A lithium-ion battery positive electrode material doped with lithium and coated with metal oxide and its preparation method

A technology of lithium ion battery and positive electrode material, which is applied in the field of positive electrode material of lithium ion battery and its preparation, can solve problems such as increasing charge transfer resistance, and achieve the effects of improving cycle stability, improving electrochemical performance and reducing usage

Active Publication Date: 2017-12-22
SOUTHEAST UNIV
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Our research found that such a layer of film can indeed improve the performance of the material, but at the same time it brings a problem that the charge transfer resistance increases. Therefore, we have carried out corresponding research in order to solve the above technical problems

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A lithium-ion battery positive electrode material doped with lithium and coated with metal oxide and its preparation method
  • A lithium-ion battery positive electrode material doped with lithium and coated with metal oxide and its preparation method
  • A lithium-ion battery positive electrode material doped with lithium and coated with metal oxide and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] Example 1 is neither manganese oxide coating nor sodium doped material Li 1.17 Ni 0.62 co 0.14 mn 0.24 o 2 The preparation of is set for comparing with the product of embodiment 3.

Embodiment 2

[0027] Example 2 is only the Li coated with manganese oxide 1.17 Ni 0.62 co 0.14 mn 0.24 o 2 0.008MnO 2 The preparation of is set for comparing with the product of embodiment 3.

Embodiment 3

[0028] Example 3 is a sodium-doped manganese oxide-coated Li 1.07 Na 0.10 Ni 0.62 co 0.14 mn 0.24 o 2 0.008MnO 2 preparation.

[0029] Example 1: Li 1.17 Ni 0.62 co 0.14 mn 0.24 o 2 preparation of

[0030] (1) Preparation of precursor

[0031] Accurately weigh the sulfates of nickel, cobalt, and manganese in a molar ratio of 0.62:0.14:0.24, add water to dissolve to form a mixed salt solution, and control the total concentration of each metal ion in the solution between 0.1mol / l and a saturated solution; Sodium carbonate that is 1.1 times the total molar number of metal ions (0.62+0.14+0.24=1) is dissolved in water to form a sodium carbonate solution with a concentration between 0.1mol / l and a saturated solution. The above two solutions were mixed and reacted completely, resulting in a suspension. Under the protection of nitrogen, the obtained suspension was continuously stirred for 24 h, during which the pH value of the solution was precisely controlled at 8.5, a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a lithium-site doped and metal oxide-coated lithium ion battery positive electrode material and a preparation method thereof. The lithium ion battery positive electrode material has the chemical formula of Li(m-x)MexMaNbCcO2.yTO2, wherein Me refers to doped alkali metal or an alkaline-earth metal element; TiO2 refers to the coated metal oxide. The lithium-site doped and metal oxide coated lithium ion battery positive electrode material has the advantages that the coating metal oxide can be used for preventing the large-area contact of the lithium ion battery positive electrode material and electrolyte, and inhibiting the reaction between the battery positive electrode material with the high reaction property and electrolyte, so that the cyclic stability of the battery material can be improved greatly; the laminar structure of the lithium ion battery positive electrode material can be perfected by adopting coating, so that the electrochemical performance is also improved; partial lithium atoms in the battery positive electrode material can be replaced with alkali metal or alkaline-earth metal ions by adopting doping, so that a metal oxide layer is strutted, embedding and de-embedding of the lithium ion are facilitated, the high-current discharge performance of the material is improved, and the use of the rare element lithium is reduced.

Description

technical field [0001] The invention relates to a lithium ion battery positive electrode material and a preparation method thereof, in particular to a lithium ion battery positive electrode material doped with lithium and coated with a metal oxide, and belongs to the field of lithium ion battery positive electrode materials and its preparation. Background technique [0002] Compared with lead-acid, nickel-cadmium, and nickel-metal hydride batteries, lithium-ion batteries have the advantage of high energy density. At present, lithium-ion batteries are still mainly used in small portable devices, and the electric vehicle industry is continuing to make lithium-ion batteries applicable to electric vehicles. Electric vehicles do not produce air pollution and have low noise during operation. They can absorb the excess electricity in the city at night and achieve the effect of peak shaving and valley filling. They can also be operated by replacing batteries that are fully charged w...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01M4/36H01M4/505H01M4/525H01M4/131H01M4/1391H01M4/04
CPCH01M4/139H01M4/362H01M4/505H01M4/525H01M10/0525Y02E60/10
Inventor 雷立旭米萨尔·艾德楠
Owner SOUTHEAST UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com