A technology of fire-resistant paint and acrylic emulsion, which is applied in the direction of fire-resistant coatings and coatings, and can solve problems such as the gap between physical and chemical properties and weather resistance, late start of research, and hazards to the environment and construction personnel, achieving good flame-retardant effects and easy painting , Improve the effect of physical strength

Inactive Publication Date: 2012-12-19
SHANDONG CHANGXING GROUP
View PDF6 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Thin-coated steel structure fireproof paint can be divided into two types: solvent-based and water-based. Solvent-based fireproof paint uses a large amount of organic solvents in the production and construction process, which is harmful to the environment and construction personnel. Water-based fireproof paint is environmentally friendly and meets low pollution , the development direction of environmentally friendly coatings, but the research in our country started relatively late, and there is still a certain gap with solvent-based fireproof paints in terms of physical and chemical properties and weather resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A kind of fireproof paint, the weight ratio is: 35% of acrylic emulsion, 16% of dipentaerythritol, 8% of expanded graphite, 8% of melamine, 2% of ammonium polyphosphate, 4% of aluminum hydroxide, 2% of zinc oxide, 1% of silicon dioxide %, carbon fiber 4%, silicon nitride fiber 5%, water 15%.

[0017] The preparation method is: mix dipentaerythritol, expanded graphite, melamine, ammonium polyphosphate, aluminum hydroxide, zinc oxide, silicon dioxide and water in a stirring tank according to the proportions of the above formula components, and then put them into a ball mill to grind for 1.5 hours , the speed of the ball mill is 2000r / min, then slowly add acrylic acid emulsion into the ball mill, continue to grind for 0.5 hours, filter to obtain a slurry with a fineness of 100 mesh, put the slurry into a stirring tank and stir at a speed of 400r / min, and add Carbon fibers and silicon nitride fibers are stirred evenly to obtain the fireproof paint of the present invention. ...

Embodiment 2

[0019] A fireproof paint, the weight ratio is: 25% of acrylic emulsion, 12% of dipentaerythritol, 6% of expanded graphite, 6% of melamine, 5% of ammonium polyphosphate, 10% of aluminum hydroxide, 3% of zinc oxide, 2% of silicon dioxide %, carbon fiber 7%, silicon nitride fiber 10%, water 14%.

[0020] The preparation method is: mix dipentaerythritol, expanded graphite, melamine, ammonium polyphosphate, aluminum hydroxide, zinc oxide, silicon dioxide and water in a stirred tank according to the proportion of the ingredients in the formula, and then put them into a ball mill to grind for 2 hours. The speed of the ball mill is 1800r / min, then slowly add acrylic acid emulsion into the ball mill, continue grinding for 1 hour, and filter to obtain a slurry with a fineness of 110 mesh, put the slurry in a stirring tank and stir at a speed of 300r / min, and add carbon fiber at the same time and silicon nitride fiber, and stir evenly to obtain the fireproof paint of the present inventio...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
flame retardantaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a fireproof paint prepared by the following raw materials by the weight: 25-45% of acrylic emulsion, 10-20% of dipentaerythritol, 5-15% of expanded graphite, 5-15% of melamine, 2-10% of ammonium polyphosphate, 3-10% of aluminium hydroxide, 2-5% of zinc oxide, 1-5% of silica, 4-10% of carbon fiber, 5-10% of silicon nitride fiber and the balance of water. The fireproof paint is the water paint; organic solvent is not needed in the preparation process; and the formula does not include halogen, so the fireproof paint does not release toxic or harmful gases containing the halogen, therefore, the fireproof pain has the advantages of security, low pollution and environmental protection, and is widely applied to various steel structure buildings.

Description

technical field [0001] The invention belongs to the field of building fire prevention, and in particular relates to a fireproof paint (coating). Background technique [0002] As a form of high-rise building structure, steel structure shows strong vitality in super high-rise and long-span buildings due to its high strength, light weight, good extensibility, earthquake resistance and short construction period. It is more and more widely used in the construction industry. However, the fire resistance of steel structure buildings is worse than that of traditional masonry structures and reinforced concrete structures. The mechanical strength of steel decreases rapidly with the increase of temperature, and quickly loses its supporting capacity, resulting in the collapse of buildings. Therefore, the protection of steel structures It must be done. Brushing or spraying fireproof paint (or fireproof paint) on the surface of steel structures is one of the commonly used protective met...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/00C09D5/18
Inventor 朱玉国
Owner SHANDONG CHANGXING GROUP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com