Preparation method for lead zinc niobate-lead titanate monocrystal

A technology of lead niobate zincate and lead titanate, which is applied in the growth field of single crystal materials, can solve the problems of environmental hazards, PbO is volatile, and has not been applied to PZN-PT single crystals, etc., and achieves accelerated growth speed and crystal integrity Good, the effect of shortening the crystal growth cycle

Inactive Publication Date: 2012-03-21
NANJING UNIV OF AERONAUTICS & ASTRONAUTICS
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, because PbO is easy to volatilize at high temperature and has certain harm to the environment, it has not been applied to the growth of PZN-PT single crystals so far.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method for lead zinc niobate-lead titanate monocrystal
  • Preparation method for lead zinc niobate-lead titanate monocrystal
  • Preparation method for lead zinc niobate-lead titanate monocrystal

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] Example 1 0.91Pb(Zn 1 / 3 Nb 2 / 3 )O 3 -0.09PbTiO 3 Single crystal preparation

[0034] Using high-purity PbO, ZnO, Nb 2 o 5 and TiO 2 As an initial raw material, the following processes are included:

[0035] 1. Raw material processing

[0036] (1), the ZnO, Nb 2 o 5 , TiO 2 Mix materials according to stoichiometric ratio, ball mill for 4 hours and pre-sinter at 850°C for about 4 hours to obtain ZnNb 2 o 6 and a small amount of zinc niobium titanium oxide;

[0037] (2) Add PbO according to the stoichiometric ratio, heat to 700°C after ball milling and hold for 3 hours to obtain 0.91PZN-0.09PT ceramic powder;

[0038] (3) According to the metering relationship of the molar ratio of PZN-PT ceramic powder to flux = 3:7, add flux to the 0.91PZN-0.09PT ceramic obtained in step (2), and the flux is pure PbO. The flux and the solute are ball milled and mixed, and pressed into blocks to obtain the starting material for single crystal growth, which is put into the pl...

Embodiment 2

[0047] Example 2 0.88Pb(Zn 1 / 3 Nb 2 / 3 )O 3 -0.12PbTiO 3 Single crystal preparation

[0048] Select high-purity chemical reagents PbO, ZnO, Nb 2 o 5 and TiO 2 Grow as starting material.

[0049] 1. Raw material processing

[0050] (1), the raw materials ZnO, Nb 2 o 5 , TiO 2 Mix materials according to stoichiometric ratio, ball mill for 8 hours and pre-sinter at 1150°C for 1 hour to obtain ZnNb 2 o 6 and a small amount of zinc niobium titanium oxide;

[0051] (2) Add PbO according to the stoichiometric ratio, heat to 800°C after ball milling and hold for 1 hour to obtain 0.88PZN-0.12PT ceramics;

[0052] (3) According to the metering relationship of the molar ratio of PZN-PT ceramic powder to flux = 5:5, add flux to the PZN ceramic powder obtained in step (2). Fluxes are PbO and B 2 o 3 mixture of PbO and B 2 o 3The mol ratio=48:2. The flux and the solute are mixed by ball milling and pressed into blocks to obtain the starting material for single crystal grow...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a preparation method for a lead zinc niobate-lead titanate monocrystal. The preparation method comprises the following steps of: mixing raw materials of PbO, ZnO, Nb2O5 and TiO2 according to chemical composition (1-x)Pb(Zn1 / 3Nb2 / 3)O3-xPbTiO3PZN-PT, wherein x is mole fraction of PT in a solid solution system and is 0-1; mixing the raw materials of ZnO, Nb2O5 and TiO2 in a stoichiometric ratio, and ball-milling and sintering to obtain ZnNb2O6 with a niobite structure and a small amount of zinc niobium titanium oxide with a rutile structure; mixing PbO and sintering to obtain PZN-PT ceramic powder with a perovskite structure; mixing the PZN-PT ceramic powder and a fluxing agent for the growth of the crystal; processing a seed crystal according to crystal orientation (111) and (011); and growing the monocrystal, namely raising the temperature to the saturated growth temperature and reducing the temperature at a speed of 0.5 to 2 DEG C per hour, wherein the pulling speed of the monocrystal is 0.1 to 0.5 mm / h and the rotating speed of the monocrystal is 10 to 25 rpm, when the temperature is reduced to be between 900 and 1,030 DEG C, the crystal is separated from a melt solution and the monocrystal is obtained by reducing the temperature to room temperature at a speed of 50 to 100 DEG C per hour. The monocrystal has large size, high uniformity and obvious crystal appearance and is easy for directional process. The crucible can be reused, and smelting cost is reduced.

Description

technical field [0001] The invention belongs to the field of material preparation and relates to the growth of a single crystal material. During the implementation process, the solid solution single crystal lead niobate zincate-lead titanate is grown by the pulling method. Background technique [0002] Lead titanate (PbTiO 3 ) is a typical perovskite ferroelectric, lead niobate zincate (Pb(Zg 1 / 3 Nb 2 / 3 )O 3 ) is a typical relaxor ferroelectric. In March 1997, the internationally renowned journal "SCIENCE" reported the pseudo-binary solid solution system formed by the two - the relaxor ferroelectric single crystal (1- x )Pb(Zn 1 / 3 Nb 2 / 3 )O 3 - x PbTiO 3 (PZN-PT, x is the mole fraction of PT in the solid solution system) piezoelectric properties. Compared with traditional PZT piezoelectric ceramics, its piezoelectric constant d 33 Increased from 600pC / N to 2500pC / N, electromechanical coupling factor k 33 Increased from 70% to 93-95%, the maximum electrostric...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C30B15/36C30B29/32
Inventor 赫崇君徐峰王吉明朱孔军刘友文
Owner NANJING UNIV OF AERONAUTICS & ASTRONAUTICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com