Sizing agent for dyeing light scattering layer on DSSC photoanode and preparation method thereof

A technology of solar cells and dye sensitization, applied in the field of solar cells, can solve the problems that the scattering layer slurry does not improve the performance of the cells significantly, cannot be market-oriented and mass-produced, and is difficult to mass-produce and industrialize. Effects of recycling efficiency, improvement of photoelectric conversion efficiency, and improvement of battery efficiency

Active Publication Date: 2014-05-14
KUSN INNOVATION INST OF NANJING UNIV
View PDF8 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] Disadvantages of this preparation technology: it is difficult to uniformly disperse and mix the particles in additives and pore-forming agents in the preparation of this technology, and it is easy to produce crack
[0011]Disadvantages of this technology: the preparation process of this technology is too complicated and redundant, it cannot be marketed and batched, and it is only limited to the laboratory, and the efficiency of the battery prepared by this technology is only It is 3.28%, and the current efficiency in the field of DSSC has already exceeded 10%, so such efficiency has no advantages and novelties in this field
[0014] Disadvantages of this technology: the preparation cycle is relatively long, at least two days, and the size of the hydrothermal kettle in the hydrothermal reaction restricts the preparation of slurry by this preparation technology Quantity, it is difficult to batch and industrialize, and the scattering layer slurry prepared by this technology is not obvious enough to improve the performance of the battery

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] Step (1): 4g of TiO with a particle size distribution range of 10-30nm 2 Nanopowder and 12g of TiO with a particle size of 0.4μm 2 powder mix;

[0043] Step (2): The TiO mixed in step (1) 2 Powder according to mass ratio TiO2 : Absolute ethanol=1:15 ratio, uniformly dispersed in absolute ethanol solution to form A solution;

[0044] Step (3): Prepare ethyl cellulose (#46080, viscosity 30-50mPa.s, purchased from Sigma) into 12wt% absolute ethanol solution to form B solution;

[0045] Step (4): Add solution B of step (3) dropwise to solution A of step (2), according to the mass ratio of TiO 2 : Ethyl cellulose = 1: 0.4 comparison dropwise addition of B solution;

[0046] Step (5): Add terpineol dropwise to step (4), according to the mass ratio of TiO 2 : Terpineol = 1:4 comparative drop;

[0047] Step (6): Stir the solution in step (5) mechanically for 2-3 hours to fully mix the solution evenly, and finally obtain a white colloidal emulsion;

[0048] Step (7): P...

Embodiment 2

[0050] Step (1): 8g of TiO with a particle size distribution range of 10-30nm 2 Nano powder and 8g of TiO with a particle size of 0.3 μm 2 powder mix;

[0051] Step (2): The TiO mixed in step (1) 2 Powder according to mass ratio TiO 2 : Absolute ethanol=1:15 ratio, uniformly dispersed in absolute ethanol solution to form A solution;

[0052] Step (3): Prepare ethyl cellulose (#46080, viscosity 30-50mPa.s, purchased from Sigma) into 10wt% absolute ethanol solution to form B solution;

[0053] Step (4): Add solution B of step (3) dropwise to solution A of step (2), according to the mass ratio of TiO 2 : Ethyl cellulose = 1:0.5 comparison drop B solution;

[0054] Step (5): Add terpineol dropwise to step (4), according to the mass ratio of TiO 2 : Terpineol = 1:5 comparative drop;

[0055] Step (6): Stir the solution in step (5) mechanically for 3 hours to fully mix the solution evenly, and finally obtain a white colloidal emulsion;

[0056] Step (7): Pour the solutio...

Embodiment 3

[0058] Step (1): 4g of TiO with a particle size distribution range of 10-30nm 2 Nano powder and 18g of TiO with a particle size of 0.2 μm 2 powder mix;

[0059] Step (2): The TiO mixed in step (1) 2 Powder according to mass ratio TiO 2 : Absolute ethanol=1:20 ratio, uniformly dispersed in absolute ethanol solution to form A solution;

[0060] Step (3): Prepare ethyl cellulose viscosity m9 (viscosity 8~10 mPa.s, Shanghai test) and m70 (viscosity 40~100 mPa.s, Shanghai test) according to the mass ratio of 1:1 to make 12wt % absolute ethanol solution to form B solution;

[0061] Step (4): Add solution B of step (3) dropwise to solution A of step (2), according to the mass ratio of TiO 2 : Ethyl cellulose = 1: 0.4 comparison dropwise addition of B solution;

[0062] Step (5): Add terpineol dropwise to step (4), according to the mass ratio of TiO 2 : Terpineol = 1:5 comparative drop;

[0063] Step (6): Stir the solution in step (5) mechanically for 3 hours to fully mix the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a sizing agent for dyeing a light scattering layer on a DSSC photoanode. The sizing agent is composed of TiO2 particles, ethylene cellulose and terpilenol, and the weight ratio of the TiO2 particles to the ethylene cellulose to the terpilenol is 1:0.2-0.5:2-8, wherein the TiO2 particles are formed by the fact that TiO2 nano particles of 10-30 nm and TiO2 particles of 0.2-0.4 micrometers are mixed in the proportion of 1:1-5 by weight. The sizing agent for the light scattering layer of the DSSC photoanode is formed by mixing big particle TiO2 and small particle TiO2 of an anatase structure in a certain proportion, the small particle TiO2 of 10 nm - 30 nm has a transition effect, combination of a transmission layer and a scattering layer is promoted, the cracking phenomenon of the photoanode after high temperature sintering is prevented, meanwhile, the optical distance is increased, and the cell efficiency is improved.

Description

technical field [0001] The invention relates to a slurry for a light scattering layer on a photoanode of a dye-sensitized solar cell and a preparation method thereof, belonging to the technical field of solar cells. Background technique [0002] As a new energy source, solar energy has attracted more and more attention under the environment of global warming and smog. Among various thin-film solar cells, dye-sensitized solar cells have attracted more and more attention due to their advantages such as simple manufacturing process, easy mass production, and low cost. In dye-sensitized solar cells, the performance of the porous photoanode is particularly important to the performance of the cell, so there have been more and more studies on the photoanode film over the years. [0003] In order to achieve as much dye adsorption as possible, while achieving a firm contact with the conductive substrate, and to realize the transport of electrons from the excited state of the dye to...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01G9/20H01G9/042
CPCY02E10/542
Inventor 文贵华顾军邹志刚
Owner KUSN INNOVATION INST OF NANJING UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com