A kind of midsole adhesive with high solid content and preparation method thereof

A high solid content, adhesive technology, applied in the direction of adhesives, adhesive types, rosin adhesives, etc., can solve the problems of precipitation, delamination, etc., achieve low cost, good storage stability, and save resources.

Active Publication Date: 2016-02-17
GUANGDONG ORIENT RESIN
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In addition, in the production process of chloroprene rubber itself, talcum powder is added in order to prevent the dry glue from sticking, and its adhesive products must be added with inorganic substances that are not compatible with solvents such as magnesium oxide and zinc oxide to absorb its release. Chlorine in order to maintain the stability of performance, so the neoprene adhesives have precipitation or even serious delamination

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0056] S1. In a reaction kettle with a stirrer and a condenser, put in the solvent methylcyclohexane, butanone and SBS elastomer according to the formula, and dissolve at room temperature for 2 hours;

[0057] S2. After the SBS is completely dissolved, add the monomers methyl methacrylate, vinyl acetate, and acrylic acid; raise the temperature to 80°C under normal pressure, and add the initiator BPO;

[0058] S3. Stir and react for 3-5 hours at 85-90°C with a rotation speed of 80-120 rpm, allowing the SBS elastomer to be synthesized by grafting monomers to obtain high-molecular polymers;

[0059] S4. Cool down to 60°C, add the polymerization inhibitor BHT;

[0060] S5. Cool down to below 40°C, add a certain amount of tackifying resin terpene resin, petroleum resin, glycerin resin, and rosin;

[0061] S6. Stir evenly, the appearance is slightly yellow and clear, and the detection viscosity range is 4000~5000CPS at room temperature. After the index is qualified, it can be disch...

Embodiment 2

[0076] S1. In a reaction kettle with a stirrer and a condenser, put in the solvent methylcyclohexane, butanone and SBS elastomer according to the formula, and dissolve at room temperature for 2 hours;

[0077] S2. After the SBS is completely dissolved, add the monomers methyl methacrylate, vinyl acetate, and acrylic acid; raise the temperature to 80°C under normal pressure, and add the initiator BPO;

[0078] S3. Stir and react for 3-5 hours at 85-90°C with a rotation speed of 80-120 rpm, allowing the SBS elastomer to be synthesized by grafting monomers to obtain high-molecular polymers;

[0079] S4. Cool down to 60°C, add the polymerization inhibitor BHT;

[0080] S5. Cool down to below 40°C, add a certain amount of tackifying resin terpene resin, petroleum resin, glycerin resin, and rosin;

[0081] S6. Stir evenly, the appearance is slightly yellow and clear, and the detection viscosity range is 4000~5000CPS at room temperature. After the index is qualified, it can be disch...

Embodiment 3

[0096] S1. In a reaction kettle with a stirrer and a condenser, put in the solvent methylcyclohexane, butanone and SBS elastomer according to the formula, and dissolve at room temperature for 2 hours;

[0097] S2. After the SBS is completely dissolved, add the monomers methyl methacrylate, vinyl acetate, and acrylic acid; raise the temperature to 80°C under normal pressure, and add the initiator BPO;

[0098] S3. Stir and react for 3-5 hours at 85-90°C with a rotation speed of 80-120 rpm, allowing the SBS elastomer to be synthesized by grafting monomers to obtain high-molecular polymers;

[0099] S4. Cool down to 60°C, add the polymerization inhibitor BHT;

[0100] S5. Cool down to below 40°C, add a certain amount of tackifying resin terpene resin, petroleum resin, glycerin resin, and rosin;

[0101] S6. Stir evenly, the appearance is slightly yellow and clear, and the detection viscosity range is 4000~5000CPS at room temperature. After the index is qualified, it can be disch...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
softening pointaaaaaaaaaa
softening pointaaaaaaaaaa
softening pointaaaaaaaaaa
Login to View More

Abstract

The invention provides a midsole adhesive with high solid content and a preparation method thereof. The midsole adhesive with high solid content is prepared from the following raw materials in parts by weight: SBS elastomer: 15-20 parts, methylcyclohexane: 50-60 parts, butanone: 10-15 parts, methyl Methyl acrylate: 10~15 parts, vinyl acetate: 2~5 parts, acrylic acid: 1~2 parts, initiator: 0.2~0.3 parts, terminator: 0.5~1 parts, terpene resin: 10~15 parts, C9 Petroleum resin: 5~10 parts, 138 glycerin resin: 5~10 parts, rosin: 20~30 parts. The midsole adhesive prepared by the invention has high solid content, low VOC content, clear glue solution, good stability, long stickiness maintenance time, low cost, wide source of raw materials, and good application prospect.

Description

technical field [0001] The present invention relates to an adhesive, more specifically, to a midsole adhesive with high solid content and a preparation method thereof. Background technique [0002] At present, the midsole adhesives for shoes on the market are all based on neoprene universal adhesives. Due to the high polarity of neoprene rubber and high solubility requirements, these products use a large amount of excellent solubility. Common triphenyls (toluene, xylene, benzene, etc.), and halogenated hydrocarbon solvents must also be added with phenolic resins to improve heat resistance, but these materials are highly toxic, and some may even cause cancer. Due to the presence of chlorine, phenol, aldehyde, triphenyl and other toxic substances, low solid content, high VOC (volatile organic compound content), and great air pollution, neoprene adhesives are eliminated products in developed countries. In addition, in the production process of chloroprene rubber itself, talcum...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09J151/00C09J145/00C09J157/02C09J193/04C08F287/00
Inventor 梁恒巨
Owner GUANGDONG ORIENT RESIN
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products