Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Ultraviolet cured rare earth polymer material and preparation method thereof

A polymer material, ultraviolet light technology, applied in chemical instruments and methods, luminescent coatings, organic chemistry, etc., can solve problems such as difficulty in adapting to environmental protection requirements, poor photothermal stability, etc., to achieve shortened curing time, low cost, synthetic simple method effect

Inactive Publication Date: 2015-04-08
NANCHANG HANGKONG UNIVERSITY
View PDF2 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But the disadvantage is that the light and heat stability is poor, it is difficult to process and shape, and the polymer matrix material is easy to process, impact resistance, corrosion resistance and light weight, etc., research on rare earth organic complexes, compound rare earth complexes into polymer matrix to make Rare earth polymer materials can improve certain properties of materials, such as mechanical properties and optical properties, to achieve functional complementarity and performance optimization
[0003] Ultraviolet light curing technology has the characteristics of wide applicability, high efficiency, energy saving and environmental protection, and has been widely used in production and life. With the global restrictions on environmental pollution emissions and the improvement of people's environmental awareness, traditional solvent-based coatings have become very Difficult to adapt to environmental protection requirements, it is bound to be replaced by UV-curable coatings

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ultraviolet cured rare earth polymer material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A method for preparing an ultraviolet-cured rare earth polymer material, characterized in that:

[0024] (1) Preparation of rare earth acrylic acid complex, weighing europium oxide, dibenzoylmethane, and acrylic acid in a molar ratio of 1:4:6, wherein europium oxide is 2 mmol;

[0025] Take 5ml of hydrochloric acid to dissolve europium oxide into a colorless transparent solution, heat until the solution is completely evaporated to dryness, and obtain a white powdery europium chloride. After the white solid is cooled, add an appropriate amount of absolute ethanol to dissolve it to obtain anhydrous transparent chlorine Europium chloride absolute ethanol solution;

[0026] Weigh 8-20mmol of acrylic acid and pour it into a three-necked flask equipped with a condenser tube and a thermometer, stir and adjust the temperature to 30°C, then add europium chloride anhydrous ethanol solution dropwise into the three-necked flask, and adjust the reaction with sodium hydroxide The pH...

Embodiment 2

[0032] A method for preparing an ultraviolet-cured rare earth polymer material, characterized in that:

[0033] (1) Preparation of rare earth acrylic acid complex, weighing europium oxide, dibenzoylmethane, and acrylic acid in a molar ratio of 1:4:6, wherein europium oxide is 2 mmol;

[0034] Take 7ml of hydrochloric acid to dissolve europium oxide to form a colorless transparent solution, heat until the solution is completely evaporated to dryness, and obtain a white powdery europium chloride. After the white solid is cooled, add an appropriate amount of absolute ethanol to dissolve to obtain anhydrous transparent chlorine Europium chloride absolute ethanol solution;

[0035] Weigh 12mmol of acrylic acid and pour it into a three-necked flask equipped with a condenser tube and a thermometer, stir and adjust the temperature to 50°C, then add the europium chloride anhydrous ethanol solution dropwise into the three-necked flask, and adjust the reaction solution with sodium hydrox...

Embodiment 3

[0041] A method for preparing an ultraviolet-cured rare earth polymer material, characterized in that:

[0042] (1) Preparation of rare earth acrylic acid complex, weighing europium oxide, dibenzoylmethane, and acrylic acid in a molar ratio of 1:4:6, wherein europium oxide is 2 mmol;

[0043]Take 10ml of hydrochloric acid to dissolve europium oxide into a colorless transparent solution, heat until the solution is completely evaporated to dryness, and obtain a white powdery europium chloride. After the white solid is cooled, add an appropriate amount of absolute ethanol to dissolve it to obtain anhydrous transparent chlorine Europium chloride absolute ethanol solution;

[0044] Weigh 12mmol of acrylic acid and pour it into a three-necked flask equipped with a condenser tube and a thermometer, stir and adjust the temperature to 70°C, then add the europium chloride anhydrous ethanol solution dropwise into the three-necked flask, and adjust the reaction solution with sodium hydrox...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses an ultraviolet cured rare earth polymer material and a preparation method thereof. The ultraviolet cured rare earth polymer material includes the following components in percentage by weight: 1%-20% of rare earth and acrylic acid complex, 40%-60% of urethane acrylate, 30-50% of active diluent, 1%-10% of photoinitiator and the balance of auxiliaries. The ultraviolet cured rare earth polymer material has the advantages that the rare earth and acrylic acid complex and the matrix resin are subjected to polymerization reaction, thus being good in consistency; the rare earth and acrylic acid complex modified resin is good fluorescence property and wide in ultraviolet absorption peak that the range stretch across the ultraviolet and near-ultraviolet areas; as the coating prepared by the above materials has the characteristics of being quick in photocuring speed, good in film property and friendly to environment; the film can be used for ultraviolet cured paint and luminous paint.

Description

technical field [0001] The invention relates to a preparation method of an ultraviolet light curing rare earth luminous coating, in particular to a preparation method of an ultraviolet light curing rare earth polymer material. technical background [0002] Rare earth elements have a unique electronic structure with the same outer layer, and the electron layer configuration of the inner layer 4f electron energy level is similar, which determines that rare earth elements have a variety of electronic layer arrangements and abundant electronic energy levels, and their rare earth compounds show many unique features. Its physical and chemical properties are widely used in the fields of light, electricity and magnetism. But the disadvantage is that the light and heat stability is poor, it is difficult to process and shape, and the polymer matrix material is easy to process, impact resistance, corrosion resistance and light weight, etc., research on rare earth organic complexes, com...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D175/14C09D7/12C09D5/22C07F5/00
CPCC09D175/14C07F5/003C08K5/0091C08K5/103C09D5/22C09D7/63
Inventor 钟荣冯英锋张涛张春辉
Owner NANCHANG HANGKONG UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com