High-performance stainless steel hook

A stainless steel, high-performance technology, applied in the field of high-performance stainless steel hooks, stainless steel hooks, can solve the problems of insufficient strength, incapable of comprehensive promotion and use, etc.

Inactive Publication Date: 2013-01-09
昆山浦力真空科技有限公司
View PDF0 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

To sum up, it is difficult for ordinary ferrous alloy hooks to fully meet the performance requirements of the hook. Therefore, stainless steel hangers have emerged as the times require. However, the current stainless steel hooks still have insufficient strength and cannot be fully promoted and used.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-performance stainless steel hook

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] The specific preparation process of the preparation method of the high-performance stainless steel hook mentioned in the present invention is as follows:

[0019] a) Material selection and preparation. The main components and percentages of raw materials are: nickel powder 8%, chromium powder 6%, manganese powder 10%, molybdenum powder 4%, silicon powder 4%, refractory metal carbide 6%, increase Plasticizer is 6%, the rest is iron powder; the raw materials are ground and screened by a ball mill, and the particle size of nickel powder, chromium powder, manganese powder, molybdenum powder and silicon powder is about 300 meshes, and that of refractory metal carbides. It is 600 meshes, the iron powder particles are 200 meshes, and the carbon content in the iron powder is controlled at 0.6%-0.8%; the powder particles are roughly spherical; the plasticizer is chlorinated paraffin 70, and the particle size is about 100 mesh; WC powder is selected for refractory metal compound;

[...

Embodiment 2

[0025] The specific preparation process of the preparation method of the high-performance stainless steel hook mentioned in the present invention is as follows:

[0026] a) Material selection and preparation, the main components and percentages of raw materials are: nickel powder 9%, chromium powder 7%, manganese powder 8%, molybdenum powder 4%, silicon powder 5%, refractory metal carbide 7%, increase The plasticizer is 7%, and the rest is iron powder; the raw materials are ground and screened by a ball mill, and the obtained nickel powder, chromium powder, manganese powder, molybdenum powder and silicon powder have a particle size of about 350 meshes, and that of refractory metal carbides. It is 650 mesh, the iron powder particle is 250 mesh, the carbon content in the iron powder is controlled at 0.6%-0.7%; the powder particles are roughly spherical; the plasticizer is chlorinated paraffin 70, and the particle size is about 100 mesh; TiC powder is selected for refractory metal c...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-performance stainless steel hook which is manufactured through a powder metallurgy process. The hook comprise, by weight, 7% to 12% of nickel powder, 5% to 10% of chromium powder, 5% to 15% of manganese powder, 3% to 8% of molybdenum powder, 2% to 6% of silicon powder, 4% to 10% of refractory metal carbides, 4% to 85 of plasticizer and the balance being iron powder, wherein the refractory metal carbides are WC or TiC powder. According to the high-performance stainless steel hook, the preparation of components is reasonable, the preparation technology is simple and convenient, and the hook has excellent usage performances on aspects of strength, abrasive resistance, corrosion resistance and the like, so that the usage of the hook is safe and reliable and the application is wide.

Description

Technical field [0001] The invention relates to a stainless steel hook, in particular to a high-performance stainless steel hook with high strength, outstanding wear resistance and corrosion resistance, and belongs to the technical field of stainless steel products. Background technique [0002] Spreader is a device for lifting heavy objects in hoisting machinery. The most commonly used spreader for lifting a piece of article is a hook, and its related accessories include lifting rings, lifting suction cups, clamps and forks. Among them, lifting suction cups, clamps and forks are used together on the crane, which can be used as a special spreader for a long time, and can also be used as an auxiliary spreader for temporary use on the hook to improve work efficiency. The spreader for grabbing bulk materials is generally a grab with open and closing jaws, and electromagnetic chucks can also be used to pick up magnetically conductive materials such as metal chips; the spreaders for l...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/58C22C32/00C22C30/00B22F1/00B66C1/34
Inventor 成军
Owner 昆山浦力真空科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com