Preparing method of positive plate lead paste for power type lead acid storage battery
A technology of lead-acid battery and preparation method, which is applied in the direction of battery electrodes, circuits, electrical components, etc., can solve the problems of low specific energy, high cost, and short life, and achieve high specific energy, strong high-current discharge capacity, and cycle life long effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment Construction
[0006] First prepare the lead paste formula, the weight percentage of the ingredients is: lead powder 100kg, short fiber 0.11kg, trilead tetroxide 50kg, tin powder 2kg, conductive graphite 1.30kg, lead acid barium 2.50kg, deionized water 10000-13000g , the concentration is 1.35g / cm 3 (25°C) sulfuric acid 8200-7000ml. First, mix and stir lead powder, short fiber, trilead tetroxide, tin powder, conductive graphite, and barium lead acid for 5-10 minutes until uniform; add deionized water within 1-3 minutes and continue stirring for 5-6 minutes. ~ 15 minutes evenly add the concentration of 1.3-1.4g / cm 3 (25°C) sulfuric acid, continue to stir for no less than 10 minutes until uniform, the temperature should be controlled within 20-70°C during the whole process; finally fine-tune with deionized water to control the density of the lead paste before discharging to 4.2-4.8g / cm 3 .
PUM
Property | Measurement | Unit |
---|---|---|
density | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com