Zirconium-silver alloy target and preparation method and application thereof

A technology of zirconium-silver alloy and target material, which is applied in metal material coating process, ion implantation plating, coating and other directions to achieve the effects of uniform structure, low cost and simple process

Active Publication Date: 2014-07-16
XIAMEN RUNNER IND CORP
View PDF2 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The melting point of zirconium is 1852°C. Zirconium is very easy to oxidize. The melting point of silver is 960.8°C. It is difficult to obtain high-purity zirconium-silver alloy targets by conventional vacuum induction melting technology or powder metallurgy.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Zirconium-silver alloy target and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] The invention relates to a method for preparing a zirconium-silver alloy target, comprising the following steps:

[0036] (1), weighing and mixing: the nuclear-grade spongy metal zirconium (the purity of zirconium is 99.8%) and silver scraps with a purity of 99.99% are weighed and mixed according to the mass percentage of 98% for zirconium and 2% for silver;

[0037] (2) Electrode pressing: place the mixed metal zirconium and silver alloy materials in a nitrogen protective atmosphere to prevent the materials from being damp and oxidized, and put the prepared zirconium silver materials evenly into the press to press them into electrodes. Each electrode is controlled at 6kg, in which zirconium and silver are evenly mixed and clothed, and the pressed electrode is placed in a nitrogen protective atmosphere to prevent the material from being damp and oxidized;

[0038] (3) Welding electrodes: The two pressed electrodes are welded into smelting electrodes by tungsten argon ar...

Embodiment 2

[0056] The invention relates to a method for preparing a zirconium-silver alloy target, comprising the following steps:

[0057] (1), weighing and mixing: the nuclear-grade spongy metal zirconium (the purity of zirconium is 99.8%) and silver scraps with a purity of 99.99% are weighed and mixed according to the mass percentage of 97% for zirconium and 3% for silver;

[0058] (2) Electrode pressing: place the mixed metal zirconium and silver alloy materials in a nitrogen protective atmosphere to prevent the materials from being damp and oxidized, and put the prepared zirconium silver materials evenly into the press to press them into electrodes. Each electrode is controlled at 4.4kg, in which zirconium and silver are evenly mixed and clothed, and the pressed electrode is placed in a nitrogen protective atmosphere to prevent the material from being damp and oxidized;

[0059] (3) Welding electrodes: The two pressed electrodes are welded into smelting electrodes by tungsten argon ...

Embodiment 3

[0073] The invention relates to a method for preparing a zirconium-silver alloy target, comprising the following steps:

[0074] (1), weighing and mixing: the nuclear-grade spongy metal zirconium (the purity of zirconium is 99.8%) and silver scraps with a purity of 99.99% are weighed and mixed according to the mass percentage of 99.5% for zirconium and 0.5% for silver;

[0075] (2) Electrode pressing: place the mixed metal zirconium and silver alloy materials in a nitrogen protective atmosphere to prevent the materials from being damp and oxidized, and put the prepared zirconium silver materials evenly into the press to press them into electrodes. Each electrode is controlled at 8.0kg, in which zirconium and silver are evenly mixed and clothed, and the pressed electrode is placed in a nitrogen protective atmosphere to prevent the material from being damp and oxidized;

[0076] (3) Welding electrodes: The two pressed electrodes are welded into smelting electrodes by tungsten ar...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
diameteraaaaaaaaaa
melting pointaaaaaaaaaa
Login to view more

Abstract

The invention provides a zirconium-silver alloy target and a preparation method and an application thereof, and relates to alloy targets. The zirconium-silver alloy target is composed of 97-99.5% of zirconium and 0.5-3% of silver according to mass percent. The preparation method includes the following steps: mixing nuclear grade sponge stage metal zirconium with silver chips to obtain a zirconium and silver mixture; pressing the zirconium and silver mixture into electrodes, placing the electrodes in a nitrogen atmosphere environment to prevent dampness and oxidation of the material; welding each two electrodes into a melting electrode; melting the melting electrode to obtain primary zirconium-silver ingots; deheading and smoothing the tails of the primary zirconium-silver ingots, welding each two primary zirconium-silver ingots into a secondary zirconium-silver melting electrode; melting the secondary zirconium-silver melting electrode to obtain secondary zirconium-silver ingots; hot forging the secondary zirconium-silver ingots to eliminate coarse-grain generated in the melting process and homogenize the tissues, carrying out a heat treatment and cooling, and processing the necessary zirconium-silver alloy target according to the size specification of the target. The prepared zirconium-silver alloy target is free of such defects as obvious pore, segregation and the like, and is uniform in tissue size.

Description

technical field [0001] The invention relates to an alloy target material, in particular to a zirconium-silver alloy target material and a preparation method and application thereof. Background technique [0002] At present, in the surface treatment and decoration industry, multi-arc zirconium targets are generally used for surface decoration coating, and various decorations with excellent corrosion resistance are obtained by feeding reactive gases such as nitrogen, argon, acetylene, etc. during the coating process. Sexual color film. The antibacterial film layer is usually sputtered with a layer of silver film to achieve antibacterial and antibacterial effects, but due to the poor stability of silver in the atmosphere and poor corrosion resistance, the color of the product will change and corrosion will occur on the surface, which seriously affects the quality of the product. Appearance quality, but not able to be applied in practice. [0003] Chinese invention patent 2009...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22C16/00C23C14/30
Inventor 余水张先超张恩瑞李明仁
Owner XIAMEN RUNNER IND CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap