Method for welding CVD diamond thick film and hard alloy

A diamond thick film and hard alloy technology, which is applied in welding equipment, metal processing equipment, manufacturing tools, etc., can solve the problems of high welding cost, large equipment investment, and high solder requirements, achieve good surface wettability, and solve the problem of high investment. , the effect of excellent bonding strength

Active Publication Date: 2014-07-02
山西新碳超硬材料科技有限公司
View PDF6 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The present invention aims at high requirements on solder when welding CVD diamond thick film and cemented carbide by active brazing method, while the currently used method of first metallizing diamond thick film and then welding has the disadvantages of large equipment investment, complicated process and high welding cost. Provide a welding method of CVD diamond thick film and hard alloy

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for welding CVD diamond thick film and hard alloy
  • Method for welding CVD diamond thick film and hard alloy
  • Method for welding CVD diamond thick film and hard alloy

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] A welding method of CVD diamond thick film and cemented carbide, first using double glow plasma metallization equipment to metallize the growth surface of CVD diamond thick film, and then using the same double glow plasma metallization equipment to metallize The final CVD diamond thick film growth surface is brazed with the cemented carbide substrate;

[0025] Among them, the metallization process of CVD diamond thick film growth surface is:

[0026] The CVD diamond thick film was prepared by microwave plasma CVD method, hot wire CVD method or DC arc plasma CVD method, and the CVD diamond thick film was ultrasonically cleaned with deionized water and alcohol for 5 minutes, and dried with hot air; The CVD diamond thick film growth side is placed on the substrate table in the vacuum furnace of the double-glow plasma metallization equipment, and the metal W with a purity of 99.9% that can form strong carbides with carbon is selected as the target material. The distance be...

Embodiment 2

[0036] A welding method of CVD diamond thick film and cemented carbide, first using double glow plasma metallization equipment to metallize the growth surface of CVD diamond thick film, and then using the same double glow plasma metallization equipment to metallize The final CVD diamond thick film growth surface is brazed with the cemented carbide substrate;

[0037] Among them, the metallization process of CVD diamond thick film growth surface is:

[0038] The CVD diamond thick film was prepared by microwave plasma CVD method, hot wire CVD method or DC arc plasma CVD method, and the CVD diamond thick film was ultrasonically cleaned with deionized water and alcohol for 5 minutes, and dried with hot air; The CVD diamond thick film growth side is placed on the substrate table in the vacuum furnace of the double-glow plasma metallization equipment, and Ti, which can form strong carbides with carbon elements, is selected as the target material. The target material and the CVD diam...

Embodiment 3

[0044] A welding method of CVD diamond thick film and cemented carbide, first using double glow plasma metallization equipment to metallize the growth surface of CVD diamond thick film, and then using the same double glow plasma metallization equipment to metallize The final CVD diamond thick film growth surface is brazed with the cemented carbide substrate;

[0045] Among them, the metallization process of CVD diamond thick film growth surface is:

[0046] The CVD diamond thick film was prepared by microwave plasma CVD method, hot wire CVD method or DC arc plasma CVD method, and the CVD diamond thick film was ultrasonically cleaned with deionized water and alcohol for 4 minutes, and dried with hot air; The CVD diamond thick film growth side is placed on the substrate table in the vacuum furnace of the double-glow plasma metallization equipment, and Zr, which can form strong carbides with carbon elements, is selected as the target material. The target material and the CVD diam...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a method for welding a CVD diamond thick film and hard alloy. The method comprises the steps that firstly, a double-glow plasma diffusion metal device metallizes a growth face of the CVD diamond thick film, and secondly, the double-glow plasma diffusion metal device is used for welding the metallized face and a hard alloy substrate in a brazing mode. According to the method, metal atoms are evenly diffused on the surface of the growth face of the diamond thick film according to the double-glow plasma diffusion metal technology, metal carbide is formed by the metal atoms and the diamond thick film, and superior bonding strength between a metal layer and the diamond thick film is guaranteed through chemical bonding. The metallized diamond thick film has good ground surface wettability, and a welding connector with high bonding strength can be formed through the metallized diamond thick film and the hard alloy under the heating action of plasma. The surface metallization of the diamond thick film and brazing can be finished through the same device, manufacturing production cost is greatly reduced, and industrialization can be achieved.

Description

technical field [0001] The invention relates to the welding field of superhard materials, in particular to a welding method of CVD diamond thick film and hard alloy. Background technique [0002] Diamond is the hardest substance in nature, and it has many excellent properties, such as ultra-high wear resistance, high thermal conductivity, etc., so it is the most ideal material for making knives among known materials. Natural diamond and polycrystalline diamond (PCD) tools are rapidly replacing traditional high-speed steel and carbide tools within a certain range of use. However, due to the extremely limited resources of natural diamond, its large-scale promotion is limited, and the PCD tool contains 5-10% binder components, resulting in the surface quality of the processed material being lower than that of natural diamond. Diamond thick film welding tool is a new type of cutting tool manufactured by welding chemical vapor deposition (CVD) diamond thick film and hard alloy. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B23K1/008B23K1/20B23K1/19
CPCB23K1/008B23K1/19B23K1/206
Inventor 于盛旺高洁申艳艳黑鸿君宁来元安康贺志勇
Owner 山西新碳超硬材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com