimensional stability of the cable material. The cable material is suitable for manufacturing wiring harnesses of parts of motormeters, illumination, air conditioners and the like.

Description

technical field [0001] The invention relates to the field of cable materials, in particular to a fluororubber modified PVC cable material for automobile wire harnesses and a preparation method thereof. Background technique [0002] Thermoplastic polyurethane (TPU) is a kind of elastomer with excellent performance, which has excellent acid and alkali resistance, oil resistance and mechanical properties, and has a wide temperature range. It can be used as a toughening agent or modifier for PVC materials. TPU can also improve the processing fluidity of PVC materials and play a plasticizing effect. However, due to the high price of TPU and poor flame retardancy, its application is limited. PVC has many grades, wide application and low cost, and is an important general-purpose plastic. Mixing and crosslinking TPU and PVC can effectively reduce the cost of TPU, improve performance and expand its application range; on the other hand, the addition of TPU can effectively improve th...

AI Technical Summary

Problems solved by technology

[0003] The formula used in the article "Development of PVC / thermoplastic polyurethane cross-linked cable material for automobiles": 100 parts of PVC, 8 parts of calcium zinc stabilizer, 50 parts of TOTM, 3 parts of TAIC, 0.2 parts of DCP, 30 parts of TPU, 0.8 parts of antioxidant, Appropriate amount of other additives can produce qualified cable materials for automobiles, but the cable materials are not good in heat resistance, oil resistance, ultraviolet resistance, oxidation resistance, corrosion resistance, atmospheric aging resistance, air tightness and wear resistance. , low temperature resistance and other aspects are not satisfactory