Method for removing sulfur in petroleum coke and desulfurizer thereof

A technology of petroleum coke and desulfurization agent, which is applied in the fields of metallurgy, chemical industry, environmental protection, and materials. It can solve the problems of increased voltage drop, high thermal brittleness of carbon anode, and ecological environmental pollution, and achieves mild desulfurization conditions, low raw material costs, and high-quality process. The effect of short process

Inactive Publication Date: 2010-08-18
CENT SOUTH UNIV
View PDF6 Cites 24 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

These S not only affect the production of carbon products, but also affect the stability of production and the cost of use in downstream industries, and pose a serious threat to the environment
Taking the production of carbon anodes for aluminum as an example, the carbon anode prepared by using high S coke has high thermal brittleness, which leads to a decrease in the thermal stability of the anode and is easy to crack; S in the high S anode will also react with the anode steel claw to form iron sulfide film, increasing the voltage drop, thereby increasing the power consumption of aluminum electrolysis; in addition, the S in the anode is converted to SO in the process of electrolysis with the consumption of the carbon anode 2 form precipitation, causing serious pollution to the surrounding ecological environment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for removing sulfur in petroleum coke and desulfurizer thereof
  • Method for removing sulfur in petroleum coke and desulfurizer thereof
  • Method for removing sulfur in petroleum coke and desulfurizer thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] Take 2g of raw petroleum coke with a sulfur content of 3.4% from an aluminum factory in China, crush it to below 150 mesh, prepare a mixed acid with hydrochloric acid and nitric acid according to the ratio of 1, and then mix the mixed acid and petroleum coke at a liquid-solid ratio of 30ml / g Mix well in the reactor, place the system in a constant temperature water bath to control the reaction temperature at 60° C., and continue the reaction at normal pressure for 24 hours. Then the reactant is vacuum filtered to recover the desulfurized liquid. The filter cake was washed with deionized water for about 5 minutes, and then vacuum-filtered with a suction filter, and the filtered cake was put into a vacuum drying oven and dried at 90°C for 24 hours to obtain desulfurized coke. The total sulfur content of the desulfurized petroleum coke was measured by microcoulomb titration, and the desulfurization rate reached 64.6%.

Embodiment 2

[0030] Take 2g of raw petroleum coke with a sulfur content of 5.6% from an aluminum factory in China, crush it to below 150 mesh, prepare a mixed acid with hydrochloric acid and nitric acid at a ratio of 0.5, and then mix the mixed acid and petroleum coke at a liquid-solid ratio of 20ml / g Mix well in the reactor, place the system in a constant temperature water bath to control the reaction temperature at 50° C., and continue the reaction at normal pressure for 24 hours. Then the reactant is vacuum filtered to recover the desulfurized liquid. Wash the filter cake with deionized water for about 5 minutes, and then perform vacuum filtration with a suction filter, put the filter cake after suction filtration into a vacuum drying oven and dry at 100°C for 20 hours to obtain desulfurized coke. The total sulfur content of the desulfurized petroleum coke was determined by microcoulomb titration, and the desulfurization rate reached 50.4%.

Embodiment 3

[0032] Take 2g of raw petroleum coke with a sulfur content of 7.6% from an aluminum factory in China, crush it to below 150 mesh, prepare a mixed acid with hydrochloric acid and nitric acid at a ratio of 1.5, and then mix the mixed acid and petroleum coke at a liquid-solid ratio of 40ml / g Mix well in the reactor, place the system in a constant temperature water bath to control the reaction temperature at 40° C., and continue the reaction at normal pressure for 24 hours. Then the reactant is vacuum filtered to recover the desulfurized liquid. Wash the filter cake with deionized water for about 5 minutes, and then perform vacuum filtration with a suction filter, put the filter cake after suction filtration into a vacuum drying oven and dry at 100°C for 20 hours to obtain desulfurized coke. The total sulfur content of the desulfurized petroleum coke was measured by microcoulomb titration, and the desulfurization rate reached 55.3%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a method for removing sulfur in petroleum coke and a desulfurizer thereof. The method adopts two types of mixed acid with a fixed ratio controlled as the desulfurizer, and comprises the following steps: placing fine petroleum coke with a high S content (the S content being 3-7 percent) in the mixed acid under the atmospheric pressure and the temperature of 0-60 DEG C, soaking the petroleum coke for reaction for a certain time, separating the petroleum coke and the soaking solution, washing and drying. The desulfurization percent of the obtained petroleum coke is 45-60 percent, the microstructure of the petroleum coke is not changed obviously, and the separated soaking solution of mixed acid can be repeatedly used when being mixed with the newly prepared liquid. The method has the advantages of low desulfurization cost, simple operation and significant desulfurization effect.

Description

technical field [0001] The invention relates to a chemical desulfurization method of petroleum coke and a desulfurizer thereof, and the method belongs to the technical fields of metallurgy, material, chemical industry and environmental protection. Background technique [0002] Petroleum coke is one of the main by-products of petroleum deep processing, and it is also an important raw material for metallurgy, chemical industry and inorganic material preparation. According to the different sulfur content, petroleum coke is divided into high sulfur coke (S ≥ 3%) and low sulfur coke (S ≤ 3%). Among them, high-sulfur coke is mainly used as fuel, and low-sulfur coke is mainly used in the production of prebaked anodes and graphite electrodes for aluminum and steelmaking furnaces and other carbon products industries. In my country, because the S content in crude oil is generally low, the S content of the produced petroleum coke is correspondingly low. With the development of the ec...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C01B31/02C10L9/06
Inventor 肖劲邓松云杨思蔚赖延清李劼
Owner CENT SOUTH UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com