Hot-rolled structural steel ST52 medium-thick plate with thickness of 15-60mm and production method thereof

A production method and technology for structural steel, applied in metal rolling, temperature control, metal rolling, etc., can solve the problems of poor steel quality and cumbersome production of thick plates.

Inactive Publication Date: 2012-02-08
NANYANG HANYE SPECIAL STEEL CO LTD
View PDF3 Cites 21 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] In the known technology, the production of traditional ST52 medium and heavy plates is quite cumbersome, and the quality of the steel produced is not very good, which has a certain impact on the improvement of competition and income of enterprises

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Hot-rolled structural steel ST52 medium-thick plate with thickness of 15-60mm and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] Through KR molten iron pretreatment, converter smelting, argon blowing treatment, LF refining, VD refining, continuous casting, heating, controlled rolling and controlled cooling, and stack cooling processes, a 15-60mm thick hot-rolled structural steel ST52 medium plate is obtained. Contains the following chemical composition in mass percent (unit, wt%): C: 0.11, Si: 0.44, Mn: 1.22, P: 0.015, S: 0.001, Als: 0.050, Nb: 0.020, Ti: 0.019, others are Fe and residual elements.

Embodiment 2

[0024]Through KR molten iron pretreatment, converter smelting, argon blowing treatment, LF refining, VD refining, continuous casting, heating, controlled rolling and controlled cooling, and stack cooling processes, a 15-60mm thick hot-rolled structural steel ST52 medium plate is obtained. Contains the following chemical composition (unit, wt%) in mass percentage: C: 0.15, Si: 0.26, Mn: 1.50, P: 0.002, S: 0.003, Als: 0.017, Nb: 0.038, Ti: 0.010, others are Fe and residual elements.

[0025] Analysis of mechanical properties

[0026] Composition and mechanical properties are implemented according to ASTM A370, and the mechanical properties are shown in the following table 1

[0027] Table 1 Mechanical and mechanical properties of hot-rolled structural steel ST52 plate with a thickness of 15-60mm

[0028]

[0029] The trial production of 15-60mm thick hot-rolled structural steel ST52 medium and heavy plates totaled 40 batches, of which: the yield strength was controlled at 3...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
elongationaaaaaaaaaa
Login to View More

Abstract

The invention discloses a hot-rolled structural steel ST52 medium-thick plate with the thickness of 15-60mm. The thick plate comprises the following chemical components by weight percent (wt%): 0.10-0.16wt% of C, 0.25-0.45wt% of Si, 1.20-1.50wt% of Mn, less than or equal to 0.017wt% of P, less than or equal to 0.003wt% of S, 0.015-0.055wt% of Als, 0.020-0.040wt% of Nb, 0.010-0.020wt% of Ti and the balance of Fe and residual elements, wherein C equivalent amount [Ceq=C+Mn / 6+(Cr+Mo+V) / 5+(Ni+Cu) / 15] is less than or equal to 0.41. According to the invention, through KR molten iron pretreatment, converter smelting, argon blowing treatment, LF (ladle furnace) refining, VD (vacuum degassing) refining, continuous casting, heating, controlled rolling and controlled cooling and piling cooling processes and on the basis of ensuring the ST52 components, the contents of harmful elements such as P, S and the like, influencing the plasticity and toughness of the steel plate, in steel are strictly controlled, and simultaneously, the heating system of rolled steel is strictly controlled; and in the rolling process, final rolling temperature, red returning temperature and cooling speed are rigidly controlled, and methods such as steel plate stacking and slow cooling and the like are adopted, the various properties of the ST52 steel plate with the thickness of 15-60mm reach standard requirements.

Description

technical field [0001] The invention belongs to the technical field of medium-thick steel plate production, and in particular relates to a 15-60mm thick hot-rolled structural steel ST52 medium-thick plate and a production method thereof. Background technique [0002] In the known technology, the production of traditional ST52 medium and heavy plates is quite cumbersome, and the quality of the steel products produced is not very good, which has a certain impact on the improvement of competition and income of enterprises. Contents of the invention [0003] Aiming at the above problems, the present invention provides a 15-60mm thick hot-rolled structural steel ST52 plate and a production method thereof which are cost-saving and easy to produce. [0004] A 15-60mm thick hot-rolled structural steel ST52 plate, containing the following chemical composition in mass percentage (unit, wt%): C: 0.10-0.16, Si: 0.25-0.45, Mn: 1.20-1.50, P≤0.017 , S≤0.003, Als: 0.015-0.055, Nb: 0.020-...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/14C21C1/02C21C5/35C21C7/072C21C7/06C21C7/10B22D11/18B22D11/22B21B37/74B21B45/02
Inventor 朱书成李亮亮许少普张立新崔冠军高照海袁永旗李忠波于飒刘庆波赵迪贾涛孙炳红
Owner NANYANG HANYE SPECIAL STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products