A kind of sheath material for control signal cable and preparation method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology for controlling signals and sheath materials, applied in the direction of insulated cables, cables, circuits, etc., can solve the problems affecting the service life of the sheath, heat resistance, cold resistance, weather resistance and aging resistance, etc., to achieve excellent wear resistance, Good high and low temperature resistance, prolonging the service life
Active Publication Date: 2016-01-27
滁州三界外信息科技有限公司
View PDF3 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
At present, domestic control signal cable sheaths usually use polyvinyl chloride or polyethylene as the sheath material. However, the above materials are not ideal in terms of heat resistance, cold resistance, and weather aging resistance, which greatly affects the service life of the sheath.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0010] A sheath material for control signal cables, made of the following raw materials in weight (kg): 70 low-density polyethylene, 20 SG-3 polyvinyl chloride, 20 styrene-butadiene rubber, HIPS7, 10 nano-calcium carbonate, and nano-kaolin 10. Ultrafine mica powder 8, naphthenic oil 5, sulfur 2, accelerator M2, zinc oxide 2, stearic acid 3, phenolic resin 6, antioxidant 10102, tert-butyl peroxybenzoate 0.8, oxidized polyethylene wax 4. Rosin pentaerythritol ester 5, accelerator TMTD1, diisobutyl phthalate 8, dioctyl nylon acid 10, composite filler 5;
[0011] The preparation method of the composite filler is as follows: a. Take bentonite, barite, and monazite in a weight ratio of 4:4:3, then add 2% coal powder and 1.5% activated carbon by weight of bentonite, and mix them evenly at 550 ° C. Calcined for 4 hours, cooled to room temperature, crushed to a particle size below 15 μm, then added water to make a slurry with a concentration of 45%, added hydrochloric acid solution wit...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
tensile strength
aaaaa
aaaaa
elongation at break
aaaaa
aaaaa
Login to view more
Abstract
The invention discloses a sheath material for a signal controlling cable and a preparation method thereof. The sheath material comprises the following raw materials in parts by weight: 65-75 parts of low density polyethylene, 20-30 parts of SG-3 type polyvinyl chloride, 15-25 parts of styrene butadiene rubber, 5-10 parts of HIPS, 10-15 parts of nano calcium carbonate, 8-12 parts of nano kaolin, 5-10 parts of an ultrafine mica powder, 3-6 parts of naphthenic oil, 2-3 parts of sulfur, 1-2 parts of an accelerant M, 1-2 parts of zinc oxide, 3-4 parts of stearic acid, 4-8 parts of phenolic resin, 2-3 parts of an anti-aging agent 1010, 0.5-1 part of tert-butyl peroxybenzoate, 3-5 parts of oxidized polyethylene wax, 4-6 parts of rosin pentaerythrityl ester, 1-2 parts of an accelerant TMTD, 5-10 parts of diisobutyl phthalate, 8-12 parts of dioctyl nylon acid ester, 3-6 parts of a composite filler. The sheath material has good high and low temperature resistance and high tensile strength, also has excellent abrasion resistance, acid and alkali resistance, oil resistance, ozone aging resistance, and ultraviolet radiation resistance, extends the service life of a sheath to a great extent, and widens the application scope.
Description
technical field [0001] The invention relates to a cable sheath material and a preparation method thereof, in particular to a sheath material for a control signal cable and a preparation method thereof. Background technique [0002] The cable jacket plays a vital role in protecting the internal components from damage to maintain their normal operation, so the jacket material must be able to resist sun and rain, ultraviolet radiation, ozone aging, chemical attack and withstand high temperature and severe cold And other harsh environmental conditions, while still ensuring normal work under accidental disasters. At present, domestic control signal cable sheaths usually use polyvinyl chloride or polyethylene as the sheath material. However, the above materials are not ideal in terms of heat resistance, cold resistance, and weather aging resistance, which greatly affects the service life of the sheath. Contents of the invention [0003] The purpose of the present invention is t...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.