Method for modifying high-temperature steel slag by using compound materials of tailings

A technology of tailings and steel slag, which is applied in the field of high-temperature steel slag reforming and high-temperature furnace slag reforming, which can solve the problems of high grinding energy consumption and poor grindability, and achieve low input costs, meet environmental protection requirements, and avoid dust pollution. Effect

Active Publication Date: 2013-08-28
迁安金隅首钢环保科技有限公司
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The purpose of the present invention is to overcome the above-mentioned deficiencies in the prior art, adopt bulk and cheap mining tailings, and use waste heat to modify steel slag, realize secondary phase reaction at high temperature, control the mineral phase composition in steel slag, and promote the separation of slag and iron , to solve the disadvantages of poor grindability and high grinding energy consumption of steel slag and post-selection slag, and facilitate the crushing and recycling of steel slag and the low-consumption application development of post-selection waste slag

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for modifying high-temperature steel slag by using compound materials of tailings
  • Method for modifying high-temperature steel slag by using compound materials of tailings

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] 1. The compound materials of high-alumina silicate tailings, high-calcium silicate tailings and calcareous carbonate tailings are selected as steel slag upgrading materials, among which bauxite tailings, gold mine tailings and The limestone tailings were mixed according to the parts by weight of 20, 80 and 5 respectively, and the main components of the mining tailings used are shown in Table 2.

[0031] 2. The particle size of the tailing compound material used as a high-temperature steel slag reforming material is less than 3 mm, and it is pelletized into an agglomerated mass, specifically an ellipsoid with a major axis of 5 mm and a minor axis of 3 cm.

[0032]3. The above-mentioned steel slag reforming material is mixed with the high-temperature steel slag discharged from the Shougang steelmaking plant and the high-temperature reforming material in a ratio of 70:30 by mass. The method of adding is: put the tailings compound material with a mass percentage of 60% in t...

Embodiment 2

[0036] 1. The compound materials of high-alumina silicate tailings, high-calcium silicate tailings and calcareous carbonate tailings are selected as steel slag upgrading materials, among which coal gangue, gold mine tailings and limestone gravel are respectively used Mixing according to the parts by weight of 30, 60 and 12 respectively, the main components of the used mining tailings are shown in Table 2.

[0037] 2. The particle size of the tailing compound material used as a high-temperature steel slag reforming material is less than 3 mm, and it is pelletized into an agglomerated mass, specifically an ellipsoid with a major axis of 5 mm and a minor axis of 3 cm.

[0038] 3. The above-mentioned steel slag reforming material is mixed with the high-temperature steel slag discharged from the Shougang steelmaking plant and the high-temperature reforming material at a ratio of 80:20 by mass. The way of adding is: put the 50% mass percentage of tailings compound in the slag tank o...

Embodiment 3

[0042] 1. The composite material of high-alumina silicate tailings, high-calcium silicate tailings and calcareous carbonate tailings is selected as steel slag upgrading material, among which coal gangue, iron tailings and limestone tailings are respectively used according to The parts by weight are respectively 24, 70 and 10 for mixing, and the main components of the used mining tailings are shown in Table 2.

[0043] 2. The particle size of the tailings composite material used as a high-temperature steel slag reforming material is less than 3 mm, and a spherical agglomeration block with a diameter of 4.5 cm is prepared by pelletizing.

[0044] 3. Mix the above-mentioned steel slag reforming material with the high-temperature steel slag discharged from the converter of Masteel and the high-temperature reforming material in a ratio of 75:25 by mass. The way of adding is: put the tailings compound material with a mass percentage of 40% in the slag tank or slag pan in advance, af...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to View More

Abstract

Provided is a method for modifying steel slag. High-temperature steel slag discharged in the final steelmaking stage is modified by using a large amount of mining tailings with low cost. 15-30 parts by weight of high alumina silicate tailings, 60-80 parts by weight of high calcium silicate tailings and 5-15 parts by weight of calcium carbonate tailings are mixed to obtain compound materials of the tailings; granulating is performed to prepare agglomerated blocks; the compound materials of the tailings are added into a steel slag pot or disc by batches according to the proportion of (70-80%):(20-30%) of the discharged steel slag and the compound materials of the tailings; the temperature of the steel slag is kept at 1200-1400°C for 30-60 min; water quenching, heat applying or heat covering is performed when the temperature is below 1200°C; breaking is performed; magnetic separation is performed. By means of the method, the separation effect of the iron slag is improved, the grindability of the steel slag is improved, the total recovery rate of the scrap steel is up to 95-100%, the components of the separated scrap slag are controllable and have high activity, and the separated scrap slag contains less than 1.5% by weight of the free calcium oxide, has the grinding work index of 14-17kw.h / t and is used to replace the silicate cement clinker.

Description

technical field [0001] The invention relates to a method for upgrading high-temperature slag, in particular to a method for upgrading high-temperature steel slag discharged in the final stage of steelmaking by using bulk and cheap mining tailings, so as to facilitate the crushing and recycling of steel slag and the low-energy consumption of waste slag after selection The development belongs to the technical field of comprehensive utilization of industrial waste. Background technique [0002] With the rapid development of urbanization and industrialization in my country, the annual steel output has exceeded 500 million tons. Steel slag is a by-product of the steelmaking process. The average production of 1 ton of steel will generate about 0.15 to 0.2 tons of steel slag. Based on this calculation, my country’s crude steel output reached 630 million tons in 2010, and the discharge of steel slag was nearly 100 million tons, of which more than 70% were It is converter steel slag....

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C21B3/06
CPCC21B3/06C21B3/08C21B2400/02C21B2400/024C21B2400/08Y02P10/20Y02P10/25
Inventor 连芳张作顺郝洪顺徐利华高小武付福旗
Owner 迁安金隅首钢环保科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com