Anti-sticking soft dope printing adhesive and preparation method

A pigment printing and adhesive technology, applied in dyeing, textiles and papermaking, etc., can solve problems such as poor fastness, achieve super soft hand feeling, excellent washing fastness, and various effects

Inactive Publication Date: 2010-06-23
SHANGHAI JAROS NEW MATERIAL +1
View PDF0 Cites 31 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although butadiene-based adhesives have a soft feel, they have poor fastness and need to be used in combination with acrylate adhesives

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Anti-sticking soft dope printing adhesive and preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] (1) Adhesive formulation

[0044] The mass percentage of raw material composition is,

[0045] Ethyl acrylate 31.0%

[0046] Methyl methacrylate 8.50%

[0047] Acrylic 3.40%

[0048] Acrylonitrile 2.60%

[0049] Trimethylolpropane Trimethacrylate 1.30%

[0050] Trimethylisocyanate 1.40%

[0051] Sodium Lauryl Sulfate 0.29%

[0052] Flat Plus 0.89%

[0053] Ammonium persulfate 0.16%

[0054] Sodium bisulfite 0.08%

[0055] Sodium bicarbonate 0.08%

[0056] Mercaptan 0.06%

[0057] Deionized water 50.24%

[0058] (2) Preparation method

[0059] A preparation method of anti-sticking soft pigment printing adhesive, the specific steps are:

[0060] (1) Add 1 / 6 of the soft monomer, hard monomer and functional monomer in the raw material components, as well as all emulsifiers and part of deionized water into the reactor, stir and emulsify at room temperature for 30 minutes, raise the temperature to 58°C, add sulfur Alcohols and some initiators;

[0061] (2) Star...

Embodiment 2

[0063] (1) Adhesive formulation

[0064] The mass percentage of raw material composition is,

[0065] Octyl Acrylate 11%

[0066] Butyl Acrylate 8%

[0067] n-Butyl methacrylate 12.47%

[0068] Styrene 6.50%

[0069] Acrylic 4.0%

[0070] Acrylonitrile 2.50%

[0071] Monobutyl itaconate 1.30%

[0072] Trimethylisocyanate 0.80%

[0073] Sodium dodecylbenzenesulfonate 0.32%

[0074] Flat Plus 0.89%

[0075] Ferrous Chloride 0.08%

[0076] Hydrogen peroxide 0.16%

[0077] Sodium acetate 0.08%

[0078] Mercaptan 0.06%

[0079] Deionized water 51.84%

[0080] (2) Preparation method

[0081] (1) Add 1 / 8 of the soft monomer, hard monomer and functional monomer in the raw material components, as well as all emulsifiers and part of deionized water into the reactor, stir and emulsify at room temperature for 40 minutes, raise the temperature to 65°C, add sulfur Alcohols and some initiators;

[0082] (2) Start to add the remaining mixed monomers dropwise. After the dropwise ...

Embodiment 3

[0084] The printing paste formula (mass percentage) that adopts the above-mentioned binder formula that prepares to carry out:

[0085] Color paste 3%

[0086] Thickener 3%

[0087] Binder 25%

[0088] Water 69%

[0089] The adhesive synthesized by the invention can replace traditional dye-printed products, and has the advantages of low pollution and convenient use. It has been staked out in many printing companies and achieved good results.

[0090] Adopt general printing process to test described adhesive and obtain following result:

[0091]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses anti-sticking soft dope printing adhesive and a preparation method. The adhesive comprises the following raw materials in percentage by mass: 25 to 50 percent of soft monomer, 6 to 20 percent of hard monomer, 0.8 to 5 percent of emulsifying agent, 0.1 to 0.25 percent of initiator, 0.05 to 0.5 percent of buffer, 0.04 to 0.2 percent of thiol and 40 to 65 percent of deionized water. The preparation method comprises the following steps: adding 1/8 to 1/6 of the soft monomer, the hard monomer and a functional monomer of the raw materials, total emulsifying agent and total deionized water into a reactor, stirring and emulsifying the mixture for 30 to 40 minutes at the room temperature, heating the mixture to between 50 and 65 DEG C, and adding the thiol and the initiator into the reactor; and beginning dripping the mixed monomer, preserving the heat for 2 hours at the temperature of between 50 and 65 DEG C after the dripping is finished, heating the mixture to 70 DEG C, preserving the heat for half an hour, and cooling a product to the room temperature, and discharging the product. The anti-sticking soft dope printing adhesive has the advantages that: the adhesive has excellent washing fastness, super-soft handfeel, environmental protection and no brittleness or after tack, overcomes the defects of hot sticking and poor handfeel of acrylic ester, has many available thickening agent categories, and easily mixes size.

Description

【Technical field】 [0001] The invention relates to the technical field of printing adhesives, in particular to an anti-adhesive soft pigment printing adhesive and a preparation method. 【Background technique】 [0002] Acrylic adhesives have the advantages of weather resistance and fast drying, and are widely used in the textile printing industry, and have gained a large market due to their low prices. Due to the advantages of simple process, resource saving, and less waste water discharge, pigment printing is suitable for the use of fiber fabrics and has been more and more widely used. However, the acrylate adhesive itself has certain defects, which cannot be solved by changing the acrylate components, which affects and limits its further application. The currently used acrylate adhesive has the disadvantage of poor hot-stick feel, which seriously affects the feel of the product when it is applied to printing. [0003] Pigment printing is a printing process that uses adhesiv...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D06P1/52C08F220/18C08F2/24C08F222/14
Inventor 潘跃进杨成龙孙洋
Owner SHANGHAI JAROS NEW MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap