In-situ synthesized mullite whisker reinforced high-temperature ceramic roller

A technology of mullite whiskers and high-temperature ceramics, which is applied in the field of in-situ generation of mullite whiskers, can solve the problem of high temperature strength creep of materials, weak binding force of mullite crystals in the main crystal phase, and restrictions on roller kilns Development and application issues, to achieve the effect of high temperature flexural strength improvement and good thermal shock resistance

Inactive Publication Date: 2011-11-23
JINGDEZHEN NUONAI TECH CERAMICS
View PDF2 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the limitation of manufacturing technology and firing temperature, the bonding force between the main crystal phase mullite crystals in the obtained ceramic roller material structure is not strong, and there are many glass phases and pores, resulting in high temperature strength of the material. Low creep and large creep, it can only be used at temperatures below 1300°C and under small loads, which seriously restricts the development and application of this continuous, high-efficiency, and energy-saving roller kiln

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0013] Implementation column 1:

[0014] Step 1: Prepare raw materials of andalusite, a zirconium-containing titanium series mineralizer: Add 100kg andalusite concentrate powder (250 mesh), 5kgAlF, 9kg ZrO in sequence in a vibrating mill with a volume of 200L 2 , 2kg TiO2 2 and 10kg of kyanite concentrate powder (325 mesh), after vibrating ball milling for 240 minutes, the particle size of the mixture (D97) was determined to be 9 microns for later use;

[0015] Step 2: Prepare in-situ mullite whisker-reinforced high-temperature ceramic rollers: 190kg of Suzhou kaolin, 50kg of refractory ball clay, 90kg of zirconium silicate, and 140kg of zirconium-containing titanium prepared in the first step are sequentially loaded into a 2-ton ball mill Mineralizer andalusite, 150kgα-Al 2 o 3 Micropowder (4 micron grade) and 850kg water are released after ball milling for 4.5 hours. The slurry is screened and iron-removed and then flows into the slurry storage tank with a screw mixer....

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
flexural strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to an in-situ synthesized mullite whisker reinforced high-temperature ceramic roller which is prepared from natural raw mineral materials and industrial raw chemical materials. The in-situ synthesized mullite whisker reinforced high-temperature ceramic roller comprises the following compositions in percentage by weight: 15-25% of kaolin, 5-15% of refractory clay, 15-25% of alpha-Al2O3 micro-powder, 3-10% of zirconium silicate, 10-20% of zirconium-titanium mineralizer containing andalusite and 30-40% of refractory corundum; and the ceramic roller is prepared through the following steps: ball-milling, stirring, molding, drying, roasting at a temperature of 1500-1600 DEG C, carrying out heat preservation for 5-10 hours, and naturally cooling, thus obtaining a ceramic roller product (the rupture strength of the product is greater than 57.40 Mpa at a temperature of 1350 DEG C). The in-situ synthesized mullite whisker reinforced high-temperature ceramic roller provided by the invention has a wide application prospect in roasting roller kilns for products such as high-temperature and high-load domestic ceramics, building sanitary ceramics, high-grade large-sized vitrified tiles, technical ceramics and magnetic materials and the like.

Description

[0001] technical field [0002] The invention belongs to the technical field of preparing ceramic rollers, in particular to an in-situ generation of mullite whiskers [0003] Reinforced high temperature ceramic rollers. Background technique [0004] Ceramic rollers refer to refractory products made of clay refractory raw materials and natural mineral raw materials through processes such as selection, crushing, forming, and calcination. Usually, the main raw materials for the production of ceramic rollers are kaolin, refractory clay, α-Al 2 o 3 And refractory corundum aggregate, etc. Until today, most of the ceramic rollers used in roller kilns are mainly made of mullite-corundum, mullite-corundum-deleyite. In this material, refractory corundum is used as aggregate, kaolin and α-Al 2 o 3 High-temperature reaction synthesizes mullite and a small amount of glass phase as a combination (matrix), and there are a certain number of pores in the matrix. Due to the limitation ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/81C04B35/10C04B35/622
Inventor 王永华郑景庐
Owner JINGDEZHEN NUONAI TECH CERAMICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com