A kind of water-based epoxy anticorrosion coating for steel structure

A technology of water-based epoxy and anti-corrosion coatings, applied in the field of coatings, can solve the problems of toxicity and unsatisfactory paint film performance, achieve excellent oil resistance and corrosion resistance, excellent wear resistance and corrosion medium resistance, and improve the quality of coatings.

Inactive Publication Date: 2016-04-20
CHANGZHOU CITY LATE COATINGS
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the water-based epoxy coatings currently on the market can be water-based, they still contain a small amount of alcohol ether solvents, which will produce certain toxicity. Although some can meet environmental protection requirements, their paint film performance is not ideal.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of water-based epoxy anticorrosion coating for steel structure
  • A kind of water-based epoxy anticorrosion coating for steel structure
  • A kind of water-based epoxy anticorrosion coating for steel structure

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] Weigh the following raw materials according to weight unit: 60 parts by weight of water-based epoxy resin, 8.8 parts by weight of deionized water, 0.9 parts by weight of dispersant (SN5040), 0.1 part by weight of defoamer (SN-154), wetting agent (OP- 10) 0.6 parts by weight, 5 parts by weight of ultrafine zinc phosphate, 5 parts by weight of titanium ash powder, 9 parts by weight of hollow glass microspheres, 6 parts by weight of microsilica powder, 3 parts by weight of precipitated barium sulfate, thickener (ACRYSOLASE‐60) 0.3 parts by weight, 1.2 parts by weight of anti-metal corrosion agent (metal chelate of ethylenediaminetetraacetic acid), 0.1 parts by weight of fungicide in the tank; 30 parts by weight of water-based epoxy curing agent.

[0023] Control the dispersion speed of the high-speed disperser at 300 rpm, and add water-based epoxy resin, deionized water, dispersant, defoamer, and wetting agent in sequence. When adding the dispersant, defoamer, and wetting a...

Embodiment 2

[0031] Weigh the following raw materials according to weight unit: 50 parts by weight of water-based epoxy resin, 5.3 parts by weight of deionized water, 0.5 parts by weight of dispersant (SN5040), 0.5 parts by weight of defoamer (SN-154), wetting agent (OP- 10) 0.4 parts by weight, 8 parts by weight of ultrafine zinc phosphate, 12 parts by weight of titanium ash powder, 10 parts by weight of hollow glass microspheres, 6 parts by weight of silicon micropowder, 4 parts by weight of precipitated barium sulfate, thickener (ACRYSOLASE-60) 0.6 parts by weight, 2.5 parts by weight of an anti-metal corrosion agent (a chelated zinc compound of ethylenediaminetetraacetic acid and dialkyl dithiophosphoric acid), 0.2 parts by weight of a fungicide in a tank, and 30 parts by weight of a water-based epoxy curing agent.

[0032] Control the dispersion speed of the high-speed disperser at 300 rpm, and add water-based epoxy resin, deionized water, dispersant, defoamer, and wetting agent in seq...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to an aqueous anticorrosive epoxy coating for steelworks. The coating is composed of a component A and a component B, a weight ratio of the component A to the component B is 100:30, the component A is composed of 50-65 parts of an aqueous epoxy resin, 5-13 parts of deionized water, 0.4-0.9 parts of a dispersant, 0.1-0.6 parts of an antifoaming agent, 0.3-0.6 parts of a wetting agent, 4-10 parts of ultrafine zinc phosphate, 5-12 parts of titanium ash, 9-22 parts of hollow glass bead, 6-12 parts of silicon micro-powder, 3-6 parts of precipitated barium sulfate, 0.3-0.6 parts of a thickening agent, 1.2-2.5 parts of a metal corrosion inhibitor, and 0.1-0.2 parts of an in-tank bactericide; and the component B is an aqueous epoxy hardener. The coating is a completely-aqueous environmentally-friendly coating, contains no chemical solvents, has better wear and corrosion medium resistances than like coatings after film solidification, and can effectively reduce the product cost.

Description

technical field [0001] The invention belongs to the technical field of coatings, and in particular relates to a water-based epoxy anticorrosion coating for steel structures. Background technique [0002] At present, global environmental protection has been paid more and more attention to, and the development and promotion of environmentally friendly low-VOC or even zero-VOC environmentally friendly high-performance anti-corrosion coatings has a broad prospect. Although the water-based epoxy coatings currently on the market can be water-based, they still contain a small amount of alcohol-ether solvents, which will produce certain toxicity. Although some can meet environmental protection requirements, their paint film performance is not ideal. Contents of the invention [0003] In order to solve the shortcomings in the above-mentioned technical problems, the present invention provides a water-based epoxy anti-corrosion coating for all water-based environment-friendly steel s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D163/00C09D5/08C09D7/12
Inventor 周永荣吴善林周建定周剑辉
Owner CHANGZHOU CITY LATE COATINGS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com