Heat-resistant rubber capacitor case packaging material

A capacitor shell and wrapping material technology, applied in capacitors, electrical components and other directions, can solve the problems of easy damage, lack of effective safety guarantee, waste of resources, etc., to achieve high-strength protection, strong adhesion, and cost savings Effect

Active Publication Date: 2013-03-13
TONGXIANG GUANGSHENG PLASTIC IND CO LTD
View PDF4 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Traditional capacitor casings are made of aluminum or plastic products, which are easily damaged in harsh environments such as corrosive acid and alkali, high temperature, low temperature, high pressure or ozone, which affect the normal operation of the capacitor, not only causing a waste of resources, but also in terms of safety. There is no effective guarantee, and the technology of using a metal mesh inner skeleton on the shell of the capacitor and wrapping the rubber material on the outside has not appeared so far.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] A heat-resistant capacitor casing rubber wrapping material, the capacitor casing adopts a metal mesh inner skeleton, and the rubber material is wrapped on the outside, and the rubber material is composed of the following raw materials in parts by weight:

[0016] Neoprene CR121 145, SG-4 type PVC resin 10, poly-4-methyl-1-pentene 10, N, N'-m-phenylene bismaleimide 2, alumina powder 30, barium sulfate Powder 40, antioxidant RD 2, 2-mercaptobenzimidazole 1, zinc stearate 5, accelerator CZ2, accelerator DM 2, 3-aminopropyltrimethoxysilane 4, aluminate coupling agent DL-4112, antioxidant 1010 1-2, high wear-resistant carbon black N330 45, carbon black N22025, isooctyl dithioglycolate di-n-octyl tin 2, epoxy octyl stearate 5, glycerol triacetate 15, carbonic acid Sodium hydrogen 2, modified fly ash 3, ferrocene 2;

[0017] The preparation method of the modified fly ash is as follows: the fly ash is soaked with 15% hydrochloric acid for 4 hours, washed with deionized water, ...

Embodiment 2

[0021] Rubber compound is made up of the raw material of following weight portion:

[0022] Neoprene CR121 140, SG-4 type PVC resin 8, poly-4-methyl-1-pentene 8, N, N'-m-phenylene bismaleimide 2, alumina powder 35, barium sulfate Powder 45, antioxidant RD 2, 2-mercaptobenzimidazole 1, zinc stearate 4, accelerator CZ1, accelerator DM 2, 3-aminopropyltrimethoxysilane 4, aluminate coupling agent DL-4112, antioxidant 1010 2, high wear-resistant carbon black N330 45, carbon black N220 24, isooctyl dithioglycolate di-n-octyl tin 2, epoxy octyl stearate 5, glycerol triacetate 12, bicarbonate Sodium 2, modified fly ash 2, ferrocene 2;

Embodiment 3

[0024] Rubber compound is made up of the raw material of following weight part:

[0025] Neoprene CR121 138, SG-4 type PVC resin 9, poly-4-methyl-1-pentene 10, N, N'-m-phenylene bismaleimide 2, alumina powder 32, barium sulfate Powder 41, antioxidant RD 2, 2-mercaptobenzimidazole 1, zinc stearate 4, accelerator CZ1, accelerator DM 2, 3-aminopropyltrimethoxysilane 4, aluminate coupling agent DL-4112, antioxidant 1010 1, high wear-resistant carbon black N330 43, carbon black N220 23, isooctyl dithioglycolate di-n-octyl tin 2, octyl epoxy stearate 5, glycerol triacetate 14, bicarbonate Sodium 2, modified fly ash 3, ferrocene 1; (the processing method of embodiment 2 and 3 is with embodiment 1)

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a heat-resistant rubber capacitor case packaging material. The heat-resistant rubber capacitor case packaging material consists of the raw materials including chloroprene rubber CR121, a SG-4 polyvinyl chloride (PVC) resin, poly-4-methyl-1-amylene, N, N'-m-phenylenedimaleimide, alumina powder, barium sulfate powder, an anti-aging agent RD, 2-mercaptobenzimidazole, zinc stearate, an accelerator CZ1-2, an accelerator DM, 3-aminopropyl trimethoxy silane, an aluminate coupling agent DL-411, an oxidant, highly-wear-resistant carbon black N330, carbon black N220, imarcaptoacetate dioctyltin, epoxy ethylhexyl stearate, glycerin triacetate, sodium bicarbonate, modified coal ash and dicyclopentadienyl iron. By virtue of a reasonable formula of the raw materials, the produced rubber material has good comprehensive performance and is high in metal adhesion, mechanical property, fatigue resistance, ageing resistance and the like, and can provide high-strength protection for capacitors.

Description

technical field [0001] The invention mainly relates to a rubber wrapping material, in particular to a heat-resistant capacitor shell rubber wrapping material. Background technique [0002] Traditional capacitor casings are made of aluminum or plastic products, which are easily damaged in harsh environments such as corrosive acid and alkali, high temperature, low temperature, high pressure or ozone, which affect the normal operation of the capacitor, not only causing a waste of resources, but also in terms of safety. There is no effective guarantee, and the technology of using a metal mesh inner skeleton on the outer shell of the capacitor and wrapping the rubber material on the outside has not appeared so far. Contents of the invention [0003] The object of the present invention is to provide a heat-resistant capacitor casing rubber wrapping material. [0004] The present invention is achieved through the following technical solutions: [0005] A heat-resistant capa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L11/00C08L27/06C08K13/06C08K9/02C08K9/04C08K3/04C08K3/30C08K3/22C08K5/103C08K5/1515H01G2/10
Inventor 褚诗泉骆方旭鲍启兵
Owner TONGXIANG GUANGSHENG PLASTIC IND CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com