Polyphthalamide (PPA) composite material with high temperature resistance and abrasion resistance and preparation method of PPA composite material

A technology of polyphthalamide and phthalamide, which is applied in the field of polyphthalamide composite materials and its preparation, can solve problems such as low lifespan and unstable mechanical properties, and ensure mechanical properties and durability Effect of thermal wear resistance, surface gloss and dimensional stability improvement

Inactive Publication Date: 2015-04-01
ANHUI KEJU NEW MATERIALS
View PDF5 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In view of this, the object of the present invention is to provide a high temperature and wear-resistant polyphthalamide composite material and its preparation method, aiming to solve the problem of using the existing polyphthalamide composite material to make parts. Technical problems of low life and unstable mechanical properties under high temperature conditions

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polyphthalamide (PPA) composite material with high temperature resistance and abrasion resistance and preparation method of PPA composite material
  • Polyphthalamide (PPA) composite material with high temperature resistance and abrasion resistance and preparation method of PPA composite material
  • Polyphthalamide (PPA) composite material with high temperature resistance and abrasion resistance and preparation method of PPA composite material

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0037] The preparation method comprises the steps of:

[0038] S101, the step of weighing raw materials. Each raw material is weighed according to the mass ratio of the raw materials of the high-temperature and wear-resistant polyphthalamide composite material.

[0039] S102, a drying treatment step. The raw materials taken symmetrically are dried.

[0040] S103, the initial mixing step. Put the dried polyphthalamide into the mixer, then add antioxidant, lubricant and nucleating agent, and mix thoroughly.

[0041] S104, a remixing step. Add the anti-wear agent into the mixer and mix thoroughly again. After the mixing is completed, the obtained material is put into a drying oven for drying treatment.

[0042] S105. Melting and granulating step. The dried material is put into a twin-screw extruder, melted and reacted, and glass fiber is added to carry out reinforced filling extrusion granulation, wherein the glass fiber is added from the fourth section of the twin-screw ex...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
heat deflection temperatureaaaaaaaaaa
Login to View More

Abstract

The invention is applicable to the field of high molecular materials and provides a polyphthalamide (PPA) composite material with high temperature resistance and abrasion resistance and a preparation method of the PPA composite material. The PPA composite material with high temperature resistance and abrasion resistance comprises the following raw material components in percentage by mass: 40-60% of PPA, 5-15% of an abrasion-resistant agent, 30-45% of a filling and reinforcing agent, 0.2-0.6% of an antioxidant, 0.2-0.8% of a lubricating agent and 0.3-0.6% of a nucleating agent. The preparation method of the PPA composite material with high temperature resistance and abrasion resistance comprises the following steps: sorting, mixing in a mixer, putting the obtained mixture into a double-screw extruder, carrying out melt extrusion, and pelletizing. The PPA composite material with high temperature resistance and abrasion resistance has the advantages that the abrasion-resistant agent is introduced into PPA, so that abrasion resistance and self-lubricating property of PPA are improved, and glass fibers are adopted for carrying out enhancement processing, and thus a modified composite material with excellent performance is obtained, mechanical properties and heat resistance and abrasion resistance properties are guaranteed, and the PPA composite material with high temperature resistance and abrasion resistance can be applied to a transmission part under high temperature condition.

Description

technical field [0001] The invention belongs to the technical field of polymer materials, and in particular relates to a high-temperature and wear-resistant polyphthalamide composite material and a preparation method thereof. Background technique [0002] Polyphthalamide (PPA) resin is a semi-aromatic polyamide material made of phthalic acid. It has the advantages of high rigidity, high heat resistance, high strength, and excellent electrical properties. At the same time, its thermal properties are also very good. High, after adding glass fiber reinforcement, the heat distortion temperature can reach 280 ℃. In the state of high temperature and high humidity, the tensile strength of polyphthalamide is 20% higher than that of nylon 6, higher than that of nylon 66; the flexural modulus of polyphthalamide material is 20% higher than that of nylon, so polyphthalamide Diformamide can be used in more severe environments. However, due to the high temperature environment and high w...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L77/06C08L27/18C08K13/04C08K7/14C08K3/04C08K3/30C08K5/134C08K5/526C08K5/098B29C47/92B29C48/92
CPCC08L77/06B29C48/92B29C2948/9258B29C2948/92704C08K3/30C08K7/14C08K13/04C08K2003/3009C08L2201/08C08L2205/24C08L27/18
Inventor 徐东付俊祺
Owner ANHUI KEJU NEW MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com