Alloy steel material for rotor of cam rotor pump and preparation method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A cam rotor pump and alloy steel technology is applied in the field of metal material preparation to achieve the effects of good wear resistance, improved yield and reduced inclusion oxides
Active Publication Date: 2014-03-26
江苏建星交通工程有限公司
View PDF6 Cites 3 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0003] There are many kinds of alloy steels for pump valves, and the technology has made great progress, but there are still many problems, such as wear resistance, hardness, rust resistance, corrosion resistance, high and low temperature resistance, brittleness, toughness, etc. Many occasions still cannot meet the requirements of production, and further improvement is needed to improve production efficiency, reduce costs, improve safety, provide guarantee for the development of high-tech, and provide impetus for social development. The task is still very arduous
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0014] A cam rotor pump rotor alloy steel material, which contains chemical element components and mass percentages: carbon 0.2-0.3, silicon 0.2-0.4, titanium 1.2-1.5, boron 0.02-0.05, chromium 4.2-4.5, manganese 2.2- 2.5, molybdenum 0.4-0.6, zinc 0.2-0.4, In0.02-0.05, As0.3-0.5, Hf0.08-0.12, Bi0.15-0.18, P≤0.030, S≤0.030, the balance is iron.
[0015] The production method of the rotor alloy steel material of the rotor cam pump is as follows:
[0016] (1) Prepare pig iron and scrap iron in a ratio of 1:1.2 as the source of iron matrix, put pig iron into the furnace for melting, perform desulfurization, deoxidation, use refining agent for one-time refining, add alloy components for alloying, and then add scrap iron to melt , adding refining agent for secondary refining, testing and adjusting the content of chemical elements to pass, casting, post-casting heat treatment, etc.;
[0017] (2) The batch sequence of alloying elements put into the furnace during the alloying process...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
tensile strength
aaaaa
aaaaa
yield strength
aaaaa
aaaaa
impact absorption energy
aaaaa
aaaaa
Login to view more
Abstract
The invention relates to an alloy steel material for a rotor of a cam rotor pump, which comprises the following chemical element components in percentage by mass: 0.2-0.3% of carbon, 0.2-0.4% of silicon, 1.2-1.5% of titanium, 0.02-0.05% of boron, 4.2-4.5% of chromium, 2.2-2.5% of manganese, 0.4-0.6% of molybdenum, 0.2-0.4% of zinc, 0.02-0.05% of In, 0.3-0.5% of As, 0.08-0.12% of Hf, 0.15-0.18% of Bi, no more than 0.030% of P, no more than 0.030% of S and the balance of iron. According to the invention, the alloy steel formed by combination of multiple raw materials such as boron, hafnium and the like has the characteristics of high strength, high hardness, favorable wear resistance and corrosion resistance; part of waste iron is used as a raw material and is subjected to secondary refining, so that the quality is stabler and more uniform, and the content of harmful elements such as sulfur, phosphorus and the like is lower; and a refining agent is added, so that the porosity is reduced by 1-2 levels, and the oxide inclusion is approximately at Level 2.
Description
technical field [0001] The invention relates to the field of metal material preparation, in particular to a cam rotor pump rotor alloy steel material and a preparation method thereof. Background technique [0002] The development of alloy steel has a history of more than 100 years. So far, a variety of alloy steels have been applied in industry, mainly including the following types: quenched and tempered steel, spring steel, rolling bearing steel, tool steel, special performance steel, Various alloy steels with excellent properties such as heat-resistant steel and low-temperature steel. [0003] There are many kinds of alloy steels for pump valves, and the technology has made great progress, but there are still many problems, such as wear resistance, hardness, rust resistance, corrosion resistance, high and low temperature resistance, brittleness, toughness, etc. In many occasions, the production requirements cannot be met, and further improvements are needed to improve pro...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more