Random-texture pigment liquid for air die material and application of pigment liquid

A technology of inflatable material and pigment liquid, which is applied in the field of pigment liquid, can solve the problems of inconspicuous color contrast, unclear surface texture of inflatable material, poor visual effect, etc., and achieve natural and clear lines, not easy to change color, and increase thixotropy Effect

Active Publication Date: 2014-04-02
FUJIAN SIJIA ENVIRONMENTAL PROTECTION MATERIAL TECH
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, the currently used pattern paint solution is easily miscible into the background paint solution, resulting in unclear surface texture of the produced inflatable material, inconspicuous color contrast, and poor visual effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0089] The preparation method of the titanium dioxide slurry comprises the following steps: firstly adding a dispersant and epoxy soybean oil to a plasticizer, stirring evenly, then adding titanium dioxide, stirring to form a paste, soaking for 24h to 48h, and then Grinding on a three-roll mill, the grinding fineness is 20~25μm.

[0090] The pigment liquid for random grain inflatable material according to the present invention, wherein the color paste contains the following components in parts by weight:

[0091] 100 parts of toner;

[0092] Epoxidized soybean oil 0.5~1.5 parts;

[0093] 90~140 parts of plasticizer;

[0094] Dispersant 1~2 parts;

[0095] UV absorber 1~3 parts.

[0096] Further, the preparation method of the color paste includes the following steps: firstly add the dispersant, epoxidized soybean oil, and ultraviolet absorber to the plasticizer, stir evenly, then add the toner, stir to form a paste, soak for 3 Day or more, and then grind on a three-roller ...

Embodiment 1

[0100] 1. Weigh the raw materials for preparing titanium dioxide slurry according to the following formula:

[0101] 100 parts of titanium dioxide;

[0102] 0.5 part of epoxidized soybean oil;

[0103] 45 parts of plasticizer;

[0104] Dispersant 2 parts.

[0105] The preparation method of the titanium dioxide slurry comprises the following steps: firstly adding a dispersant and epoxy soybean oil to a plasticizer, stirring evenly, then adding titanium dioxide, stirring to form a paste, soaking for 24h to 48h, and then Grind on a three-roll mill, the grinding fineness is 20~25μm, and then set aside.

[0106] 2. Weigh the raw materials for preparing color paste according to the following formula:

[0107] 100 parts of toner;

[0108] 1.5 parts of epoxidized soybean oil;

[0109] 90 parts of plasticizer;

[0110] 2 parts of dispersant;

[0111] UV absorber 1 part.

[0112] The preparation method of the color paste comprises the following steps: firstly add the dispersant...

Embodiment 2

[0133] 1. Weigh the raw materials for preparing titanium dioxide slurry according to the following formula:

[0134] 100 parts of titanium dioxide;

[0135] 1.5 parts of epoxidized soybean oil;

[0136] 40 parts of plasticizer;

[0137] Dispersant 4 parts.

[0138] The preparation method of the titanium dioxide slurry comprises the following steps: firstly adding a dispersant and epoxy soybean oil to a plasticizer, stirring evenly, then adding titanium dioxide, stirring to form a paste, soaking for 24h to 48h, and then Grind on a three-roll mill, the grinding fineness is 20~25μm, and then set aside.

[0139] 2. Weigh the raw materials for preparing color paste according to the following formula:

[0140] 100 parts of toner;

[0141] 0.5 part of epoxidized soybean oil;

[0142] 140 parts of plasticizer;

[0143] 1 part of dispersant;

[0144] 3 parts of UV absorber.

[0145] The preparation method of the color paste comprises the following steps: firstly add the disper...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses random-texture pigment liquid for an air die material. The pigment liquid consists of the following components in parts by weight: 100 parts of PVC (Polyvinyl Chloride) paste resin, 50-60 parts of a plasticizer, 10-20 parts of calcium carbonate, 1-5 parts of fumed silica, 2-3 parts of a liquid barium-zinc stabilizer, 10-30 parts of titanium dioxide paste, 5-20 parts of color paste and 0.5-3 parts of an adhesive. The pigment liquid for the random texture air die material, which is disclosed by the invention, has the advantages of high dispersity, freeness from color strips, weather resistance and resistance to color fading and color change; meanwhile, after the content of the pigment liquid is adjusted, the pigment liquid can be taken as background pigment liquid as well as texture pigment liquid as well as pigment liquid for the air die material. The background pigment liquid and the texture pigment liquid are used in a matching manner, so that the prepared air die material is high in surface color contrast, natural and clear strips and freeness from air bubbles on the surface.

Description

technical field [0001] The invention relates to a pigment liquid for an air-model material, in particular to a pigment liquid for a random-grain air-model material and an application thereof. Background technique [0002] The preparation process of the inflatable material is generally as follows: polyester fiber mesh is used as the base material, the polyester fiber mesh is first impregnated with PVC paste, and then the background pigment solution is coated on the surface of the polyester fiber mesh, and the texture is simultaneously coated. Pigment solution, and finally dried to obtain the air mold material with colored surface. [0003] However, the currently used pattern paint solution is easily miscible into the background paint solution, resulting in unclear surface texture, inconspicuous color contrast and poor visual effect of the produced inflatable material. Contents of the invention [0004] In order to overcome the deficiencies in the prior art, the object of t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D06P1/52D06P1/673D06P3/52D06M15/248D06M101/32
Inventor 林生雄张宏旺黄万能蒋石生邓中文
Owner FUJIAN SIJIA ENVIRONMENTAL PROTECTION MATERIAL TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap