Preparation method of flame-retardant droplet-resistant terylene

A manufacturing method and anti-melting droplet technology, applied in the field of textile fiber manufacturing, can solve the problems of poor hand feel, difficulty in spinning and weaving, weak fiber strength and elongation, etc.

Active Publication Date: 2013-03-20
ZHEJIANG SHENGYUAN CHEM FIBER
View PDF4 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The flame retardant and anti-dripping polyester produced by this method usually obtains the flame-retardant and anti-dripping properties at the expense of other properties of the fiber. With the addition of flame retardant and anti-dripping agents, the fiber strength and elongation tend to Weak; poor hand feeling; difficult spinning and weaving

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] Embodiment 1: the manufacture method of flame-retardant anti-droplet polyester of the present invention, it adopts the following steps:

[0040] A) According to the number of parts by mass, take 6 parts of basic magnesium sulfate whiskers whose characteristic parameters are 0.1-1um in diameter and 5-12um in length, and 4 parts of four-needle whiskers whose characteristic parameters are 0.1-0.8um in diameter and 6-10um in length Zinc oxide whiskers, 6 copies of magnesium salt whiskers with characteristic parameters of 0.2-0.8um in diameter and 6-10um in length, 4 copies of β-type silicon nitride crystals with characteristic parameters of 0.1-0.6um in diameter and 5-10um in length Whiskers; after mixing the above four whiskers evenly, roast them in a vacuum furnace at 400°C for 5 hours, then stir and shear them in anhydrous ethanol containing sodium hexametaphosphate for 38 minutes after cooling, then treat them with plasma at normal pressure for 15 minutes, and then in U...

Embodiment 2

[0045] Embodiment 2: the manufacture method of flame-retardant anti-droplet polyester of the present invention, it adopts the following steps:

[0046] A) According to the number of parts by mass, take 6 parts of basic magnesium sulfate whiskers whose characteristic parameters are 0.1-1um in diameter and 5-12um in length, and 4 parts of four-needle whiskers whose characteristic parameters are 0.1-0.8um in diameter and 6-10um in length Zinc oxide whiskers, 6 copies of magnesium salt whiskers with characteristic parameters of 0.2-0.8um in diameter and 6-10um in length, 4 copies of β-type silicon nitride crystals with characteristic parameters of 0.1-0.6um in diameter and 5-10um in length Whiskers; after mixing the above four whiskers evenly, roast them in a vacuum furnace at 400°C for 5 hours, then stir and shear them in anhydrous ethanol containing sodium hexametaphosphate for 38 minutes after cooling, then treat them with plasma at normal pressure for 15 minutes, and then in U...

Embodiment 3

[0050] Embodiment 3: A kind of manufacturing method of flame retardant anti-melt droplet polyester, this manufacturing method adopts the following steps:

[0051] A) According to the number of parts by mass, take 4 parts of basic magnesium sulfate whiskers whose characteristic parameters are 0.1-1um in diameter and 5-12um in length, and 2 parts of tetraneedle whiskers whose characteristic parameters are 0.1-0.8um in diameter and 6-10um in length Zinc oxide whiskers, 4 copies of magnesium salt whiskers with characteristic parameters of 0.2-0.8um in diameter and 6-10um in length, 2 copies of β-type silicon nitride crystals with characteristic parameters of 0.1-0.6um in diameter and 5-10um in length Whiskers; after mixing the above four kinds of whiskers evenly, roast them in a vacuum furnace at 350°C for 4 hours, and after cooling, stir and shear and disperse them in absolute ethanol containing sodium hexametaphosphate for 30 minutes, then treat them with atmospheric pressure pla...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of flame-retardant droplet-resistant terylene. The preparation method comprises the following steps of: A) evenly mixing four materials including a flame-retardant droplet resistant basic magnesium sulfate whisker, a beta-type silicon nitride whisker, a tetrapod-like zinc oxide whisker and a magnesium salt whisker, baking the mixture in a vacuum furnace; stirring and dispersing the mixture in a sodium hexametaphosphate solution, carrying out atmospheric pressure plasma treatment, and then filtering and baking the solution by a filter with 200 meshes; B) mixing the whiskers obtained from the step A) with flame-retardant melamine cyanurate, a microencapsulated red phosphorus retardant, and a silane coupling agent under the condition of 75 DEG C; C) preparing a flame-retardant droplet resistant whisker ethylene glycol solution by a flame-retardant droplet resistant whisker obtained in the step B); and D) preparing a flame-retardant droplet resistant polyester from the flame-retardant droplet resistant whisker in a blending or copolyester manner, and preparing the sheath-core flame-retardant droplet resistant terylene of taking the flame-retardant droplet resistant polyester as a skin layer by using a compound spinning technology.

Description

technical field [0001] The invention relates to a method for manufacturing flame-retardant and anti-melt-drip polyester, which includes polyester (PET), melamine cyanurate, microencapsulated red phosphorus flame retardant, tetrapod-like zinc oxide Whiskers, β-type silicon nitride whiskers, basic magnesium sulfate whiskers, magnesium salt whiskers; belong to the technical field of textile fiber manufacturing. Background technique [0002] Polyester is made from polyethylene terephthalate (PET). It is the largest variety of synthetic fibers at present. Because of the high rigidity of the fiber macromolecular chain and high elastic modulus, the fiber is not easily deformed, and the fabric does not wrinkle after washing, does not need to be ironed, is firm and scratchable, and is easy to wash and dry. It also has good heat resistance, cold resistance, sun resistance and abrasion resistance, and is an ideal textile raw material. Polyester is widely used in apparel, decoration,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D01F6/92D01F8/14D01F1/07C08G63/183
CPCD01F8/14D01F6/92C08K7/04D01F1/07C08K3/02C08K3/34C08K5/34924C08K2003/026C08K2003/2296C08K2003/3063C08K2201/014D01F6/62D01F6/84C08L67/02C08G63/183C08K7/08C08K7/10C08K2003/023D01F1/00
Inventor 周先何吴维光杨宝华白克服叶勇李岳春王国军
Owner ZHEJIANG SHENGYUAN CHEM FIBER
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com