In-situ cast stainless steel

A stainless steel, in-situ technology, applied in the field of stainless steel, can solve the problems of labor cost, energy, environmental protection and management, and achieve the effects of superior mechanical properties, good welding performance and excellent corrosion resistance

Inactive Publication Date: 2011-08-24
陈才金
View PDF4 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

To this end, it is necessary to use a complete set of sophisticated heat treatment equipment, and a series of cost inputs such as labor, energy, environmental protection and management are required.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] The in-situ cast stainless steel of the present invention uses steel scrap (O8F), scrap nickel-chromium stainless steel, ferroalloys such as trace elements niobium and molybdenum as raw materials, and its composition (weight %) is: 0.06%C, 19.50%Cr, 7.20%Ni, 1.50% %Mo, 1.50%Mn, 0.8%Nb, 1.00%Si, 0.02%S, 0.03%P, 0.05Re, 0.12%N, and the balance is Fe.

[0023] The mechanical properties are listed in Table 2.

Embodiment 2

[0025] The composition (weight %) of the in-situ cast stainless steel of the present invention is: 0.02%C, 18.2%Cr, 5.82%Ni, 0.08%Mo, 4.7%Mn, 0.40%Nb, 0.80%Si, 0.028%S, 0.04%P, 0.05Re, 0.08%N, the balance is Fe.

[0026] The mechanical properties are listed in Table 2.

Embodiment 3

[0028] The composition (weight %) of the in-situ cast stainless steel of the present invention is: 0.10%C, 21.00%Cr, 9.51%Ni, 2.50%Mo, 1.80%Mn, 0.95%Nb, 1.50%Si, 0.01%S, 0.04%P, 0.07Re, 0.22%N, the balance is Fe.

[0029] The mechanical properties are listed in Table 2.

[0030] Table 2

[0031] .

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to an in-situ cast stainless steel which comprises the following components in percentage by weight: 0.01-0.12% of C, 15.00-22.00% of Cr, 5.00-10.00% of Ni, 1.00-2.50% of Mo, at most 5.00% of Mn, 0.02-1.00% of Nb, 0.80-2.00% of Si, at most 0.03% of S, at most 0.06% of P, at least 0.02% of Re, 0.05-0.30% of N and the balance of Fe. The heat-treatment-free in-situ cast stainless steel has the advantages of fine structure, higher yield strength and toughness than traditional similar nickel-chromium stainless steel, acid / alkali corrosion resistance, favorable machinability, favorable weldability, environmental protection and energy saving, has favorable stress corrosion cracking resistance, crevice corrosion resistance, corrosion wear resistance and cavitation corrosion resistance especially in a chloridion-containing medium and a sea water corrosion environment, does not need excellent heat treatment equipment, and lowers the cost by about 20% as compared with the traditional stainless steel.

Description

technical field [0001] The invention relates to a stainless steel, in particular to an in-situ casting stainless steel without heat treatment. Background technique [0002] Since the invention of stainless steel with chromium or nickel-chromium as the main element for more than 100 years, there are more than 100 kinds of stainless steel with grades in the world. In order to ensure that these stainless steel products have excellent performance, they generally have to go through smelting→casting (casting) → forging (or rolling) → heat treatment → machining and a series of processing processes. And the process of smelting→casting (casting)→heat treatment is necessary. Among them, the heat treatment process has always been used to change the internal crystal structure and organizational state of cast, forged, and rolled products, and to eliminate the phenomena or defects such as coarse grains, wide grain boundaries, impurity accumulation, and serious composition segregation rem...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22C38/58C22C38/48
Inventor 陈才金鲁凤娟鲁捷
Owner 陈才金
Features
  • Generate Ideas
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com