Preparation method of micro-nano tin dioxide solid spheres

A tin dioxide, solid ball technology, applied in the directions of tin oxide, nanotechnology, nanotechnology, etc., can solve the problems of low environmental protection in the preparation process, difficulty in densifying the reinforcing phase, unfavorable industrial production, etc., and is suitable for large-scale industrial production. Smooth surface and uniform size effect

Active Publication Date: 2015-01-07
ZHEJIANG UNIV
View PDF4 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, at present, the preparation process of these tin dioxide with special morphology is relatively complicated, and the preparation process is low in environmental protection, especially when it is used as a reinforcing phase of ceramics, metals and other materials, it is difficult to densify, or the process to achieve densification is complicated and costly, which is not conducive to long-term production. large-scale industrial production

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of micro-nano tin dioxide solid spheres
  • Preparation method of micro-nano tin dioxide solid spheres
  • Preparation method of micro-nano tin dioxide solid spheres

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0022] The present invention will be further described in detail below in conjunction with examples, but those skilled in the art will understand that the following examples are only used to illustrate the present invention and should not be regarded as limiting the scope of the present invention.

[0023] The preparation method of the micro-nano tin dioxide solid ball of the present invention includes the following steps:

[0024] (1) SnCl 4 ·5H 2 O is dissolved in deionized water, and under sufficient stirring conditions, a solution with a concentration of 0.1~1.0mol / L is formed; press NaOH and H 2 The mass ratio of O is 1:5-15, the NaOH is weighed and dissolved in deionized water, and NaOH solution is obtained by stirring;

[0025] (2) Add NaOH solution uniformly to SnCl at a rate of 40-60 drops / min 4 ·5H 2 In the O solution, adjust the pH of the solution to 10-13; stir at 500-1200 revolutions per minute while dripping to obtain a uniform mixed solution;

[0026] (3) Transfer the mi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to the preparation of micro-nano materials, and aims to provide a preparation method of micro-nano tin dioxide solid spheres. The method comprises the following steps: respectively preparing a SnCl4.5H2O aqueous solution and a NaOH solution, uniformly dropwise adding the NaOH solution into the SnCl4.5H2O aqueous solution, and stirring at a high speed; transferring the mixed solution to a polytetrafluoroethylene reaction kettle, and carrying out a hydrothermal reaction on the mixed solution; carrying out centrifugal separation or filtering on the obtained product, washing the obtained object until no soluble ion exists in the solution, and drying, so that white powder is obtained; and putting the powder into a chamber electric furnace or a muffle furnace to calcine, and carrying out furnace cooling on the obtained product, so that white or light yellow powder, namely, micro-nano tin dioxide solid spheres, is obtained. Products prepared according to the preparation method disclosed by the invention are good in sphericity, smooth in surface, and uniform in size; no organic solvent as well as volatile poisonous gas and the like is used in the preparation process, so that only do sodium salts exist in products, and therefore, the product has no pollution to the environment; and no template is used, so that the method is simple in process, easily controlled in reaction process, mild in reaction condition, simple in raw material and low in cost, and therefore, the method is specially suitable for large-scale industrial production.

Description

Technical field [0001] The invention belongs to the field of micro-nano material preparation and its technical application, in particular to a preparation method of micro-nano tin dioxide solid spheres. Background technique [0002] Tin dioxide is a semiconductor material with high hardness, good chemical stability, and excellent photoelectric properties. It has important application value in electronic components, lithium-ion batteries, gas sensors, super capacitors, transparent electrodes and catalytic materials. In recent years, structural materials such as tin dioxide nanoparticles, nanowires, nanobelts and hollow spheres have been widely studied and applied, and there are many preparation methods. For example, Chinese patent CN 1789140A (publication number) discloses a zinc oxide A method for preparing hollow tin oxide sphere materials as a sacrificial template; Chinese patent CN 101012067A uses natural polymer powder as a template to prepare hollow tin oxide spheres. Howev...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C01G19/02B82Y30/00
CPCB82Y30/00C01G19/02C01P2004/32C01P2004/61C01P2004/64
Inventor 杨辉张继张玲洁陈乐生沈涛申乾宏
Owner ZHEJIANG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products