Anti-corrosion recombined composite bamboo material and manufacturing method thereof
A manufacturing method and bamboo technology, which is applied in the field of anti-corrosion recombined bamboo and its manufacturing, can solve the difficult to meet the aesthetic and functional requirements of bamboo products, prone to rot, mildew and insects, affecting the aesthetics of bamboo products, etc. problem, to achieve the effect of expanding the application field of bamboo, good dimensional stability, and good insect resistance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0027] A kind of anti-corrosion recombination composite bamboo of the present invention, this anti-corrosion recombination composite bamboo is made with bamboo as main raw material, and its density is 1.2g / cm 3 , the water absorption thickness expansion rate in the thickness direction is 1.2%, and the water absorption thickness expansion rate in the width direction is 0.8%, reaching the strong corrosion resistance level, and the bacterial damage value reaches 0 level.
[0028] A kind of manufacture method of the anticorrosion recombined composite bamboo of above-mentioned present embodiment, comprises the following steps:
[0029] (1) First use a circular saw to cut the 3-year-old raw bamboo into 1.9m-long bamboo tubes, then use a bamboo splitter to cut the bamboo tube into 15 equal pieces of bamboo; then use a cutting machine to remove the green bamboo on the surface of the bamboo slices, At the same time, part of the bamboo yellow is removed; the bamboo slices are rolled by ...
Embodiment 2
[0041] A kind of anti-corrosion recombination composite bamboo of the present invention, this anti-corrosion recombination composite bamboo is made with bamboo as main raw material, and its density is 1.1g / cm 3 , the water absorption thickness expansion rate in the thickness direction is 1.0%, and the water absorption thickness expansion rate in the width direction is 0.7%, reaching the strong corrosion resistance level, and the bacterial damage value reaches 0 level.
[0042] A kind of manufacture method of the anticorrosion recombined composite bamboo of above-mentioned present embodiment, comprises the following steps:
[0043] (1) First use a circular saw to cut the 3-year-old raw bamboo into 1.9m-long bamboo tubes, then use a bamboo splitter to cut the bamboo tube into 18 equal pieces of bamboo; then use a splitter to remove the green bamboo on the surface of the bamboo slices At the same time, part of the bamboo yellow is removed; the bamboo slices are rolled by a bamboo...
PUM
Property | Measurement | Unit |
---|---|---|
Density | aaaaa | aaaaa |
Density | aaaaa | aaaaa |
Thickness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com