Moisture-resisting and oil-resistant epoxy self-bonding paint for electromagnetic wire and preparation method of epoxy self-bonding paint

A technology of electromagnetic wire and self-adhesive paint, which is applied in the field of enameled wire paint, can solve the problems of heat resistance level lower than 120°C, difficulty in meeting different environments, and insufficient strength, etc., to achieve heat resistance level improvement, stable and easy-to-control production process, and finished products The effect of consistency improvement

Inactive Publication Date: 2014-04-16
铜陵天河特种电磁线有限公司
View PDF5 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Enameled wire enamel is a necessary insulating material for the production of enameled wire. Enameled wire enamel requires good adhesion, mechanical strength, insulation performance, heat resistance, wear resistance, salt spray resistance and harsh environment resistance, etc., but ordinary wire enamel has resistance to It is difficult to meet the requirements of different environments due to problems such as thermal resistance, poor wear resistance, insufficient strength, and heat resistance below 120°C.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0013] The moisture-resistant and oil-resistant electromagnetic wire epoxy self-adhesive paint is characterized in that it is made of the following raw materials in parts by weight (kg): E-42 epoxy resin 12, phenolic resin 10, amino resin 8, nylon 12 12, Anilinomethyltriethoxysilane 3, 1,6-Hexanediol Diacrylate 3, Benzoin 1, Zinc Oxide 2, Polyamide Wax 1, Dicumyl Peroxide 2, Cocoic Acid Monoethanolamide 1, ACR anti-impact agent 5, aluminum oxide 12, additive 7, m-p-cresol 80, xylene 100;

[0014] The auxiliary agent is made of the following raw materials in parts by weight (kg): 0.2 nanometer mica powder, crosslinking agent TAC1, lauryl dimethylamine oxide 1, methyltriethoxysilane 1, silane coupling agent KH550 2 , dimethylaminopropylamine 1, triethyl citrate 5, dipentaerythritol hexaacrylate 7, propyl gallate 2, coix seed oil 2; the preparation method is to mix the materials, heat to 60-70°C, and stir to react 30-40 minutes, that is.

[0015] The preparation method comprise...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
bond strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses moisture-resisting and oil-resistant epoxy self-bonding paint for an electromagnetic wire. The moisture-resisting and oil-resistant epoxy self-bonding paint is characterized by being prepared from raw materials in parts by weight (kilogram) as follows: 12-15 parts of E-42 epoxy resin, 10-12 parts of phenolic resin, 8-10 parts of amino resin, 12-15 parts of nylon 12, 2-3 parts of anilino-methyl-triethoxysilane, 3-4 parts of 1,6-hexanediol diacrylate, 1-2 parts of benzoin, 2-3 parts of zinc oxide, 1-2 parts of polyamide wax, 2-3 parts of dicumyl peroxide, 1-2 parts of coconut oil monoethanolamide, 3-5 parts of an ACR (acrylate copolymer) impact resisting agent, 12-15 parts of aluminum oxide, 7-9 parts of an assistant, 80-90 parts of m, p-cresol and 100-120 parts of dimethylbenzene. The process is simple, the production process is stable and easy to control, and the consistency of finished products is improved substantially; the production process is environment-friendly; the epoxy self-bonding paint prepared with the method has excellent oil resistivity and good moisture resistance, and the temperature classification is improved, so that the service lives of the finished products are prolonged; and the bonding strength and the surface smooth finish of a coated wire are improved due to adding of the coupling agent and the assistant.

Description

technical field [0001] The invention relates to an enamelled wire varnish, in particular to a moisture-resistant and oil-resistant electromagnetic wire epoxy self-adhesive varnish meeting the heat resistance requirement of a heat level of 155°C and above and a preparation method thereof. Background technique [0002] Enameled wire is a kind of electrical material. It processes a thin layer of high-strength insulating layer on the surface of a round copper wire to insulate it from the outside world. According to the specifications, it can be processed into a wool thread thinner than a hair, and a yarn-covered thread as thick as a thumb. Enameled wire has good insulation effect and waterproof ability. It is widely used in electrical appliances, such as motors, generators, water pumps, electromagnets, electric welding machines, household appliances, wireless communications, speakers, telegraphs, transformers, etc. Enameled wire enamel is a necessary insulating material for th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D4/02C09D4/06C09D7/12C09D5/25
Inventor 张勇进方小辉章小虎刘琛胡强
Owner 铜陵天河特种电磁线有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products