Thermal treatment process of low-alloy steel casting

A low-alloy steel and casting technology, applied in the field of heat treatment process of low-alloy steel castings, can solve the problems of easy to produce temper brittleness, poor toughness of low-alloy steel castings, environmental pollution, etc., to reduce environmental pollution and safety hazards, meet the Strength and hardness requirements, the effect of reducing environmental pollution

Inactive Publication Date: 2013-09-11
YINGSHAN HUAMAO SHIP OUTFITTING EQUIP
View PDF1 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the heat treatment process of low-alloy steel castings generally adopts normalizing-quenching-tempering, in which quenching medium uses quenching oil, and its ratio is 1:10 by weight, that is, 1 ton of castings is put into 10 tons of quenching oil to ensure the quenching effect After the quenching oil has been used for a period of time, the oxidized powder of the casting and the carbonization of the medium oil will increase the viscosity of the quenching oil and reduce the oil volume, and new quenching oil must be added, resulting in high oil quenching costs; Fire will bring potential safety hazards, and a large amount of harmful substances will be produced during quenching, causing pollution to the environment
The tempering temperature of conventional low-alloy steel is 550-560°C, and the cooling method is to cool out of the furnace when the temperature is lower than 200°C. The low-alloy steel castings treated by the above heat treatment process have poor toughness, and the bending angle is lower than 80°, which cannot meet the requirements. The demand for high toughness, and the above cooling method, when the casting temperature is in the range of 200-400 ℃, it is easy to produce temper brittleness, which will reduce the mechanical properties of the casting

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Thermal treatment process of low-alloy steel casting
  • Thermal treatment process of low-alloy steel casting
  • Thermal treatment process of low-alloy steel casting

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] The heat treatment process steps of the low-alloy steel casting of the present embodiment are as follows:

[0024] (1) Normalizing: Put the low-alloy steel casting in the normalizing furnace, raise the temperature to 870°C, keep it warm for 3 hours, and cool it to room temperature after taking it out of the furnace;

[0025] (2) Quenching: Place the low-alloy steel casting in a quenching furnace, raise the temperature to 850°C, keep it warm for 2.5 hours, and cool it to room temperature with water;

[0026] (3) Tempering: Place the low-alloy steel casting in a tempering furnace, raise the temperature to 700°C, keep it warm for 3 hours, and then take it out of the furnace and air-cool it to room temperature.

Embodiment 2

[0028] The heat treatment process steps of the low-alloy steel casting of the present embodiment are as follows:

[0029] (1) Normalizing: Place the low-alloy steel casting in a normalizing furnace, raise the temperature to 880°C, keep it warm for 2.5 hours, and cool it to room temperature after taking it out of the furnace;

[0030] (2) Quenching: Place the low-alloy steel casting in a quenching furnace, raise the temperature to 860°C, keep it warm for 3 hours, and cool it to room temperature after taking it out of the furnace;

[0031] (3) Tempering: Place the low-alloy steel casting in a tempering furnace, raise the temperature to 710°C, keep it warm for 3 hours, and then take it out of the furnace and air-cool it to room temperature.

Embodiment 3

[0033] The heat treatment process steps of the low-alloy steel casting of the present embodiment are as follows:

[0034] (1) Normalizing: Place the low-alloy steel casting in a normalizing furnace, raise the temperature to 890°C, keep it warm for 3 hours, and cool it to room temperature after taking it out of the furnace;

[0035] (2) Quenching: Place the low-alloy steel casting in a quenching furnace, raise the temperature to 870°C, keep it warm for 3 hours, and cool it to room temperature with water;

[0036] (3) Tempering: Put the low-alloy steel casting in the tempering furnace, raise the temperature to 710°C, keep it warm for 2.5 hours, and then take it out of the furnace and air-cool it to room temperature.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
hardnessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a thermal treatment process of a casting, and in particular relates to a thermal treatment process of a low-alloy steel casting. The thermal treatment process comprises the following steps of: normalizing, water quenching, and high-temperature tempering air cooling. By adopting the thermal treatment process of the low-alloy steel casting, the tempering temperature of the low-alloy steel casting is improved, a direct furnace tapping air cooling mode is adopted, the treated low-alloy steel casting can meet requirements on strength and hardness, and the toughness of the casting is improved at the same time; and in the thermal treatment process of the low-alloy steel casting, a water cooling mode is used in a quenching step, so that the production cost is reduced, the environmental pollution is reduced, and potential safety hazards are reduced.

Description

technical field [0001] The invention relates to a heat treatment process for castings, in particular to a heat treatment process for low alloy steel castings. Background technique [0002] Due to the advantages of high strength and high wear resistance, low-alloy steel castings gradually replace ordinary carbon steel and are widely used in the field of casting, especially ZG42CrMo, ZG35CrMo and other materials, whose strength is 2-3 times that of ordinary carbon steel. In practical application, the strength, hardness and toughness of low alloy steel need to be selected reasonably. At present, the heat treatment process of low-alloy steel castings generally adopts normalizing-quenching-tempering, in which quenching medium uses quenching oil, and its ratio is 1:10 by weight, that is, 1 ton of castings is put into 10 tons of quenching oil to ensure the quenching effect After the quenching oil has been used for a period of time, the oxidized powder of the casting and the carbon...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C21D6/00C21D1/28C21D1/18C22C38/22
Inventor 张绪清卢志峰黄红军
Owner YINGSHAN HUAMAO SHIP OUTFITTING EQUIP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com