Grass meal based degradable agricultural mulch film and preparation method thereof

An agricultural mulch and grass powder-based technology, which is applied in the direction of plant protection covers, can solve the problems of degradation induction period and degradation rate, poor mechanical properties and water resistance, and inability to play a role in fertile fields, so as to achieve sufficient supply and good fertile fields The effect of saving food resources

Active Publication Date: 2014-10-15
苏州格瑞惠农膜材料科技有限公司
View PDF7 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing above-mentioned mulch films have poor mechanical properties and water resistance, and the degradation induction period and degradation rate are slow and uncontrollable, and the degraded substances cannot play the role of fertilizing the field.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Grass meal based degradable agricultural mulch film and preparation method thereof
  • Grass meal based degradable agricultural mulch film and preparation method thereof
  • Grass meal based degradable agricultural mulch film and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] Embodiment 1: In terms of 100 kilograms, the preparation method of the grass powder-based degradable agricultural mulch film provided in this embodiment is as follows:

[0045] 1) In a 100-liter internal mixer, add 55 kg of hybrid pennisetum grass powder with a particle size of 500 mesh, 7.5 kg of Dow 3004 EAA resin, 5 kg of silicone acrylic resin containing epoxy groups, and silicone dendritic resin. 2.5 kg of resin monomer, 1 kg of epoxy soybean oil, 1 kg of polyethylene wax, 1 kg of titanium dioxide with a particle size of 1250 mesh, 1 kg of calcium carbonate with a particle size of 1500 mesh, banburying at 125°C for 2.5 hours, and then pouring into double The cone feeder is added to the single-screw granulator. The temperature of the three heating zones of the single-screw granulator is controlled at 125°C, 130°C, and 135°C respectively, and the temperature of the die head is controlled at 135°C. After cooling, enter the granulator to obtain 74 kg of modified grass ...

Embodiment 2

[0049] Embodiment 2: In terms of 100 kilograms, the preparation method of the grass powder-based degradable agricultural mulch film provided in this embodiment is as follows:

[0050] 1) Add 50 kg of Pennisetum grass powder with a particle size of 250 mesh, 7 kg of Dow 3004 EAA resin, 5 kg of epoxy-containing silicone acrylic resin, and silicone dendritic resin into a 100-liter mixer. 2 kg of monomer, 1 kg of epoxy soybean oil, 1 kg of polyethylene wax, 1 kg of titanium dioxide with a particle size of 1250 mesh, 1 kg of calcium carbonate with a particle size of 1500 mesh, banburying at 125°C for 2.5 hours, and then pouring into the double cone The feeder is added to the single-screw granulator, and the temperature of the three heating zones of the single-screw granulator is controlled at 125°C, 130°C, and 135°C respectively, and the temperature of the die head is controlled at 135°C. After entering the granulator, 68 kilograms of modified grass powder masterbatches were obtain...

Embodiment 3

[0053] Embodiment three: In terms of 100 kilograms, the preparation method of the grass powder-based degradable agricultural mulch film provided in this embodiment is as follows:

[0054] 1) Add 45 kg of 300-mesh wheatgrass powder, 15 kg of DuPont 2014 brand film grade EAA high-strength resin, 5 kg of epoxy-containing silicone acrylic resin, and silicone dendritic resin in a 100-liter internal mixer. 3 kg of monomer, 1 kg of epoxy soybean oil, 1 kg of polyethylene wax, 1 kg of 1250 mesh titanium dioxide, 1 kg of 1300 mesh calcium carbonate, banburying at 110~125°C for 1.5~2.5 hours, and then pouring into double cone The feeder is added to the single-screw granulator. The temperature of the three heating zones of the single-screw granulator is controlled at 120°C, 130°C, and 135°C respectively, and the temperature of the die head is controlled at 135°C. After entering the granulator, 72 kilograms of modified grass powder masterbatches were obtained.

[0055] 2) After mixing 22...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
particle size (mesh)aaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a grass meal based degradable agricultural mulch film which is characterized by comprising the following components as raw materials by weight: 45-55 parts of grass meal, 5-15 parts of ethylene acrylic acid (EAA) copolymer resin, namely EAA resin; 5-15 parts of silicone acrylic resin containing epoxy groups, 1-5 parts of a silicone branch resin monomer, 1-3 parts of epoxy soybean oil, 1-3 parts of polyethylene wax, 1-3 parts of titanium dioxide, 1-4 parts of calcium carbonate, 15-30 parts of polyethylene, 5-15 parts of maleic anhydride grafted modified polyethylene, 0.1-0.6 part of light degradation masterbatch and 0.3-1.5 part of moisture absorption masterbatch. The grass meal based degradable agricultural mulch film has excellent mechanical properties and water resistance, and can control the degradation rate according to different regions, climatic conditions and crop varieties. The invention also provides a preparation method of the agricultural mulch film, and the method has the advantages of simple process, abundant raw materials and easy popularization.

Description

technical field [0001] The invention relates to a grass powder-based degradable agricultural mulch film and a preparation method thereof, belonging to the technical field of polymer materials. Background technique [0002] Agricultural plastic mulch was adopted in agricultural production in the 1950s. my country introduced agricultural mulch film from Japan in 1978, and it is widely used in domestic crop cultivation. In order to make full use of the production-increasing effect of plastic mulch and eliminate the problems of land fertility decline and environmental pollution caused by plastic mulch, developed countries have successively begun to study degradable mulch. [0003] At present, the main degradable mulch films include: biodegradable mulch films, photodegradable mulch films, light / biodegradable mulch films and degradable mulch films made of plant fibers. However, the existing above-mentioned mulch films have poor mechanical properties and water resistance, and the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L97/02C08L23/08C08L33/08C08L51/06C08L83/06C08L23/06C08K13/02C08K5/1515C08K3/22C08K3/26C08J3/22B29C47/92B29C55/28A01G13/02B29C48/92
CPCB29C47/0054B29C47/0026B29C47/92B29C48/0017B29C48/10B29C48/92B29C2948/926B29C2948/92704
Inventor 谢洪德夏心蕾徐磊鲍清
Owner 苏州格瑞惠农膜材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com