A kind of bismuth-doped vanadate solid solution phosphor and preparation method thereof

A vanadate and phosphor technology, applied in the field of bismuth-doped vanadate solid solution phosphor and its preparation, can solve the problems of weak light emission, high color temperature, low color rendering index and the like, and achieve the effect of avoiding saturation effect

Inactive Publication Date: 2015-09-16
SOUTH CHINA UNIV OF TECH
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The disadvantage of this kind of WLED is that it emits weak light in the red spectrum region, which directly leads to the high color temperature of commercial WLEDs (usually located in 4500-6500K), and the low color rendering index (hereinafter referred to as CRI), usually less than 80
[0003] In addition, in addition to the above WLED preparation technology, WLED can also be prepared by combining ultraviolet LED chips with blue and yellow phosphors that can be excited by ultraviolet light. UV-WLED devices prepared using this idea have not been reported. largely due to the lack of yellow phosphors that can be excited by ultraviolet light

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of bismuth-doped vanadate solid solution phosphor and preparation method thereof
  • A kind of bismuth-doped vanadate solid solution phosphor and preparation method thereof
  • A kind of bismuth-doped vanadate solid solution phosphor and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] Select yttrium oxide, lutetium oxide, scandium oxide, ammonium vanadate, bismuth oxide as starting compound raw materials, press Y a Lu b Sc c VO 4 : The molar ratio of the elements shown in d%Bi, respectively, weigh five kinds of compound raw materials, a total of 9 groups, and the proportions are as follows:

[0029] (1) Y:Lu:Sc:V=1:0:0:1, corresponding to a=1, b=0, c=0, bismuth replaces 2% of Y, that is, d%=2%;

[0030] (2) Y:Lu:Sc:V=0.8:0.2:0:1, corresponding to a=0.8, b=0.2, c=0, bismuth replaces 2% of (Y, Lu), that is, d%=2%;

[0031] (3) Y:Lu:Sc:V=0.6:0.4:0:1, corresponding to a=0.6, b=0.4, c=0, bismuth replaces 2% of (Y, Lu), that is, d%=2%;

[0032] (4) Y:Lu:Sc:V=0.4:0.6:0:1, corresponding to a=0.4, b=0.6, c=0, bismuth replaces 2% of (Y, Lu), that is, d%=2%;

[0033] (5) Y:Lu:Sc:V=0:1:0:1, corresponding to a=0, b=1, c=0, bismuth replaces 2% of Lu, that is, d%=2%;

[0034] (6) Y:Lu:Sc:V=0:0.8:0.2:1, corresponding to a=0, b=0.8, c=0.2, bismuth replaces 2% (...

Embodiment 2

[0044] Select yttrium nitrate, lutetium nitrate, scandium nitrate, vanadium oxide, bismuth powder as starting compound raw materials, press Y a Lu b sc c VO 4 : The element molar ratio ratio shown in d%Bi, take five kinds of compound raw materials respectively, totally 7 groups, the ratio is as follows:

[0045] (1) Y:Lu:Sc:V=0:1:0:1, corresponding to a=0, b=1, c=0, bismuth replaces 0.01% of Lu, that is, d%=0.01%;

[0046] (2) Y:Lu:Sc:V=0:1:0:1, corresponding to a=0, b=1, c=0, bismuth replaces 1.00% of Lu, that is, d%=1.00%;

[0047] (3) Y:Lu:Sc:V=0:1:0:1, corresponding to a=0, b=1, c=0, bismuth replaces 2.00% of Lu, that is, d%=2.00%;

[0048] (4) Y:Lu:Sc:V=0:1:0:1, corresponding to a=0, b=1, c=0, bismuth replaces 3.00% of Lu, that is, d%=3.00%;

[0049] (5) Y:Lu:Sc:V=0:1:0:1, corresponding to a=0, b=1, c=0, bismuth replaces 5.00% of Lu, that is, d%=5.00%;

[0050] (6) Y:Lu:Sc:V=0:1:0:1, corresponding to a=0, b=1, c=0, bismuth replaces 10.00% of Lu, that is, d%=10.00%; ...

Embodiment 3

[0055] Select yttrium nitrate, lutetium nitrate, scandium nitrate, vanadium oxide, bismuth subcarbonate as starting compound raw materials, press Y a Lu b sc c VO 4 : The molar ratio of the elements shown in d%Bi, respectively weigh five kinds of compound raw materials, a total of 1 group, the specific ratio is as follows: Y:Lu:Sc:V=1:0:0:1, corresponding to a=1, b=0, c=0, bismuth replaces 2.00% of Y, that is, d%=2.00%; the total weight of the control mixture is 5 grams. After grinding and mixing 5 grams of the mixture, put it into a corundum crucible, and then put the crucible into a high-temperature electric furnace. The heating rate is precisely controlled, and the sample is pre-fired at 500°C for 5 hours. Take out the pre-fired sample, grind and mix it again, put it into a crucible, burn it at 900°C for 15 hours under oxygen, take it out and grind it again, burn it at 900°C for 15 hours under oxygen, and cool it naturally with the furnace, that is Bismuth doped fluore...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses bismuth-doped vanadate fluorescent powder. An expression general formula of the bismuth-doped vanadate fluorescent powder is YaLubSccVO4: d%Bi; a crystal structure belongs to a tetragonal system, and an active ion is bismuth. The invention further discloses a preparation method of the fluorescent powder. The preparation method comprises the following steps: respectively weighing chemical raw materials containing yttrium, lutecium, scandium, vanadium and bismuth according to the element molar ratio expressed by the general formula, grinding and uniformly mixing, pre-sintering for 1-10 hours at 400-800 DEG C in the presence of oxidizing atmosphere, taking out, grinding and uniformly mixing, firing for 1-15 hours at 900-1500 DEG C in the presence of oxidizing atmosphere, taking out, grinding and uniformly mixing, and firing for 1-15 hours at 900-1500 DEG C in the presence of oxidizing atmosphere. The fluorescence peak of the fluorescent powder prepared by the invention is controllable and adjustable by changing the proportion of elements Y, Lu and Sc and changing the doping concentration of the Bi; and the fluorescent powder can be applied to the field of preparing a white light LED (light-emitting diode) apparatus through a combination scheme of an ultraviolet LED chip and the fluorescent powder.

Description

technical field [0001] The invention relates to a luminescent material, in particular to a bismuth-doped vanadate solid solution phosphor and a preparation method thereof. Background technique [0002] At present, commercial white LEDs (hereinafter referred to as WLEDs) use blue InGaN LEDs to excite Y 3 Al 5 O 12 :Ce 3+ Yellow phosphor, the yellow light is mixed with the transmitted blue light to produce white light. The disadvantage of this WLED is that it emits weakly in the red spectral region, which directly leads to a high color temperature of commercial WLEDs (usually at 4500-6500K) and a low color rendering index (hereinafter abbreviated as CRI), usually less than 80. To solve this problem, a red phosphor (which can be excited by blue light) can be introduced into commercial WLEDs, or an LED chip emitting 350-410nm ultraviolet light can be used to excite a mixed phosphor of red, blue, and green to make another phosphor. kind of WLED. The CRI of WLED based on UV ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09K11/82
Inventor 彭明营康逢文邱建荣
Owner SOUTH CHINA UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com