Method for preparing carbon-coated superparamagnetic ferroferric oxide gel

A technology of ferric oxide and superparamagnetism, which is applied in the direction of iron oxide/iron hydroxide, magnetic properties of inorganic materials, oxides of ferrous iron, etc. It can solve the problems of complicated process, high requirement of reaction conditions, poor stability, etc. Problems, to achieve the effect of simple process, high chemical and colloidal stability, and overcome the high cost of raw materials

Inactive Publication Date: 2010-08-04
UNIV OF SCI & TECH OF CHINA
View PDF8 Cites 43 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The above methods for preparing ferroferric oxide particles either mainly focus on the synthesis mechanism, or require high reaction conditions and complicated processes, and cannot prepare particles with both large particle size and superparamagnetic characteristics.
In addition, the common ferroferric oxide is often surface-modified with high-molecular organic substances, and its stability at high temperatures is not good, so these methods are limited in practical applications

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing carbon-coated superparamagnetic ferroferric oxide gel
  • Method for preparing carbon-coated superparamagnetic ferroferric oxide gel
  • Method for preparing carbon-coated superparamagnetic ferroferric oxide gel

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] Embodiment 1. prepares uniform ferric oxide colloidal ball

[0034] Take 0.3g of ferrocene, dissolve it in 30.0mL of acetone, ultrasonically disperse it, then add 1.5ml of 30% hydrogen peroxide dropwise, stir magnetically at 1000r / min for 30 minutes, and then transfer the solution to a volume of 40ml In an autoclave, seal and heat to 240°C, keep it warm for 72 hours, and then cool to room temperature to obtain a black powdery solid; then wash the sample 3 times with acetone and ethanol to remove residual organic matter in the solid powder; then the solid The powder was dried in a vacuum oven at 40°C for 6 hours to obtain the product.

[0035] Such as figure 1 Shown, according to the X-ray diffraction of present embodiment product Figure, all diffraction peak positions correspond to (111), (220), (311), (222), (400), (422), (511), (440) face of ferric oxide respectively, show product as Ferric oxide; By the transmission electron microscope electron diffraction image ...

Embodiment 2

[0036] The influence of the amount of embodiment 2.ferrocene on product

[0037] Take 0.1g and 0.2g of ferrocene, dissolve in 30.0mL of acetone, ultrasonically disperse, then add 1.5ml of 30% hydrogen peroxide dropwise, stir magnetically at 1000r / min for 30 minutes, then transfer the solution to In an autoclave with a capacity of 40ml, seal and heat to 240°C for 72 hours, then cool to room temperature to obtain a black powdery solid; then wash the sample 3 times with acetone and ethanol to remove residual organic matter in the solid powder; then The solid powder was dried in a vacuum oven at 40° C. for 6 hours to obtain the product. The product looks like Figure 8 (0.10g) and Figure 9 (0.20g). Figure 8 with Figure 9 It shows that the smaller the amount of ferrocene, the smaller the thickness of the carbon layer on the surface of ferric oxide nanospheres.

Embodiment 3

[0038] Embodiment 3. The influence of the amount of hydrogen peroxide on product

[0039] Adopt the same method as in Example 1 to configure a portion of the same solution, that is, weigh 0.3g ferrocene, dissolve it in 30.0ml acetone, and only change the amount of hydrogen peroxide added later to 0.5ml, 1.5ml, 3ml , and the other processes are the same. The obtained results were confirmed by X-ray diffraction analysis, all of which were colloidal spheres of ferric oxide. The difference was that colloidal spheres with particle diameters of 90nm, 150nm and 200nm were obtained respectively. A smaller amount of hydrogen peroxide can only obtain small particles with weaker magnetic properties, not ferric oxide, and too much hydrogen peroxide has little effect on the change of particle size, so the amount of hydrogen peroxide is usually between 0.5ml- between 3ml. The resulting product looks like Figure 10 , Figure 11 with Figure 12 shown. Figure 10 , Figure 11 with Fi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for preparing carbon-coated superparamagnetic ferroferric oxide gel, which comprises: dissolving ferrocene and surfactant in an acetone solvent; adding solution of hydrogen peroxide into the solution to directly oxidize the ferrocene to synthesize polycrystal uniform magnetic nano balls under a low-temperature (180 to 240 DEG C) solvothermal condition; and allowing the polycrystal uniform magnetic nano balls to react in a magnetic field to prepare a magnetic linear nano material. The polycrystal uniform magnetic nano balls and nano chains are characterized in that: the particle size of the polycrystal uniform magnetic nano balls is limited to a narrow range and controllable; and the nano chains consist of uniform spherical particles and have high stability, and the inter-chain distance is controllable. The superparamagnetic polycrystal uniform nano ball and linear nano chain materials have high superparamagnetism and high chemical stability and gel stability and have promising application prospect in the field of biomedicine, nano self-assembly and the like; the nano balls are grafted by medicaments and can be used as medicament carriers; under the action of the magnetic field, the nano balls can be used as magnetic control photonic crystal; and the nano chains have a promising application prospect in the field of Bragg reflectors, magnetic probes, biomedicine and the like.

Description

technical field [0001] The invention belongs to the technical field of magnetic nanomaterial preparation, in particular to a preparation method of carbon-coated superparamagnetic ferric oxide nanospheres. Background technique [0002] According to China's "Inorganic Salt Industry" (2007, Vol. 39, Page 5), nano-Fe3O4 is widely used in magnetic liquids, magnetic recording materials, catalysis, biomedicine, and microwave absorbing materials. For example, the ferrofluid prepared by ferroferric oxide has been widely used in the fields of vacuum sealing, voice coil heat dissipation, rapid printing, mineral sorting, precision grinding, sensors and aerospace technology. In biomedicine, Fe3O4 nanoparticles have broad application prospects in targeted drug delivery, NMR enhancer, magnetic separation and other fields. [0003] Journal of the American Chemical Society (J.AM.CHEM.SOC., 2002, volume 124, page 8204) reported a method for synthesizing monodisperse iron ferric oxide nanopar...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): H01F1/34C01G49/08C04B35/628
Inventor 陈乾旺王辉孙玉冰
Owner UNIV OF SCI & TECH OF CHINA
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com