Method for recovering scandium and titanium in titanium white wastewater

A technology of titanium dioxide wastewater and recovery methods, applied in the direction of improving process efficiency, etc., can solve the problems of unconsidered and neglected titanium element recovery, etc., and achieve the effects of improving yield, environmental protection process, and reducing scandium cost

Active Publication Date: 2011-07-20
河南荣佳钪钒科技有限公司
View PDF1 Cites 40 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

There are also those who do not wash titanium and use TBP to extract scandium, and titanium remains in the solution. These methods often ignore the recovery of titanium, and all methods do not consider the secondary pollution caused by the organic phase in the water phase after extraction.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for recovering scandium and titanium in titanium white wastewater
  • Method for recovering scandium and titanium in titanium white wastewater

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] 1000 liters of titanium dioxide wastewater in the 2M3 reactor, (acidity 5Mol H 2 SO 4 , containing scandium 16mg / liter, titanium 6g / liter, iron 30g / liter), add 50 liters of P2O4 and 4% TBP and the kerosene of remaining volume by volume fraction, carry out single-stage extraction, stir 20 minutes, stir The speed is 100 rpm, and the equilibrium time is 15 minutes; static stratification, the extraction rate of scandium is 90%, and the extraction rate of titanium is 40%. After linoleum treatment, the organic phase content in the water phase is 50mg / L, and it is discharged.

Embodiment 2

[0021] 500 liters of the organic phase after extraction in Example 1 was put into a 1.5M3 reactor, and 500 liters of single-stage stripping with 1molNaOH and 0.7molNaCl lye was used, at a temperature of 70C °, stirred for 15 minutes, and the stirring speed was 120 rpm ;Static stratification, the stripping rate of scandium is 98%, and the stripping rate of titanium is 98%. Dissolve the stripped alkali cake with 9molH2SO4, adjust the pH to 0.5 with Na2CO3, heat to boiling for 10 minutes, hydrolyze the titanium, and filter and recover the titanium; the hydrolysis rate of titanium is more than 90%, and the loss of scandium is 1%, Ti / Sc= 50:1.

Embodiment 3

[0023] 500 liters of mother liquor after hydrolysis in embodiment 2, put into 1.5M3 Reactor, first use H2SO4Adjust acidity 5mol and carry out second extraction and back extraction again, condition is the same as embodiment 1, embodiment 2. After the second hydrolysis, Ti / Sc=1:1, control pH=2, precipitate scandium with oxalic acid, and burn at 800C° for 1 hour to obtain 95% crude scandium oxide.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
extraction efficiencyaaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for recovering scandium and titanium from wastewater in the production of titanium white powder. The method comprises the following steps of: carrying out single stage extraction in titanium white wastewater with P2O4, TBP and kerosene, wherein a phase ratio O / A is 1:50 to 1:10, and balance time is 10-20 min; then, stripping with alkali, filtering and dissolving a stripped substance with acid; heating a solution in a reaction kettle, adjusting a pH value, hydrolyzing titanium, filtering and recovering titanium, repeating the above process to process supernatant fluid, secondarily extracting and dissolving a stripped substance alkali cake with acid; precipitating scandium with oxalic acid and burning to obtain scandium oxide with the purity of 95 percent; and further refining to obtain high-pure scandium oxide. In the invention, titanium is recovered under the condition of ensuring scandium recovery without adopting a titanium washing process of sulfuric acid and hydrogen peroxide, and a hydrolysis mode is adopted to recover titanium, and the recovery cost of scandium is decreased. In addition, a degreasing device and oil-absorbing felt are adopted in waste liquid generated after extraction. The invention has the advantages of environmental protection and simple process, the wastewater contains the organic phase of less than 50 mg / l and reaches an emission standard.

Description

technical field [0001] The invention relates to a method for recovering valuable elements in industrial waste water, in particular to a method for recovering scandium and titanium and purifying scandium oxide from titanium white waste water produced in the production process of titanium dioxide. Background technique [0002] Scandium is a rare element, which is mainly extracted from other minerals, such as rare earth ore, ilmenite, bauxite, tungsten ore, etc. With the expansion of the civilian application of scandium, a large amount of cheap scandium is needed. The cost is high, and a large amount of scandium is lost from the titanium dioxide wastewater without recycling. There are two main production methods of titanium dioxide (titanium dioxide): chloride method and sulfuric acid method, and sulfuric acid method is mainly used in my country; in the process of producing titanium dioxide by sulfuric acid method, a large amount of waste acid water will be generated, and every...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22B7/00C22B34/12C22B59/00
CPCY02P10/20
Inventor 李孝良陈卫平杨钊谭东正杨庆山陈青松周俊军
Owner 河南荣佳钪钒科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com