Anti-static and flame-retardant PP non-woven fabric masterbatch formula and preparation method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A non-woven fabric and antistatic technology, which is applied in the formulation and preparation of antistatic flame retardant pp nonwoven fabric masterbatch, which can solve the problems of poor flame retardancy, single performance of nonwoven fabric, and dust absorption.
Inactive Publication Date: 2015-06-03
JINAN JIAOTAI INFORMATION TECH
View PDF6 Cites 1 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
However, the performance of conventional non-woven fabrics is relatively simple, it cannot be antistatic, and its flame retardant performance is poor. Since non-woven fabrics are made of polymer materials, they are prone to static electricity, and they will absorb dust and interfere with the use of instruments during use and application. , have a bad impact on people's production and life
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0013] The preparation method of antistatic flame retardant pp nonwoven fabric masterbatch formula of the present invention comprises the following steps:
[0014] Mix 86% of the above pp resin, 2% polyethylene wax, 4% conductive carbon black, 2% lubricant, 4% flame retardant, 1% antistatic agent, and 1% antiaging agent in proportion, and stir in a high-speed mixer After 2-5 minutes, mix well and add to a twin-screw extruder, control the temperature of the extruder to 230 degrees Celsius, melt and extrude, cool and cut into pellets for storage.
Embodiment 2
[0016] The preparation method of antistatic flame retardant pp nonwoven fabric masterbatch formula of the present invention comprises the following steps:
[0017] Mix 90% of the above pp resin, 2% polyethylene wax, 2% conductive carbon black, 1% lubricant, 3% flame retardant, 1.5% antistatic agent, and 0.5% antiaging agent in proportion, and stir in a high-speed mixer After 2-5 minutes, mix well and add to the twin-screw extruder, control the temperature of the extruder to 220 degrees Celsius, melt and extrude, cool and cut into pellets for storage.
Embodiment 3
[0019] The preparation method of the antistatic flame retardant pp nonwoven masterbatch formula of the present invention comprises the following steps:
[0020] Mix 76% of the above pp resin, 5% polyethylene wax, 7% conductive carbon black, 3% lubricant, 8% flame retardant, 3% antistatic agent, and 1% antiaging agent in proportion, and stir in a high-speed mixer After 2-5 minutes, mix well and add to the twin-screw extruder, control the temperature of the extruder to 200-230 degrees Celsius, melt and extrude, cool and cut into pellets for storage.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention belongs to the technical field of chemical engineering, and particularly relates to an anti-static and flame-retardant PP non-woven fabric masterbatch formula and a preparation method thereof. The anti-static and flame-retardant PP non-woven fabric masterbatch formula is prepared from components in percentage by mass as follows: 76-90% of PP resin, 2-5% of polyethylene wax, 2-7% of conductive carbon black, 1-3% of a lubricant, 3-8% of a flame retardant, 1.5-3% of an antistatic agent and 0.5-1% of an antiaging agent. The masterbatch is applied to production of non-woven fabrics and has the characteristics that the masterbatch is flame-retardant, anti-static and the like, and problems that existing non-woven fabrics adsorb dust easily and interfere with usage of electronic instruments are solved, so that the non-woven fabrics can meet more diversified use requirements.
Description
(1) Technical field [0001] The invention belongs to the technical field of chemical industry, and in particular relates to a formula of antistatic and flame retardant PP non-woven fabric masterbatch and a preparation method thereof. (2) Background technology [0002] Non-woven fabric is a kind of non-woven fabric, which directly uses polymer chips, short fibers or filaments to form fibers through airflow or machinery, and then undergoes hydroentanglement, needle punching, or hot rolling reinforcement, and finally finishes finishing Formed non-woven fabric. A new type of fiber product with soft, breathable and planar structure. The advantage is that it does not produce lint, is strong, durable, silky soft, and has a cotton feel. It is mainly used for women's sanitary napkins, diapers, napkins, and clothing interlinings , shoes and hats interlining, and disposable surgical gowns, surgical caps, operating table covers, and are widely used in artificial leather, furniture, chem...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more