Preparation method of non-ironing finishing agent of modified self-crosslinking organosilicon anti-wrinkle microemulsion

A non-iron finishing and self-crosslinking technology, which is applied in fiber treatment, fiber type, textiles and papermaking, etc., can solve the problems of unsatisfactory non-ironing effect, harsh production conditions, and high fabric strength, so as to facilitate large-scale production, Ease of operation and simple experimental methods

Active Publication Date: 2011-04-27
江苏印盟科技有限公司 +1
View PDF4 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The strength of the fabric after the non-ironing finishing agent of polycarboxylic acid is high, and the hand feeling is poor, and the non-ironing effect is not ideal
The fabrics finished with polyurethane anti-wrinkle and non-ironing finishing agent have good anti-wrinkle effect and good hand feeling. The disadvantage of polyurethane anti-wrinkle and non-ironing finishing agent is that the production conditions are harsh and the price is expensive. Questioned the nature of the isocyanate group and clearly stipulated the residual amount of the isocyanate group on the textile, which limits the application of polyurethane in the textile

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of non-ironing finishing agent of modified self-crosslinking organosilicon anti-wrinkle microemulsion
  • Preparation method of non-ironing finishing agent of modified self-crosslinking organosilicon anti-wrinkle microemulsion
  • Preparation method of non-ironing finishing agent of modified self-crosslinking organosilicon anti-wrinkle microemulsion

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] The preparation method of the modified self-crosslinking silicone anti-wrinkle micro-emulsion non-ironing finishing agent in this embodiment includes the preparation process of modified amino silicon crude oil and the preparation process of emulsified finishing agent.

[0026] In the preparation process of modified amino silicone crude oil, the raw materials used include 400kg amino silicone oil, 400kg solvent and 22.2kg epichlorohydrin, wherein isopropanol is used as solvent, and the ammonia value of amino silicone oil is 0.6. The weight ratio of amino silicone oil in the present invention: solvent: epichlorohydrin can be 1: (1-1.5): 0.09252X, where X is the ammonia value of amino silicone oil, and the value of X is usually 0.3-0.9, amino The degree of polymerization of silicone oil is usually 4000-8000, and the solvent in the present invention can be absolute alcohol or isopropanol or isobutanol or glycerol. The equipment used in the preparation process of modified am...

Embodiment 2

[0032] The preparation method of the modified self-crosslinking silicone anti-wrinkle micro-emulsion non-ironing finishing agent in this embodiment includes the preparation process of modified amino silicon crude oil and the preparation process of emulsified finishing agent.

[0033] In the preparation process of the modified amino silicone crude oil, the raw materials used include 400kg amino silicone oil, 400kg solvent and 33.3kg epichlorohydrin, wherein isopropanol is used as the solvent, and the ammonia value of the amino silicone oil is 0.9. The weight ratio of amino silicone oil in the present invention: solvent: epichlorohydrin can be 1: (1-1.5): 0.09252X, where X is the ammonia value of amino silicone oil, and the value of X is usually 0.3-0.9, amino The degree of polymerization of silicone oil is usually 4000-8000, and the solvent in the present invention can be absolute alcohol or isopropanol or isobutanol or glycerol. The equipment used in the preparation process of...

Embodiment 3

[0039] The preparation method of the modified self-crosslinking silicone anti-wrinkle micro-emulsion non-ironing finishing agent in this embodiment includes the preparation process of modified amino silicon crude oil and the preparation process of emulsified finishing agent.

[0040] Wherein the raw material in the modified amino silicon crude oil preparation process comprises amino silicone oil, solvent and epichlorohydrin, this amino silicone oil: solvent: the weight ratio of epichlorohydrin is 1: 1:0.09252X, and wherein X is the ammonia of amino silicone oil value, the value of X is 0.3, the solvent is absolute alcohol or isopropanol or isobutanol or glycerol, and the degree of polymerization of amino silicone oil is 4000-8000. First, mix the amino silicone oil and the solvent evenly, and then slowly drop epichlorohydrin into the mixture of amino silicone oil and solvent through the elevated tank. The dripping time of the epichlorohydrin is 0.5-3 hours, preferably 0.5 hours....

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
degree of polymerizationaaaaaaaaaa
Login to View More

Abstract

The invention relates to a preparation method of a non-ironing finishing agent of a modified self-crosslinking organosilicon anti-wrinkle microemulsion. At present, the non-ironing finishing agent with good performance does not exist. The preparation method comprises a process of preparing amino-modified silicone crude oil and a process of preparing an emulsion finishing agent; the process of preparing the amino-modified silicone crude oil comprises the steps of: mixing amino-modified silicone oil and a solvent, dripping epoxy chloropropane, heating the mixed liquor to a temperature of 40-60DEG C, preserving the temperature to react for 2-4h, and cooling to a temperature of 15-25DEG C to obtain the amino-modified silicone crude oil, wherein the proportion of the amino-modified silicone oil to the solvent to the epoxy chloropropane by weight is 1: (1-1.5): 0.09252X, and X is 0.3-0.9; and the process of preparing the emulsion finishing agent comprises the steps of: preparing the following materials in percentage by weight: 8-15% of fatty alcohol-polyoxyethylene ether, 0.2-0.3% of glacial acetic acid, 54.7-73.8% of water and 18-30% of amino-modified silicone crude oil, adding the fatty alcohol-polyoxyethylene ether in the modified amino-modified silicone crude oil to emulsify, and adding the glacial acetic acid and the water to obtain the product. The preparation method of the non-ironing finishing agent of the modified self-crosslinking organosilicon anti-wrinkle microemulsion is simple in process, easy for preparation and reliable in product performance.

Description

technical field [0001] The invention relates to a preparation method of a modified self-crosslinking silicone anti-wrinkle microemulsion non-ironing finishing agent. The modified self-crosslinking silicone anti-wrinkle microemulsion non-ironing finishing agent is mainly used for anti-wrinkle of cellulose fabrics and blended fabrics Easy-care finishing. Background technique [0002] In 1926, the first anti-wrinkle finishing patent applied by the British TBL company clearly stated that the two initial shrinkage bodies of phenolic formaldehyde and urea-formaldehyde should be condensed into resin inside the cellulose fiber, which may be the origin of the original name of anti-wrinkle finishing as resin finishing. Due to the color change of phenolic initial shrinkage after finishing, its popularization and application is limited (only for dark colors) and gradually eliminated. [0003] In 1955, some new anti-wrinkle finishing agents with better performance appeared on the market...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06M15/65C08G77/388C08J3/03D06M101/06D06M101/32
Inventor 熊磊陈小利姚庆才林森
Owner 江苏印盟科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com