A high-hardness alloy steel and pump valve technology, applied in the field of metal material preparation, can solve harsh and demanding problems, and achieve high fatigue strength, low cost, and good casting performance

Inactive Publication Date: 2014-03-19
TONGLING SIDE TECH
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002]Pumps and valves work in various and harsh environments, and have high requirements for materials. At present, there are many kinds of alloy steels used for pumps and valves, and the technology has made great progress, but There are still many problems, such as wear resistance, hardness, antirust performance, corrosion resistance, high and low temperature resistance, brittleness, toughness, etc., which cannot meet the production requirements in many occasions, and further improvement is needed to increase production efficiency. , reduce costs, improve safety, provide guarantee for the development of high-precision technology, and provide impetus for social development, the task is still very arduous

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0013] A high-hardness alloy steel material for pump valves, which contains chemical element components and mass percentages: carbon 0.9-1.4, silicon 0.8-1.1, manganese 2.1-2.4, chromium 0.6-0.8, vanadium 0.03-0.05, molybdenum 0.12 -0.14, lanthanum 0.01-0.02, magnesium 2.1-2.3, W0.04-0.06, Tm0.12-0.16, S≤0.04, P≤0.04, and the balance is iron.

[0014] The production method of the high-hardness alloy steel material for the pump valve is:

[0015] (1) Prepare pig iron and scrap iron in a ratio of 1:3 as the source of iron matrix, put pig iron into the furnace for melting, perform desulfurization, deoxidation, use refining agent for primary refining, add alloy components for alloying, and then add scrap iron to melt , adding refining agent for secondary refining, testing and adjusting the content of chemical elements to pass, casting, post-casting heat treatment, etc.;

[0016] (2) The batch sequence of alloying elements put into the furnace during the alloying process is: (1) s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
yield strengthaaaaaaaaaa
impact absorption energyaaaaaaaaaa
Login to view more

Abstract

A high-hardness alloy steel material for pump valves comprises the following chemical element components by mass percent: 0.9-1.4% of carbon, 0.8-1.1% of silicon, 2.1-2.4% of manganese, 0.6-0.8% of chromium, 0.03-0.05% of vanadium, 0.12-0.14% of molybdenum, 0.01-0.02% of lanthanum, 2.1-2.3% of magnesium, 0.04-0.06% of W, 0.12-0.16% of Tm, not more than 0.04% of S, not more than 0.04% of P, and the balance of iron. The low alloy steel provided by the invention not only has high hardness, but also has good toughness, good wear resistance, high thermal strength, low dynamic load gap sensitivity, and high fatigue strength, and also is good in casting performance, and high in casting yield. The method of the invention partly adopts scrap iron as a raw material; secondary refining is performed; heat treatment temperature after casting is controlled reasonably; raw materials are fed in batches; and thus the alloy is provided with more stable and uniform quality, and improved comprehensive mechanical properties.

Description

technical field [0001] The invention relates to the field of metal material preparation, in particular to a high-hardness alloy steel material for pump valves and a preparation method thereof. Background technique [0002] The working environment of pump valves is diverse and harsh, and the requirements for materials are very high. At present, there are many kinds of alloy steel used in pump valves, and the technology has made great progress, but there are still many problems, such as wear resistance, hardness, rust resistance Performance, corrosion resistance, high and low temperature resistance, brittleness, toughness, etc., cannot meet the production requirements in many occasions, and further improvement is needed to improve production efficiency, reduce costs, and improve safety. Guaranteeing and providing impetus for social development are still arduous tasks. Contents of the invention [0003] The object of the present invention is to provide a high-hardness alloy ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/38C22C33/04C21D6/00
Inventor 孔华英
Owner TONGLING SIDE TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap