A weather-resistant steel plate

A technology of weather resistance and steel plate, applied in the direction of coating, layered products, polyester coatings, etc., can solve the problems of difficult large-area construction, poor metal adhesion, long curing time, etc., to achieve excellent adhesion and processability, Effect of better heat resistance and hot hardness, excellent solvent resistance

Active Publication Date: 2016-12-28
GUANGDONG ARMSTRONG METAL CEILING PRODS
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] With the advancement of technology, it is found that silicone resin also has better heat resistance. The basic skeleton of silicone resin is the main chain of Si-O, which has higher bond energy than the C-C bond of ordinary polymers. Heat resistance and anti-oxidation are also strong. Normally, the heat resistance temperature of silicone resin is 300°C. It has been proved by practice that in addition to heat resistance, silicone resin also shows excellent weather resistance and stain resistance. , water removal, cold resistance and chemical corrosion resistance, etc., but in actual use, there are still the following problems, such as: need high temperature curing (above 250 ℃) and long curing time, difficult large-scale construction, adhesion to metal Poor, poor solvent resistance and high production cost, for this reason, we must find a high-performance material that can replace silicone resin for the coating treatment of steel plates. Polyester resin or epoxy resin for higher heat resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A weather-resistant steel plate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] The weather-resistant steel plate involved in this embodiment is prepared by coating and baking the pre-coated steel plate with the base coating and the surface coating in sequence, wherein the base coating is applied to the surface of the pre-coated steel plate to form a base coating , by weight percentage, the base coating contains the following components:

[0029] Silicone modified polyester resin: 30%; filler: 20%;

[0030] Silicone coupling agent: 1%; Phthalate: 0.5%;

[0031] Xylene solvent: 48.5%.

[0032] The surface coating is applied to the surface layer of the base coating film to form a surface coating film. In terms of weight percentage, the surface coating comprises the following components:

[0033] Silicone modified polyester resin: 40%; pigment: 10%;

[0034] Polyamide curing agent: 5%; Filler: 10%;

[0035] Siloxane coupling agent: 1.2%; Xylene solvent: 33.8%.

[0036] The following is a further description of the composition of the above compone...

Embodiment 2

[0041] The weather-resistant steel plate involved in this embodiment is prepared by coating and baking the pre-coated steel plate with the base coating and the surface coating in sequence, wherein the base coating is applied to the surface of the pre-coated steel plate to form a base coating , by weight percentage, the base coating contains the following components:

[0042] Silicone modified polyester resin: 50%; filler: 46%;

[0043] Silicone coupling agent: 2%; Phthalate: 1%;

[0044] Xylene solvent: 1%.

[0045]The surface coating is applied to the surface layer of the base coating film to form a surface coating film. In terms of weight percentage, the surface coating comprises the following components:

[0046] Silicone modified polyester resin: 60%; pigment: 15%;

[0047] Polyamide curing agent: 7%; Filler: 15%;

[0048] Siloxane coupling agent: 1.8%; Xylene solvent: 1.2%.

[0049] The following is a further description of the composition of the above components:

...

Embodiment 3

[0054] The weather-resistant steel plate involved in this embodiment is prepared by coating and baking the pre-coated steel plate with the base coating and the surface coating in sequence, wherein the base coating is applied to the surface of the pre-coated steel plate to form a base coating , by weight percentage, the base coating contains the following components:

[0055] Silicone modified polyester resin: 45%; filler: 46%;

[0056] Silicone coupling agent: 1.5%; Phthalate: 0.5%;

[0057] Xylene solvent: 7%.

[0058] The surface coating is applied to the surface layer of the base coating film to form a surface coating film. In terms of weight percentage, the surface coating comprises the following components:

[0059] Silicone modified polyester resin: 55%; Pigment: 12%;

[0060] Polyamide curing agent: 6%; Filler: 14%;

[0061] Siloxane coupling agent: 1.5%; Xylene solvent: 11.5%.

[0062] The following is a further description of the composition of the above componen...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
acid valueaaaaaaaaaa
thermal resistanceaaaaaaaaaa
acid valueaaaaaaaaaa
Login to View More

Abstract

The invention discloses a weather-resistant steel plate which is prepared from a pre-coated steel plate coated and roasted by a basic coating and a surface coating sequentially. The basic coating and the surface coating used by the invention are prepared from organosilicone modified polyester resin as a base material and other auxiliaries. According to the weather-resistant steel plate disclosed by the invention, due to excellent heat resisting temperature, excellent adhesiveness and processibility on metal materials, excellent solvent resistance, good high-heat hardness and the like, the organosilicone modified polyester resin can be used for being sprayed on metal surfaces of iron materials, aluminum products or stainless steel and the like and can be widely applied to heat-resisting materials, such as a petroleum refining furnace, an aluminum refining furnace, an engine exhaust system and an engine silencer, which are in a high-temperature working condition for a long time.

Description

technical field [0001] The invention belongs to the field of metal materials, in particular to a weather-resistant steel plate. Background technique [0002] The steel plate is made by coating and drying the pre-coated steel plate before processing and forming. Since the film is formed after the film is formed, it is not only required that the pre-coated steel plate can meet the high requirements of hardness and formability. The coating material used for its coating also needs to be resistant to processing. In the field of metal materials, the coating on the metal can not only protect and beautify the appearance of the metal, such as rust prevention and coloring, etc. Sometimes, the coating can also be used to achieve some special functions, such as improving lubrication and improving deep drawing. performance etc. In the actual application process, the effect of the coating is closely related to the coating. Taking heat-resistant coatings as an example, heat-resistant co...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D167/00C09D7/12B32B33/00
CPCC08K3/08C08K3/22C08K3/34C08K3/346C08K3/36C08K3/40C08K13/02C08K2003/0812C08K2003/2241C08K2003/2251C08K2201/014C08L2201/08C09D7/20C09D7/61C09D7/63C09D167/00
Inventor 张一帆
Owner GUANGDONG ARMSTRONG METAL CEILING PRODS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com