High-performance ocean platform steel and its production method

An offshore platform and production method technology, which is applied in the field of steel plate manufacturing, can solve the problems of low low-temperature toughness and affect the use of steel plates, etc., and achieve the effects of high low-temperature impact energy, good structure, and guaranteed hardenability

Inactive Publication Date: 2012-10-17
WUYANG IRON & STEEL +1
View PDF4 Cites 31 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The current strength and low temperature toughness of steel for offshore platforms are relatively small, which affects the use of such steel plates

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-performance ocean platform steel and its production method
  • High-performance ocean platform steel and its production method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] The thickness of the steel for the offshore platform of this embodiment is greater than 90mm, and the actual composition (by weight percentage) of the steel plate is: C: 0.10%, Si: 0.28%, Mn: 1.56%, P: 0.010%, S: 0.001%, Al :0.037%, Nb: 0.037%, V: 0.075%, Ti: 0.045%, the balance is Fe and inevitable impurities, Ceq is 0.40%, Pcm is 0.20%.

[0037] The production method of the steel plate of the present invention is as follows:

[0038] (1) Smelting: Molten steel is first smelted by an electric furnace. When the ladle is tapped, 1 ton of alloy is added, including the deoxidizer Si-Mn, to avoid the increase in the degree of overoxidation of the molten steel, and when the ladle is tapped, P must be less than 0.008%, slag tapping is not allowed; sent to LF refining furnace for refining, and fed with 650 meters of Al wire, 1720kg of lime, 123kg of Si-Fe powder, white slag maintained for 55min, vacuum treatment in VD furnace, 130kg of SiCa block added before vacuum Furnace, the v...

Embodiment 2

[0048] The thickness of the steel for the offshore platform of this embodiment is ≤40mm, and the actual composition (by weight percentage) of the steel plate is: C: 0.12%, Si: 0.27%, Mn: 1.48%, P: 0.009%, S: 0.001%, Al: 0.038%, Nb: 0.027%, V: 0.038%, the balance is Fe and unavoidable impurities, Ceq is 0.38%, Pcm is 0.21%.

[0049] The production method of the steel plate of the present invention is as follows:

[0050] (1) Smelting: Molten steel is first smelted by an electric furnace. When the ladle is tapped, 1 ton of alloy is added, including the deoxidizer Si-Mn, to avoid the increase in the degree of overoxidation of the molten steel, and when the ladle is tapped, P must be less than 0.008%, slag tapping is not allowed; sent to LF refining furnace for refining, and fed with 650 meters of Al wire, 1720kg of lime, 123kg of Si-Fe powder, white slag maintained for 55min, vacuum treatment in VD furnace, 130kg of SiCa block added before vacuum Furnace, the vacuum degree is 66 Pa, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention provides high-performance ocean platform steel and its production method. When the thickness of a steel plate is 8-40mm, the steel plate is composed of the following chemical components, by weight, 0.11-0.13% of C, 0.20-0.50% of Si, 1.45-1.55% of Mn, 0.012% or less of P, 0.003% or less of S, 0.035-0.045% of V, 0.025-0.030% of Nb, 0.050% or less of Ti, 0.020-0.050% of Al, and the balance Fe and inevitable impurities; and when thickness of a steel plate is 40-100mm, the steel plate is composed of the following chemical components, by weight, 0.10-0.12% of C, 0.20-0.50% of Si, 1.50-1.60% of Mn, 0.012% or less of P, 0.003% or less of S, 0.070-0.075% of V, 0.030-0.040% of Nb, 0.050% or less of Ti, 0.020-0.050% of Al, and the balance Fe and inevitable impurities. The production method of the steel plate of the invention comprises the steps of electric furnace smelting, LF furnace refining, VD vacuum treatment, continuous casting (or die casting), heating, control rolling, cooling, stacking, and normalizing to prepare the steel plate. Through a reasonable component design and process optimization, the steel plate of the invention has excellent mechanical performances, welding performances and processing performances, and has strong market competitiveness.

Description

Technical field [0001] The invention belongs to the technical field of steel plate manufacturing, and specifically relates to a high-performance offshore platform steel and a production method thereof. Background technique [0002] In the development of offshore oil and gas resources in my country, the marine engineering equipment manufacturing industry is a strategic industry that provides equipment for marine development. It is estimated that by 2020, the global offshore engineering equipment market investment will exceed 120 billion yuan, of which platform and offshore engineering ships will invest about 70 billion yuan, and deepwater equipment investment will account for more than 45%. Liwan, Lishui, Panyu Jutao, Shengbaowang and other projects are CNOOC South China Sea deep-water natural gas development projects, with recoverable reserves of 4-6 trillion cubic feet of natural gas, and are the first deep-water jack-up ocean independently developed and designed by my country P...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/14
Inventor 韦明李红文吕建会刘丹华小和胡丽周
Owner WUYANG IRON & STEEL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com