Propylene butene high melt strength polypropylene foam board or sheet and preparation method thereof

A high-melt-strength, foamed sheet technology, applied in the polymer field, can solve the problems of increasing low-molecular-weight random substances, high n-hexane extract, limited application scope, etc., to meet the requirements of food hygiene, and to achieve smooth self-skinning. , The effect of the process is easy to adjust

Active Publication Date: 2015-09-16
CHINA PETROLEUM & CHEM CORP +1
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the low molecular weight part of ethylene propylene random copolymerization polypropylene often has too high ethylene content, thereby increasing the content of low molecular random substances in the product, resulting in a high n-hexane extract of the product, which limits its application range, especially In the field of food hygiene packaging

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Propylene butene high melt strength polypropylene foam board or sheet and preparation method thereof
  • Propylene butene high melt strength polypropylene foam board or sheet and preparation method thereof
  • Propylene butene high melt strength polypropylene foam board or sheet and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0031] Preparation of matrix resin HMSPP301

[0032] The polymerization reaction was carried out on a polypropylene pilot plant. Its main equipment includes prepolymerization reactor, first loop reactor and second loop reactor.

[0033] Pre-polymerization reaction: the main catalyst (titanium-containing solid catalyst active component) is obtained by the method described in Example 1 of Chinese patent CN93102795, the Ti content is 2.4wt%, the Mg content is 18.0wt%, and the di-n-phthalic acid The butyl ester content is 13 wt%. The main catalyst, co-catalyst (triethylaluminum), and the first external electron donor (dicyclopentyldimethoxysilane, DCPMS) are pre-contacted at 10°C for 20 minutes, and then continuously added to the pre-polymerization reactor for pre-polymerization. In the polymerization reactor, the pre-polymerization is carried out in the environment of the propylene liquid phase bulk, the temperature is 15°C, and the residence time is about 4 minutes. Under this...

Embodiment 1~10

[0045] Put 100 parts by weight of high melt strength polypropylene HMSPP301 or HMSPP302, foaming agent (azodicarbonamide, namely industrial grade AC foaming agent), cell control agent (talc powder) and additives into a high-speed mixer at high speed After mixing for 1 minute, add the middle layer twin-screw, the torque is controlled at about 65%, and the speed is 10-170rpm. Among them, the additives include acid absorbing agent calcium stearate, antioxidant (calcium stearate with a weight ratio of 1:2:2, BASF antioxidant 1010 and antioxidant 168 compounded, accounting for 0.2 parts by weight in total) and Lubricant MB50-002 (high molecular weight polysiloxane), the weight parts of cell control agent, foaming agent and lubricant are shown in Table 3; the foaming temperature and the density of the product sheet are shown in Table 3, using specific GB / T1033 .1-2008 for density measurements. Examples 1~3 and 6~10 use high melt strength polypropylene HMSPP301, and Examples 4~5 use...

Embodiment 11

[0047] The remaining steps are the same as in Examples 1-10, and the specific data are shown in Table 3; only the blowing agent is changed from azodicarbonamide to 5 parts by weight of dinitrosopentamethylenetetramine.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
melt flow indexaaaaaaaaaa
melting pointaaaaaaaaaa
Login to View More

Abstract

The invention provides a polypropylene foamed board or sheet. The foamed board or sheet is prepared by foaming a base resin high-melt-strength polypropylene with a foaming agent, wherein the high-melt-strength polypropylene has the following characteristics: the melt index MFR is 0.2-10 g / 10 minutes, the molecular weight distribution Mw / Mn is 6-20, the content of substances with the molecular weight of greater than 5 million is greater than or equal to 0.8 wt%, the M[z+1] / Mn is greater than or equal to 70, and the butylene content is 0.1-15 wt%. The high-melt-strength polypropylene with wide molecular weight distribution is utilized as the raw material to implement stabilization of the polypropylene raw material, so that the foaming window is effectively enlarged, and the technique is easy to adjust; the method can be used for preparing the polypropylene foamed board or sheet with the density of 0.2-0.9 g / cm<3> and the thickness of 0.1-400mm, which has the advantages of smooth surface crust, uniform pore diameter and close-pore hard structure; and the polypropylene foamed board or sheet can be widely used in the fields of thermal insulation tableware, automobile interior ornaments, architectural moldboards, camping supplies, decorating material interlayers, product damping packages and the like.

Description

technical field [0001] The invention relates to the field of macromolecules, in particular to a propylene-butylene copolymerized high-melt-strength polypropylene foam board or sheet and a preparation method thereof. Background technique [0002] Foamed materials mainly include foamed beads, foamed plates or sheets and other apparent forms; foamed plates or sheets are widely used in containers, building materials, auto parts and impact energy absorbing materials. Compared with polystyrene foam board or sheet, polypropylene (PP) foam board or sheet has excellent rigidity and thermal stability, and the demand for it has been increasing in recent years. Polypropylene foamed boards and sheets are mainly obtained by extrusion foaming. Specifically, the mixing and melting of the foaming components are directly completed in the extruder, and the foaming is completed by decomposing and overflowing the foaming agent at the machine head. bubble process. [0003] Compared with foamed ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L23/14C08J9/04C08J9/10C08J9/12C08F210/06
CPCC08F210/06C08J9/103C08J9/105C08J9/107C08J2203/04C08J2205/052C08J2323/14C08L23/14C08L2201/06C08L2201/08C08L2203/14C08F210/08C08F2500/04C08F2500/11C08F4/6465
Inventor 郭鹏吕明福张师军刘有鹏董穆刘建叶
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com