Special PVDC (Polyvinyl Dichloride) latex for lining paper and preparation method of special PVDC latex

A technology of lining paper and latex, which is applied in papermaking, paper coating, textiles and papermaking, etc. It can solve the problems of unsatisfactory packaging requirements, poor stiffness of lining paper, etc., and achieve good environmental protection performance and good stability.

Active Publication Date: 2013-10-09
HAINAN SHINER IND
View PDF9 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

For example, the PVDC latex for cellophane coating and its preparation method and application involved in patent CN103059200A, the special PVDC latex for kraft paper used in food packaging and its preparation method and application involved in CN103059195A, and the special PVDC latex for oily paper used in food packaging involved in CN103059194A And its production method and application. The PVDC latex mentioned in the above patents has poor stiffness when applied to the inner lining paper, which cannot meet the needs of modern high-speed cigarette packaging.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Special PVDC (Polyvinyl Dichloride) latex for lining paper and preparation method of special PVDC latex
  • Special PVDC (Polyvinyl Dichloride) latex for lining paper and preparation method of special PVDC latex
  • Special PVDC (Polyvinyl Dichloride) latex for lining paper and preparation method of special PVDC latex

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] Raw material of PVDC latex for lining paper:

[0035] Mixed monomer 50kg;

[0036] Vinylidene chloride 39kg;

[0037] Methacrylamide 9kg;

[0038] Ethyl acrylate 1.5kg;

[0039] Acrylic acid 0.5kg;

[0040] Additives: 15g of ammonium acetate, 0.5g of ferrous chloride, 3kg of nano inorganic silicon;

[0041] Initiator: benzoyl peroxide 100g and N,N-diethylaniline 150g;

[0042] Emulsifier: sodium alkyl succinate sulfonate 500g and polyacrylamide 500g;

[0043] Seed emulsifier: sodium lauryl sulfate 100g and OP-7 emulsifier 200g;

[0044] Deionized water 54kg.

[0045] 1) Preparation of raw materials:

[0046] (1) Preparation of mixed monomers, mixing vinylidene chloride, methacrylamide, acrylate and acrylic acid of the above weight, and stirring for 1.5h to prepare mixed monomers;

[0047] (2) preparation of emulsifier, sodium alkyl succinate sulfonate 500g and polyacrylamide 500g add 6kg deionized water to make emulsifier solution;

[0048] (3) the preparation...

Embodiment 2

[0054] Raw material of PVDC latex for lining paper:

[0055] Mixed monomer 50kg;

[0056] Vinylidene chloride 40kg;

[0057] Methacrylamide 8kg;

[0058] Butyl acrylate 1.75kg;

[0059] Acrylic acid 0.25kg;

[0060] Additives: 15g of ammonium acetate, 0.5g of ferrous chloride, 3kg of nano inorganic silicon;

[0061] Initiator: benzoyl peroxide 100g and N,N-diethylaniline 150g;

[0062] Emulsifier: sodium alkyl succinate sulfonate 500g and polyacrylamide 500g;

[0063] Seed emulsifier: sodium lauryl sulfate 100g and OP-7 emulsifier 200g;

[0064] Deionized water 54kg.

[0065] 1) Preparation of raw materials:

[0066] (1) Preparation of mixed monomers, mixing vinylidene chloride, methacrylamide, acrylate and acrylic acid of the above weight, and stirring for 1.5h to prepare mixed monomers;

[0067] (2) preparation of emulsifier, sodium alkyl succinate sulfonate 500g and polyacrylamide 500g add 6kg deionized water to make emulsifier solution;

[0068] (3) the preparati...

Embodiment 3

[0073] Raw material of PVDC latex for lining paper:

[0074] Mixed monomer 55kg;

[0075] Vinylidene chloride 44.55kg;

[0076] Methacrylamide 7.7kg;

[0077] Ethyl acrylate 1.47kg;

[0078] Acrylic acid 0.28kg;

[0079] Additives: 15g of ammonium acetate, 0.5g of ferrous chloride, 2kg of nano-organic silicon;

[0080] Initiator: benzoyl peroxide 200g and N,N-diethylaniline 150g;

[0081] Emulsifier: sodium alkyl succinate sulfonate 500g and polyacrylamide 1kg;

[0082] Seed emulsifier: sodium lauryl sulfate 200g and OP-7 emulsifier 200g;

[0083] 49kg of deionized water.

[0084] 1) Preparation of raw materials:

[0085] (1) Preparation of mixed monomers, mixing vinylidene chloride, methacrylamide, acrylate and acrylic acid of the above weight, and stirring for 1.5h to prepare mixed monomers;

[0086] (2) preparation of emulsifier, sodium alkyl succinate sulfonate 500g and polyacrylamide 1kg add 6kg deionized water to make emulsifier solution;

[0087] (3) the prepa...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to special PVDC (Polyvinyl Dichloride) latex for lining paper. The PVDC latex comprises the following raw materials: a mixed monomer, auxiliaries, an initiator, an emulsifying agent, a seed emulsifying agent and deionized water, wherein the auxiliaries include ammonium acetate, ferrous chloride and nano inorganic silicon. The inorganic silicon in the nano inorganic silicon is one or more of silicon dioxide, silicon disulfide, sodium silicate, potassium metasilicate, aluminum silicate, calcium silicate, silicic acid and silicon carbide. The invention also provides a preparation method of the special silicon disulfide for lining paper. The auxiliary, namely the nano inorganic silicon is added into the PVDC latex, so that the stiffness of a paper sheet is increased effectively; in addition, the mixed monomer containing vinylidene chloride, methacrylamide, acrylic ester and acrylic acid as well as the initiator, the emulsifying agent, the seed emulsifying agent and the auxiliaries are adopted, so that the PVDC latex is prepared; and the prepared PVDC latex has good stability and has the characteristics of environmental friendliness, good air and oxygen resistance and particularly high stiffness when used for packaging cigarettes after being coated on the lining paper.

Description

technical field [0001] The invention relates to a special PVDC latex for lining paper and a preparation method thereof, which belongs to the field of new polymer materials. Background technique [0002] Cigarette lining paper is the paper packed between cigarette sticks and cigarette packs, and its main function is to prevent moisture and preserve fragrance. Cigarette lining papers currently used in the domestic and foreign markets include: 1. Composite aluminum foil lining paper, such as patent application CN1378013A, its production process is simple, and it is mainly made of aluminum foil, base paper and composite glue through composite equipment. Strong resistance, good barrier performance. However, the aluminum foil used is not easy to degrade and recycle, and does not meet the requirements of establishing an environmentally friendly society; 2. Vacuum aluminized lining paper, which is characterized by a low amount of aluminum, which is only 1 / 200 of the composite alumi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08F214/08C08F220/56C08F220/18C08F220/06C08F2/30C08F2/26C08F2/44C08K3/36C08K3/34D21H19/40D21H19/44D21H19/58D21H19/64
Inventor 邢青涛袁业兴朱海
Owner HAINAN SHINER IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com