Core-shell structure lithium manganate and preparation method thereof

A technology of structural lithium manganate and lithium manganate, applied in structural parts, electrical components, battery electrodes, etc., can solve problems such as short battery cycle life, achieve the effect of enhancing cycle stability, improving performance, and solving serious capacity attenuation

Inactive Publication Date: 2016-09-14
ANHUI NORMAL UNIV
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0009] The invention provides a core-shell structure lithium manganese oxide and a preparation method thereof. The core-shell structure lithium manganese oxide separates the LiMn2O4 electrode material in the inner layer from the electrolyte, which can inhibit the reaction between the electrode and the electrolyte, and reduce the dissolution loss of manganese. Improve its electrochemical performance and high temperature performance, and solve the problem of short battery cycle life of lithium manganate battery cathode materials under high temperature, high current and other working conditions

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Core-shell structure lithium manganate and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] 1) Take commercial manganese carbonate and lithium carbonate at a molar ratio of 4:1, put them into an acetic acid solution with a volume concentration of 50%, emulsify with an ultrasonic emulsifier to form a homogeneous emulsion, and dry in a dryer at 95°C;

[0032] 2) In an open high-temperature furnace, raise the temperature to 550°C at a rate of 5°C / min and keep it warm for 3 hours;

[0033] 3) Then use a fan to blow air into the high-temperature furnace, raise the temperature to 700°C at a rate of 5°C / min and hold it for 3 hours for sintering;

[0034] 4) Gradually lower the temperature to 550°C at a cooling rate of 5°C / min, and keep the fan blowing air into the high-temperature furnace during the cooling process;

[0035] 5) When the furnace temperature drops to 550°C, stop feeding air into the high-temperature furnace, and no longer control the cooling rate at this time, and naturally cool to room temperature to obtain a spinel-type lithium manganate material;

...

Embodiment 2

[0049] 1) Take commercial manganese carbonate and lithium carbonate at a molar ratio of 3.8:1, put them into an acetic acid solution with a volume concentration of 40%, emulsify with an ultrasonic emulsifier to form a homogeneous emulsion, and dry in a dryer at 95°C;

[0050] 2) In an open high-temperature furnace, raise the temperature to 560°C at a rate of 5°C / min and keep it warm for 3 hours;

[0051] 3) Then use a fan to blow air into the high-temperature furnace, raise the temperature to 710°C at a rate of 5°C / min and hold it for 3 hours for sintering;

[0052] 4) Gradually lower the temperature to 560°C at a cooling rate of 5°C / min, and keep the fan blowing air into the high-temperature furnace during the cooling process;

[0053] 5) When the furnace temperature drops to 560°C, stop feeding air into the high-temperature furnace, and no longer control the cooling rate at this time, and naturally cool to room temperature to obtain a spinel-type lithium manganate material; ...

Embodiment 3

[0058] 1) Take commercial manganese carbonate and lithium carbonate at a molar ratio of 4.2:1, put them into an acetic acid solution with a volume concentration of 60%, emulsify with an ultrasonic emulsifier to form a homogeneous emulsion, and dry in a dryer at 95°C;

[0059] 2) In an open high-temperature furnace, raise the temperature to 540°C at a rate of 5°C / min and keep it warm for 3 hours;

[0060] 3) Then use a fan to blow air into the high-temperature furnace, raise the temperature to 690°C at a rate of 5°C / min and hold it for 3 hours for sintering;

[0061] 4) Gradually lower the temperature to 540°C at a cooling rate of 5°C / min, and keep the fan blowing air into the high-temperature furnace during the cooling process;

[0062] 5) When the furnace temperature drops to 540°C, stop feeding air into the high-temperature furnace, and no longer control the cooling rate at this time, and naturally cool to room temperature to obtain a spinel-type lithium manganate material; ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
thicknessaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides lithium manganate of a core-shell structure and a preparation method of the lithium manganate. According to the lithium manganate of the core-shell structure, a LiMn2O4 electrode material on the inner layer is separated from electrolyte, reaction between the electrode and the electrolyte can be inhibited, dissolution loss of manganese is reduced, the electrochemical performance and high-temperature performance are improved, and the problem that the cycle life of the battery made of a lithium manganate battery cathode material is short under the working conditions such as high temperature and large current is solved. The lithium manganate of the core-shell structure with the advantages of small impurity phases and high specific capacity can be prepared under relatively simple conditions by using low-price raw materials, the lithium manganate of the core-shell structure is simple in process, mild in conditions, low in energy consumption, low in cost and environmentally friendly, and large-scale production is easily realized. According to the core-shell structure, the crystal form of lithium manganate is effectively protected, and dissolution of bivalent manganese is relieved. Moreover, according to the super-capacitor performance of Co3O4, impact of large current on lithium manganate can be alleviated, and the fall time of lithium manganate is prolonged, so that the cycling stability of the battery is enhanced. When the temperature rises, the performance of the material is strengthened.

Description

technical field [0001] The invention relates to core-shell structure lithium manganese oxide and a preparation method thereof. Background technique [0002] Lithium-ion battery is a secondary battery with high energy density, high power density and long life, which plays an important role in modern society. In various mobile devices, electric vehicles, and power tools, the role of lithium-ion batteries is almost irreplaceable. Cathode material is one of the decisive factors for the performance and cost of lithium-ion batteries, and is an important direction for the improvement of lithium-ion batteries. At present, the active cathode material used in lithium-ion batteries is mainly lithium cobalt oxide, but due to the lack of cobalt resources, high price, and poor safety performance, it is not conducive to the popularization and application of lithium-ion batteries; lithium iron phosphate has many expected advantages. Ion batteries have also been widely tried, but with less...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01M4/505
CPCH01M4/505Y02E60/10
Inventor 陶海升党建成王斌涂丹丹
Owner ANHUI NORMAL UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com