Halogen-free fire resistance resin composite and application thereof

A resin composition, flame retardant technology, applied in chemical instruments and methods, printed circuits, printed circuit manufacturing, etc., can solve problems such as the inability to meet halogen-free environmental protection requirements, achieve excellent heat resistance, good heat resistance, The effect of excellent heat resistance

Inactive Publication Date: 2011-04-20
GUANGDONG SHENGYI SCI TECH
View PDF10 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The composition is composed of cyanate ester, epoxy resin, and filler, but this system uses bromine-containing bisphenol A epoxy resin in order to achieve flame retardancy. Due to the presence of bromine, thermal decomposition will produce corrosive bromine, bromine Hydrogen problem, can not meet the requirements of halogen-free environmental protection

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Halogen-free fire resistance resin composite and application thereof
  • Halogen-free fire resistance resin composite and application thereof
  • Halogen-free fire resistance resin composite and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] Use 40 parts of XZ92530, 10 parts of PMP, 35 parts of HF-1, 15 parts of PX200 supplemented with catalyst 2-PI and zinc naphthenate, use 80 parts of MEK to dissolve the above compounds, and prepare a glue with a suitable viscosity. Use 2116-type electronic grade glass cloth to soak the glue, and bake it in an oven at 155 degrees to remove the solvent to obtain a B-stage prepreg.

[0034] Laminate eight prepregs and two one-ounce electrolytic copper foils together, and laminate them with a hot press to obtain a double-sided copper-clad laminate (a laminate for printed circuits). The lamination conditions are as follows: 1. When the material temperature is 80-120 degrees, the heating rate is controlled at 1.0-3.0 degrees / minute; 2. The pressure is set to 20kg / cm 2 ; 3, curing temperature at 190 degrees, and maintain this temperature for 90 minutes. The corresponding properties are shown in Table 1.

Embodiment 2

[0036] Use 25 parts of XZ92530, 20 parts of N695, 35 parts of PMP, 10 parts of HF-1, 10 parts of PX200 supplemented with catalyst 2-PI and zinc naphthenate, use 80 parts of MEK to dissolve the above compounds, and adjust to a suitable viscosity glue. Use 2116-type electronic grade glass cloth to soak the glue, and bake it in an oven at 155 degrees to remove the solvent to obtain a B-stage prepreg.

[0037] Laminate eight prepregs and two one-ounce electrolytic copper foils together, and laminate them with a hot press to obtain a double-sided copper-clad laminate. The lamination conditions are as follows: 1. When the material temperature is 80-120 degrees, the heating rate is controlled at 1.0-3.0 degrees / minute; 2. The pressure is set to 20kg / cm2; 3. The curing temperature is 190 degrees, and keep this temperature for 90 minutes . The corresponding properties are shown in Table 1.

Embodiment 3

[0039] Use 45 parts of XZ92530, 5 parts of N695, 5 parts of PMP, 30 parts of HF-1, 15 parts of PX200 supplemented with catalyst 2-PI, zinc naphthenate, use 100 parts of MEK to dissolve the above compounds, and adjust to a suitable viscosity glue. Use 2116-type electronic grade glass cloth to soak the glue, and bake it in an oven at 155 degrees to remove the solvent to obtain a B-stage prepreg.

[0040] Laminate eight prepregs and two one-ounce electrolytic copper foils together, and laminate them with a hot press to obtain a double-sided copper-clad laminate. The lamination conditions are the same as in Example 1, and the corresponding properties are shown in Table 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a halogen-free fire resistance resin composite and application thereof. The halogen-free fire resistance resin composite comprises the following components: bifunctional or multifunctional halogen-free epoxy resin, reactive polyphosphonate and cyanate resin. The halogen-free fire resistance resin is applied to a prepreg; the prepreg comprises a base material and the halogen-free fire resistance resin composite attached to the base material after being impregnated and dried. The halogen-free fire resistance resin composite is applied to a plyboard for a printing circuit; the plyboard for the printing circuit comprises a plurality of stacked prepregs and single-surface or double-surface metal foil arranged on the stacked prepregs; each prepreg comprises the base material and the halogen-free fire resistance resin composite attached to the base material after being impregnated and dried. The halogen-free fire resistance resin composite has high heat resistance, fire resistance and dip soldering resistance, and thereby, the halogen-free fire resistance resin composite can be used for manufacturing the resin sheet, the resin composition metal foil, the prepreg, the plyboard and the printed wiring board.

Description

technical field [0001] The invention relates to a resin composition, in particular to a halogen-free flame-retardant resin composition and its application. Background technique [0002] With the rapid development of electronic and electrical products in the world, the environmental hazards of electronic and electrical product waste and toxic substances in electronic and electrical products are becoming more and more serious. In order to achieve excellent flame retardancy, existing electronic materials usually use bromine-containing epoxy resin or bromine-containing flame retardants. However, they will dissociate to form hydrogen bromide and bromine under high temperature and long-term use, and have Wire corrosion may cause danger; in addition, a large amount of suffocating smoke will be produced during the combustion process, and carcinogens such as dioxin and dibenzofuran will also be produced during the combustion process. In addition, it is quite difficult to dispose or ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L63/00C08L63/02C08L63/04C08L63/10C08L85/02C08L79/04C08G59/40C08G59/62H05K1/03
CPCH05K3/4602C08L79/04H05K1/0366H05K2201/012H05K3/4655C08G73/0655C08K5/5333C08L85/02H05K1/0373B32B15/092H05K2201/0209C08J2363/00C08J5/244C08J5/249C08L63/00
Inventor 陈勇苏民社
Owner GUANGDONG SHENGYI SCI TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com