Polyethylene terephthalate fiber-adding inflaming retarding material and preparation method thereof

A technology of polyethylene terephthalate and ethylene phthalate, which is applied in the field of polyethylene terephthalate fiber-reinforced flame retardant materials and their preparation, can solve the problem of inability to produce high-performance auxiliary materials. To solve the problems such as high requirements for chemical products, technical processing technology and poor fluidity, it can achieve the effect of low warpage, high surface finish and good fluidity.

Inactive Publication Date: 2012-03-28
重庆可益荧新材料有限公司
View PDF2 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] High-performance engineering plastics are basically monopolized by the United States and Japan, especially most of the domestic high-performance engineering plastics are imported from Japan, and the price is relatively expensive
At present, the products of domestic counterparts are mainly concentrated in general-purpose products with low requirements. Almost no one is involved in the field of high-performance engineering plastics. It is related to the inability of my country's fine chemical industry to produce high-performance additives

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polyethylene terephthalate fiber-adding inflaming retarding material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] Get 35 parts by weight of polyethylene terephthalate, 5 parts of toughening agent, 5 parts of fire retardant, 2 parts of montmorillonite, 0.8 part of polyethylene glycol glycidyl ether, through high-speed kneader Mix at 110°C for 15 minutes, and then granulate at 270°C through a twin-screw extruder. At the same time, 5 parts of glass fiber are added through the fiber-filling port to obtain polyethylene terephthalate fiber-added resistance. combustible material.

Embodiment 2

[0028] Take 60 parts of polyethylene terephthalate in parts by weight, 20 parts of maleic anhydride grafted styrene-butadiene rubber SBS, 15 parts of silicon nitrogen compounded halogen-free environmental protection flame retardant, 6000 mesh Mongolian 2 parts of soil removal, 0.8 parts of polyethylene glycol glycidyl ether, mixed by high-speed kneader at 90 ° C for 10 minutes, and then granulated at 240 ° C by twin-screw extrusion granulator, while 15 parts of glass fiber Add fiber through the port to make polyethylene terephthalate fiber reinforced flame retardant material.

Embodiment 3

[0030] Take 45 parts of polyethylene terephthalate in parts by weight, 15 parts of maleic anhydride grafted styrene-butadiene rubber SBS, 10 parts of silicon nitrogen compounded halogen-free environmental protection flame retardant, 6000 mesh Mongolian 2 parts of soil removal, 0.8 parts of polyethylene glycol glycidyl ether, mixed by high-speed kneader at 100 °C for 12 minutes, and then granulated at 250 °C by twin-screw extrusion granulator, and 10 parts of glass fiber Add fiber through the port to make polyethylene terephthalate fiber reinforced flame retardant material.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a polyethylene terephthalate fiber-adding inflaming retarding material. The polyethylene terephthalate fiber-adding inflaming retarding material is prepared from the following raw materials in parts by weight: 35-60 parts of polyethylene terephthalate, 5-20 parts of flexibilizer, 5-15 parts of fire retardant, 15-30 parts of glass fiber, 2 parts of montmorillonoid and 0.8 part of polyethylene glycol diglycidyl ether. The special PET (polyethylene terephthalate) fiber-adding inflaming retarding material has the characteristics of low price, low mould processing temperature, rapid crystallization rate, low warping, good flowability, good weather resistance and ultraviolet ray resistance, high thermal deformation temperature (195 DEG C), high surface finish, good fire resistance (UL-V0), rapid formation period, low formation shrinkage (0.2%), high notch impact strength (IDZO11-17KJ / m<2>) and the like, and is the preferred product for computer accessories, automobile accessories, electric connectors, switches, mechanical shell accessories and the like.

Description

technical field [0001] The invention belongs to the field of polymer materials, and in particular relates to a polyethylene terephthalate fiber-added flame-retardant material and a preparation method thereof. Background technique [0002] High-performance engineering plastics are basically monopolized by the United States and Japan, especially most of the domestic high-performance engineering plastics are imported from Japan, and the price is relatively expensive. At present, the products of domestic counterparts are mainly concentrated in general-purpose products with low requirements. Almost no one is involved in the field of high-performance engineering plastics. It is related to the inability of my country's fine chemical industry to produce high-performance additives. With the rapid development of my country's economy, in terms of adjusting the structure and transforming the new growth model, metal substitutes for parts near the vehicle engine and electronic products ar...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L67/02C08K13/06C08K9/06C08K7/14C08K3/34
Inventor 咸旭胜
Owner 重庆可益荧新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap