Water-based plastic coating and preparation method thereof

A plastic coating, water-based technology, applied in the direction of polyurea/polyurethane coatings, coatings, etc., can solve the problems of late research and development of water-based plastic coatings, poor orientation of flash pigments, easy to be affected by humidity, etc., to achieve excellent hand feel, color retention, etc. Good performance, controllable hardness and softness

Active Publication Date: 2015-01-07
JIANGSU MARINE VICTORY COATING
View PDF2 Cites 25 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the requirements for environmental protection and resources, people have requested to limit the use of high VOC content and toxic coatings. The research and development of water-based plastic coatings in my country is relatively late.
Due to the nature of water, although plastic water-based coatings have many advantages, compared with traditional solvent-based coatings, there are still some problems. The first is that water has a high latent heat of evaporation and is easily affected by humidity, resulting in sagging and flashing pigments. Misorientation and other issues

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] This embodiment provides a water-based plastic coating, which comprises the following components by mass percentage: water-based resin emulsion: 45%, deionized water: 40%, calcium carbonate: 10%, additives: 5%;

[0034] Among them, the water-based resin emulsion is formed by mixing siloxane-modified UV-curable water-based polyurethane emulsion and water-based polyurethane / polyacrylate composite emulsion at a mass ratio of 1:1;

[0035] The siloxane-modified UV-curable water-based polyurethane emulsion includes the following components in parts by mass: isophorone diisocyanate: 15 parts, polyether siloxane diol: 15 parts, polytetrahydrofuran diol: 8 parts , dihydroxypropionic acid: 5 parts, 1,4-butanediol: 5 parts, pentaerythritol triacrylate: 15 parts, triethylamine: 4 parts;

[0036] The water-based polyurethane / polyacrylate composite emulsion includes the following components in parts by mass: Polyoxypropylene glycol: 10 parts, dimethylol propionic acid: 13 parts, iso...

Embodiment 2

[0047] This embodiment provides a water-based plastic coating, which comprises the following components by mass percentage: water-based resin emulsion: 50%, deionized water: 38%, titanium dioxide: 8%, additives: 4%;

[0048] Among them, the water-based resin emulsion is formed by mixing siloxane-modified UV-curable water-based polyurethane emulsion and water-based polyurethane / polyacrylate composite emulsion at a mass ratio of 1:1;

[0049] The siloxane-modified UV-curable water-based polyurethane emulsion includes the following components in parts by mass: isophorone diisocyanate: 10 parts, polyether siloxane diol: 13 parts, polytetrahydrofuran diol: 5 parts , dihydroxypropionic acid: 7 parts, 1,4-butanediol: 10 parts, pentaerythritol triacrylate: 20 parts, triethylamine: 2 parts;

[0050] The water-based polyurethane / polyacrylate composite emulsion includes the following components in parts by mass: Polyoxypropylene glycol: 13 parts, dimethylol propionic acid: 15 parts, isop...

Embodiment 3

[0061] This embodiment provides a water-based plastic coating, which comprises the following components by mass percentage: water-based resin emulsion: 47%, deionized water: 40%, bentonite: 10%, additives: 3%;

[0062] Among them, the water-based resin emulsion is formed by mixing siloxane-modified UV-curable water-based polyurethane emulsion and water-based polyurethane / polyacrylate composite emulsion at a mass ratio of 1:1;

[0063] The siloxane-modified UV-curable water-based polyurethane emulsion includes the following components in parts by mass: isophorone diisocyanate: 12 parts, polyether siloxane diol: 10 parts, polytetrahydrofuran diol: 10 parts , dihydroxypropionic acid: 8 parts, 1,4-butanediol: 8 parts, pentaerythritol triacrylate: 20 parts, triethylamine: 5 parts;

[0064] The water-based polyurethane / polyacrylate composite emulsion includes the following components in parts by mass: Polyoxypropylene glycol: 15 parts, dimethylol propionic acid: 10 parts, isophorone...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a water-based plastic coating. The water-based plastic coating comprises the following components: a water-based resin emulsion, deionized water, a filler and additives. The invention further designs a preparation method of the water-based plastic coating, and the preparation method comprises the following steps: adding the filler into the water-based resin emulsion, adding an appropriate amount of deionized water, stirring, pouring into a sand mill for grinding, putting into a dispersing cylinder when the fineness is below 80mu m, adding the additives, sealing, stirring and detecting the viscosity for not less than 95s to prepare the water-based plastic coating. The water-based plastic coating has excellent water absorption, water retention, water suction and drainage and a good humidity adjusting effect, can be used for regulating the indoor relative humidity, and has the advantages of relatively high scrubbing resistance, water resistance and solvent resistance, corrosion resistance, alkali resistance, light resistance, weather resistance, good film-forming property, excellent color retention, wear resistance, corrosion resistance, controllable hardness, high performance-price ratio and the like, and the preparation method is simple, easy to operate without pollution, good in construction and safe to use.

Description

technical field [0001] The invention belongs to the field of industrial paint preparation, in particular to a water-based plastic paint and a preparation method thereof. Background technique [0002] Plastic is light in weight, easy to process and corrosion-resistant. Rich resources and other characteristics have widely replaced traditional materials such as metals. Wood, leather, etc., commonly appear in our daily life. However, when plastic products are molded and processed, they will have defects such as uneven color, monotonous color, mottled defects, etc., and are prone to problems such as aging and brittleness, scratches, stains, and static electricity. Coating can avoid the above-mentioned defects and problems. The research and development of plastic coatings has been widely concerned by paint workers. However, since plastics are low surface energy substances, their surface coating is much more difficult than that of steel, wood, buildings, etc. Efforts have become...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D175/14C09D175/08C09D133/02C09D7/12C08G18/75C08G18/67C08G18/66C08G18/48C08G18/61C08G18/34C08G18/32
CPCC09D175/14C08G18/3206C08G18/3228C08G18/348C08G18/4845C08G18/61C08G18/6692C08G18/672C08G18/755C08L2205/02C08L2205/03C09D7/61C09D7/63C09D133/02C09D175/08C08L75/08C08L33/02C08K13/02C08K2003/265C08K5/06C08K5/17C08K5/098C08K5/18C08K3/346C08L75/14
Inventor 郑化陈廷生刘小林
Owner JIANGSU MARINE VICTORY COATING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction