High-tenacity gas shielded welding wire for welding low-temperature steel and using method thereof

A technology of gas-shielded welding wire and high toughness, which is applied in the direction of welding/welding/cutting articles, welding media, welding equipment, etc. Ductile-brittle transition temperature, good low-temperature toughness, and the effect of improving low-temperature toughness

Active Publication Date: 2012-08-15
山东索力得焊材股份有限公司
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

One type of welding wire cannot meet the low temperature toughness requirements of the weld metal at -60°C due to its high S and P content and low Ni content; the other type of welding wire belongs to submerged arc welding wire and needs to be matched with the corresponding flux to meet The low temperature toughness requirements of the weld, so it cannot be used as a welding material for gas shielded welding

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-tenacity gas shielded welding wire for welding low-temperature steel and using method thereof
  • High-tenacity gas shielded welding wire for welding low-temperature steel and using method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0021] Below in conjunction with experimental data and embodiment the present invention will be further described.

[0022] According to the chemical composition range of the welding wire of the present invention and the mass percentages used in the following examples, a vacuum induction furnace is used to smelt multi-furnace welding wire steel, and through forging, rolling, wire drawing, copper plating and shaft winding, it is processed into a wire with a diameter of 1.2mm. The chemical composition of the finished welding wire and the welding wire of each furnace is shown in Table 1.

[0023] The welding wire of each furnace adopts volume 80% Ar+20% CO 2 Under argon-enriched gas protection, the same part was welded by the same person by the same person, and the same mechanical properties were tested with the same equipment and conditions at the same time after welding. The mechanical properties of the deposited metal are shown in Table 2.

[0024] The chemical composition of...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a high-tenacity gas shielded welding wire for welding low-temperature steel, which is suitable for welding the low-temperature steel subjected to service in the environment of over minus 60 DEG C. The gas shielded welding wire comprises the following chemical components in percentage by mass: 0.04 to 0.10 percent of C, 0.20 to 0.60 percent of Si, 1.20 to 1.60 percent of Mn,1.5 to 2.0 percent of Ni, 0.10 to 0.30 percent of Mo, 0.02 to 0.10 percent of Ti, 0.02 to 0.08 percent of Zr, less than or equal to 0.010 percent of S, less than or equal to 0.010 percent of P, less than or equal to 0.0025 percent of O, less than or equal to 0.0070 percent of N, and the balance of Fe and inevitable impurities. The welding wire welds by adopting Ar + 20%CO2 full-argon gas shielding so a weld metal has high low-temperature tenacity in a welding state and under a heat treatment condition after welding.

Description

technical field [0001] The invention belongs to the field of welding materials, and specifically relates to a high-toughness gas-shielded welding wire with high Ni content and Ti and Zr microalloying and a use method thereof. Background technique [0002] With the increasing application of welded structures in low-temperature environments, such as low-temperature pressure vessels, gas pipelines, petrochemical equipment, refrigeration equipment, food industry and liquid gas storage equipment, etc., all need to be used in low-temperature environments. Therefore, it is the primary consideration to require such steels to have sufficient low-temperature toughness and high resistance to low-temperature embrittlement. This will put forward higher requirements on the low temperature toughness of welded joints, and then on welding materials and welding processes. However, in the existing technology, there are very few gas-shielded welding wires that can meet the requirements of equi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B23K35/30B23K9/16B23K103/04
Inventor 关常勇国旭明张金生
Owner 山东索力得焊材股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products