Manufacture formula of rail grinding wheel and manufacture method thereof

A manufacturing method and technology of grinding wheels, which are applied in the field of grinding wheels to achieve the effect of not being easily broken, not easy to burn and crack, and having good grinding performance

Inactive Publication Date: 2011-11-16
李冰湜
View PDF3 Cites 22 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] In order to solve the above problems, the object of the present invention is to provide a rail grinding wheel with better self-sharpening performance and grinding performance, higher cutting efficiency, and less prone to burns and cracks on the rail during the grinding process.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] This embodiment discloses a preparation formula for rail grinding wheel, which is made of the following components, and its weight fraction ratio is: 70 parts of zirconium corundum, 5 parts of iron sulfide powder, 4 parts of cryolite, 1 part of calcium carbonate, gypsum 1 part of powder and 7 parts of phenolic resin are mixed according to the aforementioned production process, sintered, wound, dried and hardened to shape. In order to make the produced grinding wheel stronger in cutting force, the zirconium corundum with a grain size of 14-16 meshes is selected.

Embodiment 2

[0037] This embodiment discloses a preparation formula of a rail grinding wheel, which is made of the following components, and its weight fraction ratio is: 100 parts of zirconium corundum, 8 parts of iron sulfide powder, 8 parts of cryolite, 3 parts of calcium carbonate, gypsum 4 parts of powder and 10 parts of phenolic resin are mixed according to the above-mentioned production process, sintered, wound, dried and hardened to shape. In order to make the produced grinding wheel stronger in cutting force, the zirconium corundum with a grain size of 14-16 meshes is selected.

Embodiment 3

[0039] As the best embodiment of the present invention, it is made of the following components, and its weight fraction ratio is: 85 parts of zirconium corundum, 6.5 parts of iron sulfide powder, 6 parts of cryolite, 2 parts of calcium carbonate, 2 parts of gypsum powder, phenolic 8.5 parts of resin, mixed, sintered, wound and dried and hardened according to the aforementioned production process. In order to make the produced grinding wheel stronger in cutting force, the zirconium corundum with a grain size of 14-16 meshes is selected.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to a wheel, in particular to a rail grinding wheel, which is formed by mixing, sintering, wrapping, drying and hardening the following components in parts by weight: 70-100 parts of zirconia alumina, 5-8 parts of vulcanized iron powder, 4-8 parts of cryolite, 1-3 parts of calcium carbonate, 1-4 parts of gypsum powder and 7-10 parts of phenolic resin. In the invention, the zirconia alumina is selected as the main material of the rail grinding wheel and the vulcanized iron powder, the cryolite, the calcium carbonate, the gypsum powder and the phenolic resin for heat rejection, heat conduction and reinforcement are added on condition that the cutting force is ensured. The wheel manufactured by the invention not only has the advantages of better self-sharpening performance and grinding performance, higher cutting efficiency and low frequency of burn and crackle when a rail is grinded via the wheel, but also has the advantages of higher strength and good breakage proofness.

Description

technical field [0001] The invention relates to a grinding wheel, in particular to a formula for making a grinding wheel for rail grinding and a manufacturing method thereof. Background technique [0002] The steel rail is the main component of the railway track. Its function is to guide the wheels of the rolling stock, withstand the huge pressure of the wheels, and transmit them to the sleepers. The steel rail must provide a continuous, smooth and least resistance rolling surface for the wheels. [0003] Now, railway trains are all developing towards high speed, and the running speed is constantly increased. In order to make the trains run safely at high speed, one is to change the performance of the locomotive, and the other is to ensure that the rails are intact. The rails change due to factors such as high speed, heavy pressure, wind, rain, sand and dust, and phenomena such as edge pushing, wear, and corrosion occur, which makes it difficult to ensure the stability and s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09K3/14B24D3/28B24D18/00
Inventor 李冰湜
Owner 李冰湜
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com