A kind of polylactic acid/polyester alloy and preparation method thereof

A polyester alloy and polylactic acid technology, applied in the polymer field, can solve the problems of unstable phase structure, difficult to meet, toughness, rigidity, and heat resistance difficult to balance, etc., to avoid design difficulties and reduce investment costs.

Active Publication Date: 2016-09-14
FINE BLEND POLYMER SHANGHAI CO LTD
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to solve the problem that toughness, rigidity, and heat resistance are difficult to balance in the modification process of polylactic acid. The multi-element alloy obtained by simple compatibilization treatment has unstable phase structure and is difficult to meet higher requirements. need

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of polylactic acid/polyester alloy and preparation method thereof
  • A kind of polylactic acid/polyester alloy and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] 1000g each of PLA and PC, dried at 80°C for 2h, compatibilizer (styrene-butadiene-acrylonitrile-GMA) 300g, antioxidant (168 / 1010) 60g, lubricant (TAF) 40g, using the above extrusion After mixing the above raw materials for 3 to 5 minutes in a high-speed mixer, they were respectively put into a two-stage extruder with an ultrasonic treatment power of 400W, extruded and granulated to obtain sample 4, and the granules were dried at 90°C for 3 hours, and then injection molded into samples. strip, test.

Embodiment 2

[0031] PLA 800g and PC 1200g, dried at 80°C for 2h, compatibilizer (styrene-butadiene-acrylonitrile-GMA) 300g, antioxidant (168 / 1010) 60g, lubricant (TAF) 40g, using the above Extrusion process, the above raw materials are mixed by a high-speed mixer for 3 to 5 minutes, and then put into a two-stage extruder respectively, with an ultrasonic treatment power of 500W, extruded and granulated to obtain sample 5, and the particles are dried at 90°C for 3 hours, and then injection molded into Spline, test.

Embodiment 3

[0033] PLA 1400g and PC 600g, dried at 80°C for 2h, compatibilizer (styrene-butadiene-acrylonitrile-GMA) 600g, antioxidant (168 / 1010) 60g, lubricant (TAF) 40g, using the above Extrusion process, the above raw materials are mixed by a high-speed mixer for 3 to 5 minutes, and then put into a two-stage extruder respectively, with an ultrasonic treatment power of 350W, extruded and granulated to obtain sample 6, and the granules are dried at 90°C for 3 hours, and then injection molded into Spline, test.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a polylactic acid / polyester alloy and a preparation method thereof. The polylactic acid / polyester alloy comprises the following components in percentage by weight: polylactic acid, polyester, a compatilizer, a flexibilizer, an antioxidant and a lubricant. The preparation method comprises the following steps: firstly, proportioning the raw materials and mixing at a room temperature; and respectively carrying out melting extrusion, carrying out ultrasonic treatment at the first late stage, extruding at the second stage and pelletizing, so as to obtain degradable, high-impact-resistant and high-heat-resistant polylactic acid / polyester alloy. Compared with an existing method, the controllable ultrasonic treatment is utilized; and a similar polylactic acid-g-polyester structure is formed by in-situ reaction, so that the heat resistance of the polyester and the biodegradability of the polylactic acid are reserved; and meanwhile, a toughening system with a core-shell structure is formed in an alloy system through interface interaction of a special toughening compatilizer, so that the alloy product with high impact resistance, high heat resistance and high biodegradability can be obtained.

Description

technical field [0001] The invention belongs to the field of macromolecules, and relates to a degradable, high-impact-resistant, high-heat-resistant polylactic acid / polyester alloy and a preparation method thereof. Background technique [0002] With the development of science and technology and the times, the modification or alloying of polymer materials has been widely used as an inevitable means; at the same time, with the development of the times, people pay more and more attention to green environmental protection. Polylactic acid is a polymer obtained by polymerizing lactic acid as the main raw material. The raw material source is sufficient and can be regenerated. The production process of polylactic acid is non-polluting, and the product can be biodegraded to realize the cycle in nature, so it is an ideal green polymer material. Polylactic acid can be used in many fields such as extrusion, injection molding, film drawing, spinning, etc., but the shortcomings of polyl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L69/00C08L67/02C08L67/04C08L55/02C08K13/02C08K5/098C08K5/20B29B9/06B29C47/40B29C47/08
CPCC08L67/04C08L69/00C08L2201/06C08L2201/08C08L2205/03C08L55/02C08K5/1345C08K5/526
Inventor 段浩李昌鸿杨威汤俊杰齐阳城
Owner FINE BLEND POLYMER SHANGHAI CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com