Baking-free plant straw building wall material and production method thereof

A technology for a building wall and a production method, which is applied in the field of building wall materials, can solve the problems of difficulty in separation, limited use, inability to use paper making, etc., and achieves the effect of a simple production process

Active Publication Date: 2011-10-26
新疆西营海华新型建材有限公司
View PDF5 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] 1. It is used to make compressed fiberboard, and due to technological reasons, such as a large amount of adhesive must be added, especially if it contains a certain amount of formaldehyde, and it will be harmful to the human body when used as a civil building material. Due to the process, its strength is generally low, and its use is limited.
[0005] 2. As a raw material for papermaking, but at present, many agricultural production areas, especially the northern arid areas, use a large number of plastic film planting models, and a large amount of old plastic film is also mixed in when recycling orange stalks, which is a fatal problem for papermaking. Separate them Very difficult, almost impossible according to current processing methods, thus making it unusable for papermaking
[0006] CN101417459A discloses a method and material for making wood-plastic composite materials by using plant straws and waste plastics, in which a method for utilizing cotton straws is proposed, and the recovered cotton straws are crushed and mixed with waste and old plastics, and composite additives are added to the Molding under high temperature and high pressure, this method needs to add plastics and compounding additives, the manufacturing process is complicated and the energy consumption is high, especially the use of a large amount of plastics, which weakens the environmental protection effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] Example 1: Take dry cotton stalks with a moisture content of ≤ 15% and pulverize them into 500 μm granules to obtain cotton stalk powder; take 25 parts of cotton stalk powder, 20 parts of light calcium carbonate, 10 parts of bentonite, and 10 parts of silica fume by weight , 5 parts of triethanolamine, 1 part of silicone, mix evenly, add 40 parts of liquid sodium silicate, stir at 600 rpm for 3 to 4 minutes, put it into the extrusion molding machine and extrude it under the pressure of 10Mpa.

Embodiment 2

[0021] Example 2: Take dry cotton stalks with a moisture content of ≤ 10% and pulverize them into 600 μm granules to obtain cotton stalk powder, and pulverize light calcium carbonate, bentonite, silica fume, triethanolamine, and silicone to 600 μm granules respectively, Take 20 parts of the above-mentioned cotton straw powder, 20 parts of light calcium carbonate, 20 parts of bentonite, 10 parts of silica fume, 5 parts of triethanolamine and 3 parts of organic silicon by weight, mix well, add 45 parts of liquid sodium silicate at 120 rpm / Stir for 3 to 4 minutes, put it into the extrusion molding machine and extrude it under the pressure of 15Mpa.

Embodiment 3

[0022] Example 3: Take dry cotton stalks with a moisture content of ≤18% and pulverize them into 800 μm granules to obtain cotton stalk powder, and pulverize light calcium carbonate, bentonite, silica fume, triethanolamine, and silicone into 400 μm granules, respectively, Take 15 parts of the above-mentioned cotton straw powder, 5 parts of light calcium carbonate, 30 parts of bentonite, 15 parts of silica fume, 4 parts of triethanolamine and 3 parts of organic silicon by weight, mix well, then add 40 parts of liquid sodium silicate to 300 parts Stir for 3 to 4 minutes at rev / min, put it into the extrusion molding machine and extrude it under the pressure of 12Mpa.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a baking-free plant straw building wall material and a production method thereof. The wall material is mainly obtained by the following steps: mixing the following components in parts by weight: 5-20 parts of light calcium carbonate, 10-30 parts of bentonite, 5-15 parts of silicon ash, 2-5 parts of triethanolamine, 1-3 parts of organic silicon and 15-25 parts of cotton straw powder; adding 40-55 parts of modified sodium carbonate for abundantly and evenly stirring; and placing the mixture in an extrusion forming machine for extrusion formation under the pressure of 10-15 Mpa so as to obtain the building wall material. Compared with the prior art, the wall material disclosed by the invention is naturally solidified at room temperature after raw material smashing, stirring and extrusion forming, thus production process is extremely simple, and the produced product has the characteristics of light weight, low energy consumption, no pollution, corrosion resistance, dampproof property, mothproof property and the like and can be widely applied to walls, wallboards and sound insulation plates in the field of buildings.

Description

technical field [0001] The invention relates to a building wall material produced by using plant straws as raw materials and a production method thereof, in particular to a non-burning type building wall material produced by using cotton straw raw materials and a production method thereof. Background technique [0002] At present, a large number of orange stalks produced by agricultural production, especially a large number of cotton stalks produced in cotton production areas in my country, are crushed and returned to the fields as fertilizers. However, the long-term use of this treatment method will increase the possibility of crop diseases. The value of utilization is also low; second, as a fuel, the value of its utilization is greatly reduced, and some are treated as waste, such as incineration, which not only causes waste of resources, but also pollutes the environment. [0003] At present, the industrial utilization of cotton straw mainly includes the following types. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/26
CPCC04B28/26Y02W30/91C04B14/104C04B14/28C04B18/146C04B18/248C04B20/0076C04B24/122C04B24/42C04B40/0071
Inventor 余建国
Owner 新疆西营海华新型建材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products