Vegetable fiber environmental protection material product and preparation method thereof

A plant fiber and environmental protection material technology, applied in the field of plant fiber environmental protection material products, can solve the problems of poor toughness of plant fiber environmental protection material products, reduce the yield of plant fiber environmental protection material products, difficulty in preparation of plant fiber environmental protection material products, etc., and achieve the color of the finished product Smooth and well-proportioned, good toughness, and the effect of improving yield

Inactive Publication Date: 2011-01-19
朱超群
View PDF3 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, in the process of preparing plant fiber environmental protection material products through molds, due to the poor toughness of plant fiber environmental protection materials, it brings certain difficulties to the preparation of plant fiber environmental protection material products, and also reduces the finished product of plant fiber environmental protection material products. Rate
In addition, the degradation performance of the plant fiber environmental protection material products of the prior art needs to be further improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Vegetable fiber environmental protection material product and preparation method thereof
  • Vegetable fiber environmental protection material product and preparation method thereof
  • Vegetable fiber environmental protection material product and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] Plant fiber environmental protection material products are prepared from the following raw materials in parts by mass: 51 parts of plant fiber, 21 parts of electric jade powder, 10 parts of tapioca starch, 1 part of paraffin, 0.5 parts of sodium benzoate, 1.5 parts of zinc stearate, 1 part of antibacterial Oxygen agent 1010, 2 parts of organic pigments, 1 part of maltose, 4 parts of dextrin, 5 parts of light calcium carbonate, 2 parts of titanium dioxide, 0 parts of edible oil.

[0020] The preparation method of the above-mentioned plant fiber environmental protection material product comprises the following steps:

[0021] a. Grinding the plant fiber to 80 meshes to obtain plant fiber powder, at room temperature, place the plant fiber powder in a high-speed mixer and stir for 20 minutes to make it evenly mixed, wherein the water content of the plant fiber powder is 2%;

[0022] b. After adding binder, starch dextrin, maltose, release agent, waterproofing agent, organic...

Embodiment 2

[0025] Plant fiber environmental protection material products are prepared from the following raw materials in parts by mass: 20 parts of plant fiber, 40 parts of electric jade powder, 10 parts of tapioca starch, 1.5 parts of paraffin, 0.5 parts of sodium benzoate, 1 part of zinc stearate, 1 part of antibacterial Oxygen agent 1010, organic pigment 5 parts, titanium dioxide 1 part, dextrin 10 parts, maltose 10 parts, light calcium carbonate 0 parts, edible oil 0 parts.

[0026] The preparation method of the above-mentioned plant fiber environmental protection material product comprises the following steps:

[0027] a. Grinding the plant fiber to 30 meshes to obtain plant fiber powder, at normal temperature, place the plant fiber powder in a high-speed mixer and stir for 30 minutes to make it evenly mixed, wherein the water content of the plant fiber powder is 5%;

[0028] b. After adding binder, starch dextrin, maltose, release agent, water repellant, organic pigment or food co...

Embodiment 3

[0031] Plant fiber environmental protection material products are prepared from the following raw materials in parts by mass: 40 parts of plant fiber, 25 parts of electric jade powder, 5 parts of melamine, 15 parts of tapioca starch, 1 part of paraffin, 0.5 parts of sodium benzoate, 1.5 parts of zinc stearate 1 part, 1 part antioxidant 1010, 1 part organic pigment, 1 part maltose, 8 parts light calcium carbonate, 1 part edible oil, 0 part titanium dioxide.

[0032] The preparation method of the above-mentioned plant fiber environmental protection material product comprises the following steps:

[0033] a. Grinding the plant fiber to 120 meshes to obtain plant fiber powder, at room temperature, place the plant fiber powder in a high-speed mixer and stir for 40 minutes to make it evenly mixed, wherein the water content of the plant fiber powder is 7%;

[0034] b. After adding binder, starch dextrin, maltose, release agent, waterproofing agent, organic pigment or food coloring, p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
melting pointaaaaaaaaaa
water contentaaaaaaaaaa
Login to View More

Abstract

The invention discloses a vegetable fiber environmental protection material product and a preparation method thereof. The vegetable fiber environmental protection material product is prepared from the following raw materials in part by mass: 20 to 80 parts of vegetable fibers with 1 to 10 percent of moisture content, 10 to 60 parts of adhesive, 3 to 20 parts of starch, 1 to 10 parts of dextrin, 1 to 10 parts of malt sugar, 1 to 5 parts of release agent, 1 to 5 parts of waterproofing agent, 1 to 5 parts of organic pigment or food dye, 0.5 to 3 parts of preservative, 1 to 3 parts of antioxidant, 0 to 5 parts of edible oil, 0 to 10 parts of light calcium carbonate or kaolin and 0 to 5 parts of titanium white. Due to new raw material compositions, the proportioning of raw material components and the new preparation method, the vegetable fiber environmental protection material product has good toughness, and the finished product ratio of the vegetable fiber environmental protection material product is improved; and simultaneously, the vegetable fiber environmental protection material product has the advantage of easy degradation.

Description

technical field [0001] The invention relates to an environment-friendly material product, in particular to a plant fiber environment-friendly material product and a preparation method of the plant fiber environment-friendly material product. Background technique [0002] In the prior art, plant fiber environmental protection material products such as food containers, disposable tableware, gift packaging, flower pots, life decoration products and gift craft products are usually made of plant fibers after grinding and mixing with adhesives and fillers. Then it is prepared by mold under high temperature and high pressure conditions. Among them, the plant fiber is mainly obtained from rice husk, straw, wheat straw, corn stalk, cotton stalk, wood chips, bamboo chips and other crop straws or stalks of other plants. The adhesive mainly uses natural vegetable glue or formaldehyde series urea-formaldehyde resin, phenolic resin or melamine resin. [0003] However, in the process of ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L97/02C08L3/02C08L5/16C08L61/24C08L61/30C08K13/02C08K5/098C08K3/26C08K3/22B29C43/58
Inventor 朱超群
Owner 朱超群
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com