High solid epoxy paint formula and preparation process as well as application thereof

A technology of epoxy coating and preparation process, which is applied in the direction of epoxy resin coating, anti-corrosion coating, anti-fouling/underwater coating, etc., can solve the problem of low coating quality, achieve good coating film quality, good surface adaptability, and energy saving high efficiency effect

Active Publication Date: 2012-07-11
TIANJIN MEISHIBANG PAINT CHEM IND
View PDF3 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The earliest drying oils or some oil-based paints were high solids paints, which added little or no solvent, but these paints were not of high quality

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High solid epoxy paint formula and preparation process as well as application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0048] The mass ratio formula of gray high solid epoxy paint is as follows:

[0049] The specific composition and content of the main agent are as follows:

[0050] Epoxy resin: 23.7 parts

[0051] Reactive diluent E10P: 1 part

[0052] Titanium dioxide BA01-01: 5 parts

[0053] Epoxy diluent n-butanol: 10 parts

[0054] Bentonite 908: 1.0 parts

[0055] Dispersant ATU: 0.30 parts

[0056] Barite powder 500 mesh: 13 parts

[0057] Talcum powder 600 mesh: 15 parts

[0058] Superfine barium sulfate: 28 parts

[0059] Anti-sagging agent 3300: 2.5 parts

[0060] Black epoxy color paste: 0.5 parts

[0061] The specific composition and content of curing agent are as follows:

[0062] Epoxy diluent n-butanol: 15 parts

[0063] Polyamide curing agent: 10 parts

[0064] Mannich alkali curing agent: 75 parts

[0065] When in use, the mass ratio of the main agent and the curing agent is 84:16.

[0066] The preparation process of this gray high solid epoxy paint is as follow...

Embodiment 2

[0076] The mass ratio formula of iron red high solid epoxy paint is as follows:

[0077] The specific composition and content of the main agent are as follows:

[0078] Epoxy resin E-51: 23.9 parts

[0079] Reactive diluent E10P: 2 parts

[0080] Epoxy diluent n-butanol: 10 parts

[0081] Bentonite 908: 0.8 parts

[0082] Dispersant ATU: 0.3 parts

[0083] Barite powder 500 mesh: 12 parts

[0084] Talcum powder 600 mesh: 14 parts

[0085] Iron oxide red: 6 parts

[0086] Superfine barium sulfate: 28 parts

[0087] Anti-sagging agent 3300: 3.0 parts

[0088] The specific composition and content of curing agent are as follows:

[0089] Epoxy diluent n-butanol: 12 parts

[0090] High molecular polyamide: 10 parts

[0091] Mannich alkali curing agent: 78 parts

[0092] When in use, the mass ratio of the main agent and the curing agent is 84:16.

[0093] The preparation process of this gray high solid epoxy paint is as follows:

[0094] The preparation process steps o...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a high solid epoxy paint formula and a preparation process as well as application thereof. The formula comprises main agents and a curing agent, wherein the main agents comprise an epoxy resin matrix, a diluting agent, pigment and filler and auxiliary agents. The invention also discloses the preparation process of the paint. The preparation process comprises the steps of preparing, grinding, mixing and the like. The high solid epoxy paint is widely applied of petroleum drilling equipment and ship industry. The high solid epoxy paint is of high solid, low viscosity and thick coating, meanwhile has excellent surface adaptability and is extremely suitable for the current environmental protection requirement; in addition, the high solid epoxy paint can be widely applied to the petroleum drilling equipment and the ship industry, and has the characteristics of high energy saving efficiency, high construction performance, high filming quality, no strict requirements on processing of a metal surface, greatly reduced construction cost and the like.

Description

technical field [0001] The invention belongs to the technical field of coating production, and in particular relates to a high-solid epoxy coating formula and its preparation process and application. Background technique [0002] With the increasing awareness of human environmental protection, the requirements for the content of volatile solvents in coatings will become more and more stringent. Although there are still developments in water-based coatings, powder coatings, and radiation-cured coatings, high-solid coatings containing certain solvents and Its unique characteristics determine its irreplaceable status. [0003] At present, although the proportion of environmentally friendly products in my country's coating industry continues to rise, ordinary coatings with high VOC (volatile organic substances) still account for nearly half of the share, and most of the manufacturers of high-solid coatings are wholly foreign-owned or Sino-foreign joint ventures . After the deve...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D163/02C09D5/08C09D5/16C09D7/12
Inventor 于涛
Owner TIANJIN MEISHIBANG PAINT CHEM IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More