A kind of zn-ca system zinc alloy and its preparation method and application

A zinc alloy, zn-ca technology, applied in medical science, prosthesis and other directions, to achieve the effect of overcoming the degradation rate too fast, good histocompatibility, and long-term effective mechanical support

Active Publication Date: 2016-09-21
PEKING UNIV
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0009] At present, there are no literature and patent reports on the synthesis and properties of Zn-Ca alloys at home and abroad, and it is proposed to use Zn-Ca alloys as biodegradable biomedical materials.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of zn-ca system zinc alloy and its preparation method and application
  • A kind of zn-ca system zinc alloy and its preparation method and application
  • A kind of zn-ca system zinc alloy and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0090] Embodiment 1, preparation as-cast Zn-Ca series alloy

[0091] Using pure Zn (99.99wt.%) and pure Ca (99.95wt.%) (purchased from Beijing Cuibin Nonferrous Metal Technology Development Center) as raw materials, according to different mass ratios (the mass ratio of Zn and Ca is 99:1 and 95:5) mixed in CO 2 +SF 6 Under the protection of the atmosphere, smelt at 800 ° C, after the raw materials are fully melted, after 10 minutes of heat preservation, the circulating water is rapidly cooled, and the Zn-Ca alloy ingot is obtained (photo as figure 1 shown), where Zn-1Ca means that the mass ratio of Zn to Ca is 99:1, and Zn-5Ca means that the mass ratio of Zn to Ca is 95:5.

Embodiment 2

[0092] Embodiment 2, preparation rolling state Zn-Ca series alloy

[0093] First, the as-cast Zn-Ca alloy ingot is prepared according to the steps in Example 1; then the Zn-Ca alloy ingot obtained above is hot-rolled, and the ingot is preheated at 250° C., and then hot-rolled. It is repeatedly rolled in a reciprocating rolling mill with a hot rolling temperature of 250°C, and finally rolled to 1.5mm in a finishing mill at 250°C.

[0094] figure 2 This is a photograph of the as-rolled Zn-Ca alloy (Zn-1Ca) obtained in this example.

Embodiment 3

[0095] Embodiment 3, preparation extruded state Zn-Ca series alloy

[0096] Prepare according to the following 1) or 2) steps:

[0097] 1) First, the as-cast Zn-Ca alloy ingot (Zn-1Ca) was prepared according to the steps in Example 1, and the Zn-Ca alloy rod (Zn-1Ca) was prepared by extrusion, and radial extrusion Zn-Ca alloy rods (Zn-1Ca) with a diameter of 10 mm were prepared at an extrusion temperature of 200°C and an extrusion ratio of 20.

[0098] 2) First prepare the as-cast Zn-Ca alloy ingot according to the steps in Example 1, and use a high-vacuum rapid quenching system to prepare a rapidly solidified Zn-Ca alloy thin strip. The specific method is: mix the raw materials according to the stated ratio Afterwards, a high-vacuum quenching system is used to prepare rapidly solidified Zn-Ca thin strips. The parameters are 2-8g feeding amount, 3-7kW induction heating power, 0.80mm distance between nozzle and roller, 0.1MPa injection pressure, and 2000r / mln roller speed. An...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
tensile strengthaaaaaaaaaa
yield strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a Zn-Ca series zinc alloy as well as a preparation method and application thereof. The zinc alloy of the present invention includes Zn and Ca; in terms of weight percentage, the mass percentage of Ca in the zinc alloy is 0-30%, but 0 is not included. The zinc alloy also includes trace elements, and the trace elements are at least one of silicon, phosphorus, lithium, silver, tin and rare earth elements; in the zinc alloy, the mass percentage of the trace elements is 0 ~3%, but excluding 0. The mechanical properties of the Zn-Ca-based zinc alloy of the present invention meet the requirements of the strength and toughness of medical implant materials, are non-toxic, have good tissue compatibility and blood compatibility, and can be degraded by body fluids at the same time, and the dissolved metal ions It can be absorbed and utilized by organisms to promote bone growth or be excreted from the body by metabolism, and can be applied to the preparation of medical implants.

Description

technical field [0001] The invention relates to a Zn-Ca series zinc alloy and its preparation method and application, in particular to a Zn-Ca series zinc alloy and its preparation method and its application in the preparation of body fluid degradable medical implants, belonging to medical metal materials Preparation technology field. Background technique [0002] Biomedical materials currently used in clinical practice mainly include biomedical metal materials, inorganic materials, polymer materials, composite materials, and bionic materials. Compared with polymer materials and ceramic materials, medical metal materials have higher strength, toughness and processing performance, so they are the most widely used. Such as: 316L, 317L, 304V stainless steel, Co-Cr-Mo alloy, pure titanium, Ti-6Al-4V, TiNi alloy, etc. These materials are non-degradable in the human body and are permanently implanted. When the implant expires in the human body, it must be removed through a secon...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C18/00C22C1/02A61L27/04
Inventor 郑玉峰李华芳秦岭
Owner PEKING UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com